Teijin Panlite® G-3410R Glass Fiber Reinforced Polycarbonate Resin

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Glass Fiber Filled, Flame Retardant
Manufacturer Teijin
Trade Name Panlite®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Teijin Panlite® G-3410R Glass Fiber Reinforced Polycarbonate Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
GF 10% reinforced and mold release grade, meeting UL 94 V-2.Applications:Mechanical, electric and electronic components that need mechanical property e.g., stiffnessPrecision machinery components that need dimensional accuracy.Information provided by Teijin Chemicals Ltd.
Physical Properties Metric English Comments
Density 1.27 g/cc
0.0459 lb/in³
ISO 1183
Water Absorption 0.16 %
0.16 %
in water, 23°C, 24h; ISO 62
Linear Mold Shrinkage 0.0030 - 0.0050 cm/cm

@Thickness 4.00 mm
0.0030 - 0.0050 in/in

@Thickness 0.157 in
Linear Mold Shrinkage, Transverse 0.0040 - 0.0060 cm/cm

@Thickness 4.00 mm
0.0040 - 0.0060 in/in

@Thickness 0.157 in
Mechanical Properties Metric English Comments
Tensile Strength at Break 70.0 MPa
10200 psi
50mm/min; ISO 527
Elongation at Break 3.5 %
3.5 %
50mm/min; ISO 527
Tensile Modulus 3.70 GPa
537 ksi
1mm/min; ISO 527
Flexural Strength 120 MPa
17400 psi
2mm/min; ISO 178
Flexural Modulus 3.60 GPa
522 ksi
2mm/min; ISO 178
Charpy Impact Unnotched 5.50 J/cm²
26.2 ft-lb/in²
ISO 179
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
CTE, linear 40.0 µm/m-°C

@Temperature 20.0 °C
22.2 µin/in-°F

@Temperature 68.0 °F
ISO 11359
CTE, linear, Transverse to Flow 60.0 µm/m-°C

@Temperature 20.0 °C
33.3 µin/in-°F

@Temperature 68.0 °F
ISO 11359
Deflection Temperature at 0.46 MPa (66 psi) 149 °C
300 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 144 °C
291 °F
ISO 75
Vicat Softening Point 151 °C
304 °F
50°C/hr, 50N; ISO 306
UL RTI, Electrical 130 °C

@Thickness 1.47 mm
266 °F

@Thickness 0.0579 in
UL 746B
UL RTI, Mechanical with Impact 120 °C

@Thickness 1.47 mm
248 °F

@Thickness 0.0579 in
UL 746B
UL RTI, Mechanical without Impact 130 °C

@Thickness 1.47 mm
266 °F

@Thickness 0.0579 in
UL 746B
Flammability, UL94 HB

@Thickness 0.430 mm
HB

@Thickness 0.0169 in
V-2

@Thickness 0.800 mm
V-2

@Thickness 0.0315 in
V-1

@Thickness 3.00 mm
V-1

@Thickness 0.118 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
Dielectric Constant 3.2

@Frequency 100 Hz
3.2

@Frequency 100 Hz
IEC 60250
3.2

@Frequency 1e+6 Hz
3.2

@Frequency 1e+6 Hz
IEC 60250
Dielectric Strength 35.0 kV/mm
889 kV/in
IEC 60243
Dissipation Factor 0.0010

@Frequency 100 Hz
0.0010

@Frequency 100 Hz
IEC 60250
0.0090

@Frequency 1e+6 Hz
0.0090

@Frequency 1e+6 Hz
IEC 60250
Comparative Tracking Index 175 V
175 V
IEC 60112