Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 3.60 GPa | 522 ksi | |
Plastcom SLOVASTER® B1 GF 15 FRX 5 PBT reinforced with 15% glass fibre, with flame retardant Features: PBT with the content of 15 % chemically bound glass fibre and with the halogen freeflame retardant. Anisotropy of shrinkage enables the injection moulding of round, cylindrical or other ho.. |
|||
Flexural Modulus | 3.60 GPa | 522 ksi | |
Plastcom SLOVASTER® B2 GF 10 PBT, 10% glass fibre FeaturesPBT for injection moulding, chemically reinforced with 10% glass fibre. Characterised by excellent properties also at minus temperatures like eg. modulus of elasticity in tension and bending.. |
|||
Flexural Modulus | 3.60 GPa | 522 ksi | ASTM D790M-93 |
Propex Fabrics Curv™ C100A Polypropylene/Polypropylene Thermoformable Composite Curv™ key features include weight savings, total recyclability, no glass content, thermoformable, high impact strength, inertness, and abrasion resistance.Data provided by BP Amoco; Curv was spun o.. |
|||
Flexural Modulus | 3.60 GPa | 522 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® FXE4271L PC (Asia Pacific) Lexan* FXE4271L is a 10% glass filled, impact modified polycarbonate with excellent light-shield capability. It is designed for high flow, superior surface appearance, enhance release and good impac.. |
|||
Flexural Modulus | 3.60 GPa | 522 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP FARADEX NX07330 PC+ABS (Asia Pacific) Faradex NX07330 is a compound based on PC+ABS blend resin containing stainless steel and glass fiber. Added features of this material include EMI/RFI Shielding and ESD. |
|||
Flexural Modulus | 3.60 GPa | 522 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP DFL32 PC (Europe-Africa-Middle East) LNP* Lubricomp* DFL32 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. |
|||
Flexural Modulus | 3.60 GPa | 522 ksi | ASTM D790 |
Gharda Chemicals GATONE™ 5700 Polyetheretherketone (PEEK)
(discontinued **) Characteristics: Outstanding Chemical Resistance Outstanding Wear Resistance Outstanding Resistance to HydrolysisExcellent Mechanical Properties Outstanding Thermal properties Very good Dielectric.. |
|||
Flexural Modulus | 3.60 GPa | 522 ksi | |
Lehmann & Voss LUVOCOM® 1105-7741 PEEK, with mineral filler, lubricant modified Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Dynamic stressed parts at high movement velocity.Chemical and hydrolysis resistance parts,.. |
|||
Flexural Modulus | 3.60 GPa @Thickness 3.20 mm |
522 ksi @Thickness 0.126 in |
15mm/min; ASTM D790 |
LG Chemical 82TR SAN, High Transparency, Heat Resistance, Chemical Resistance Feature: Injection Molding, SAN, High Transparency, Heat Resistance, Chemical ResistanceApplication: Refrigerator Sleeves, MiscellaneousCAS No. 9003-54-7Information provided by LG Chemical |
|||
Flexural Modulus | 3.60 GPa @Temperature 80.0 °C |
522 ksi @Temperature 176 °F |
2 mm/min, 64mm span; ISO 178 |
SABIC Innovative Plastics SABIC STAMAX 30YK270 PP SABIC® STAMAX 30YK270 is a 30% long glass fiber reinforced polypropylene with improved impact and flow properties. The glass fibers are chemically coupled to the PP matrix, resulting in high stif.. |
|||
Flexural Modulus | 3.60 GPa | 522 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Valox® VX5011 PBT (Europe-Africa-Middle East) VALOX VX5011 is a 10% glass fibre reinforced PBT+PC blend with low warpage characteristics. |
|||
Flexural Modulus | 3.60 GPa | 522 ksi | ISO 178 |
SABIC Innovative Plastics LNP Thermocomp IF002 PA 6/12 (Asia Pacific) LNP* Thermocomp* IF002 is a compound based on Nylon 6/12 resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Flexural Modulus | 3.60 GPa | 522 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP KFB41 (Europe-Africa-Middle East) LNP* THERMOCOMP* KFB41 is a compound based on Acetal Copolymer resin containing Glass Fiber, Glass Bead. |
|||
Flexural Modulus | 3.60 GPa | 522 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Thermocomp WB006 PBT LNP* Thermocomp* WB006 is a compound based on Polybutylene Terephalate resin containing Glass Bead.This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Modulus | 3.60 GPa | 522 ksi | Tangent |
Schmelzer Industries Curveil 220-30 Fiberglass Veil Good for curved applications - drapable and flexible. Suitable for hand lay-up, pre-form molding, press molding, vacuum molding, and injection molding. The 200 series contains a binder additive. .. |
|||
Flexural Modulus | 3.60 GPa | 522 ksi | Tangent |
Schmelzer Industries Pearlveil 110-20 Fiberglass Veil Economical alternative for flat or shallow applications. Suitable for hand lay-up, pre-form molding, press molding, vacuum molding, and injection molding. Data provided by the manufacturer, Schmel.. |
|||
Flexural Modulus | 3.60 GPa | 522 ksi | ISO 178 |
Polyram PlusTek PA340S8 Nylon 6.6 for Injection Molding, 40% Glass-beads Reinforced 40% Glass-beads reinforced Nylon 6.6 for injection molding applications.Information provided by Polyram. |
|||
Flexural Modulus | 3.60 GPa | 522 ksi | Tangent; ASTM D790 |
Washington Penn PPUP4G402 Polypropylene, 40% Talc Filled, High Flow Exceptional retention of mechanical properties and appearance upon long term heat aging.Applications: Appliance parts.Data provided by Washington Penn Plastic Co., Inc. |
|||
Flexural Modulus | 3.60 - 4.10 GPa | 522 - 595 ksi | ASTM D790 |
Zeus PEEK Tubing PEEK (polyetheretherketone) is a high-performance engineered polymer with excellent endurance to heat and one of the highest strength-to-weight ratios of any thermoplastic. This material can be used.. |
|||
Flexural Modulus | 3.60 GPa | 522 ksi | ASTM-D790 |
Polyram RamOfin PPC364I6 Polypropylene, 30% Mineral and Glass Fiber 30% mineral and glass fiber reinforced, heat resistant polypropylene for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Flexural Modulus | 3.60 GPa | 522 ksi | ASTM D790, ISO 178 |
EPICHEM Epilon PC GF 10 V0 Polycarbonate, 10% Glass Fiber Characteristics: self-extinguishing V0 at 1,6 mm, 10% glass fibre filled |
|||
Flexural Modulus | 3.60 GPa | 522 ksi | ASTM D790 |
Aclo Accutech Polycarbonate POL051G10L Glass Reinforced |
|||
Flexural Modulus | 3.60 GPa | 522 ksi | ASTM D790 |
Aclo Accutech Polypropylene HP0335T40V Homopolymer Talc Reinforced Approved to ESF-M4D355B White B12391 |
|||
Flexural Modulus | 3.60 GPa | 522 ksi | ASTM D790 |
Ashley Polymers Ashlene® 525-13G Nylon 66, 13% Glass Reinforced High impact Nylon 66 reinforced with 13% glass fibers.Data provided by the manufacturer |
|||
Flexural Modulus | 3.60 GPa | 522 ksi | ISO 178 |
BASF Ultramid® C3U10 BK 23079 PA6/66 FR (Dry) Description: Flame-retardant injection-molding grade; light colorable. Burning behavior optimized for glow-wire requirements of IEC 60335. Typical applications are switches, housings, plug connector.. |
|||
Flexural Modulus | 3.60 GPa | 522 ksi | ISO 178 |
BASF Ultramid® C3U10 PA6/66 FR (Dry) Description: Flame-retardant injection-molding grade; light colorable. Burning behavior optimized for glow-wire requirements of IEC 60335. Typical applications are switches, housings, plug connector.. |
|||
Flexural Modulus | 3.60 GPa | 522 ksi | ASTM D790 |
Ashley Polymers Ashlene® P1410 Polycarbonate, 10% Glass Reinforced A 10% glass reinforced polycarbonate for increased mechanical strength and thermal properties. P1413: with UV stabilizer.Data provided by the manufacturer |
|||
Flexural Modulus | 3.60 GPa | 522 ksi | ASTM D790 |
Aclo Accutech Polypropylene Homopolymer HP0339T40L Talc Reinforced |
|||
Flexural Modulus | 3.60 - 9.80 GPa @Temperature 100 - 175 °C |
522 - 1420 ksi @Temperature 212 - 347 °F |
Average value: 5.87 GPa Grade Count:8 |
Overview of materials for Polyphthalamide (PPA), 30% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, 30% Glass Fiber Reinforced". Specific grades with glass content between 25% and 34% are.. |