Styrolution Terblend® N NM-19 XP Beige 38163 ABS+PA (Dry)
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend , Nylon |
| Manufacturer | Styrolution |
| Trade Name | Terblend® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution Terblend® N NM-19 XP Beige 38163 ABS+PA (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Terblend® N NM-19 XP is an UV stabilized ABS/PA blend combining very high impact strength, even at low temperatures with an outstanding processability and excellent surface appearance.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.2 % | 1.2 % | 23°C/50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm | 0.0070 in/in | ISO 2577 |
| Melt Flow | 42.8 g/10 min @Load 10.0 kg, Temperature 240 °C |
42.8 g/10 min @Load 22.0 lb, Temperature 464 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 103 | 103 | ISO 2039-2 |
| Ball Indentation Hardness | 86.0 MPa @Load 36.5 kg, Time 30.0 sec |
12500 psi @Load 80.5 lb, Time 0.00833 hour |
ISO 2039-1 |
| Tensile Strength, Yield | 43.0 MPa | 6240 psi | ISO 527-1/-2 |
| Elongation at Break | 30 % | 30 % | Nominal; ISO 527-1/-2 |
| Elongation at Yield | 3.5 % | 3.5 % | ISO 527-1/-2 |
| Tensile Modulus | 2.00 GPa | 290 ksi | ISO 527-1/-2 |
| Flexural Strength | 62.0 MPa | 8990 psi | ISO 178 |
| Flexural Modulus | 1.80 GPa | 261 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
ISO 180/A |
| 65.0 kJ/m² @Temperature 23.0 °C |
30.9 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A | |
| Charpy Impact Unnotched | NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179/1eU |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 1.50 J/cm² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 6.50 J/cm² @Temperature 23.0 °C |
30.9 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 100 µm/m-°C @Temperature 23.0 - 80.0 °C |
55.6 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-1/-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ISO 75-1/-2 |
| Vicat Softening Point | 102 °C | 216 °F | VST/B/50; ISO 306 |
| 160 °C | 320 °F | VST/A/50; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 |
| Dielectric Constant | 2.9 @Frequency 1.00e+6 Hz |
2.9 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dissipation Factor | 0.015 @Frequency 1.00e+6 Hz |
0.015 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 - 270 °C | 464 - 518 °F | Injection Molding |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Injection Molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Beige 38163 | |
| Commercial Status | Europe | |
| Primary Processing Technique | Injection Molding and Extrusion |