- Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded
- Styrolution Novodur® H802 ABS
Styrolution Novodur® H802 ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded |
| Manufacturer | Styrolution |
| Trade Name | Novodur® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution Novodur® H802 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Novodur H802 is a high heat injection molding grade with high stiffness, especially suitable for being painted.Information provided by Styrolution
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ISO 294-4 |
| Melt Flow | 8.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
8.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 115 MPa | 16700 psi | ISO 2039-1 |
| Tensile Strength, Yield | 51.0 MPa | 7400 psi | ISO 527 |
| Elongation at Yield | 2.8 % | 2.8 % | ISO 527 |
| Tensile Modulus | 2.70 GPa | 392 ksi | ISO 527 |
| Charpy Impact Unnotched | 8.00 J/cm² @Temperature -30.0 °C |
38.1 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 10.0 J/cm² @Temperature 23.0 °C |
47.6 ft-lb/in² @Temperature 73.4 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.700 J/cm² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 1.50 J/cm² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359 |
| Deflection Temperature at 0.46 MPa (66 psi) | 107 °C | 225 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 101 °C | 214 °F | ISO 75 |
| Vicat Softening Point | 109 °C @Load 5.10 kg |
228 °F @Load 11.2 lb |
50°C/h; ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.1 @Frequency 100 Hz |
3.1 @Frequency 100 Hz |
IEC 60250 |
| Dielectric Strength | 34.0 kV/mm @Thickness 1.50 mm |
864 kV/in @Thickness 0.0591 in |
Short Time; IEC 60243-1 |
| Dissipation Factor | 0.0060 @Frequency 100 Hz |
0.0060 @Frequency 100 Hz |
IEC 60250 |
| 0.010 @Frequency 1.00e+6 Hz |
0.010 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 230 - 270 °C | 446 - 518 °F | ISO 294 |
| Mold Temperature | 70.0 °C | 158 °F | ISO 294 |
| Injection Velocity | 240 mm/sec | 9.45 in/sec | ISO 294 |
| Drying Temperature | 80.0 °C @Time 7200 - 14400 sec |
176 °F @Time 2.00 - 4.00 hour |
Users viewing this material also viewed the following:
- Osprey Metals 90/10 Cu Sn Powder (Grade 90% - 16)
- Pyrotek L-8 Fiberseal Blanket
- LNP ULTEM® SMU5872 Polyetherimide, 25% PTFE Lubricant (discontinued **)
- Materion Brush 1915â„¢ Annealed Temper Rod
- Styron XZ 97224.00 Carboxylated SB
- UBE UBESTA® 3024U Rigid Electronic Grade Nylon 12
- Eagle Brass 110 EPT COPPER, Annealed
- Epoxy Technology EPO-TEK® H81A Epoxy
- Saint-Gobain Chemfab® 1565V PTFE Coated Fiberglass Conveyor Belting
- LG Chemical LUXY KS G55 Amorphous PA6
Copyright © lookpolymers.com All Rights Reserved