LG Chemical LUXY KS G55 Amorphous PA6

Category	Polymer , Thermoplastic , Nylon , Amorphous Nylon
Manufacturer	LG Chemical
Trade Name	LUXY
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LG Chemical LUXY KS G55 Amorphous PA6.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Injection Molding, Amorphous PA6, High Modulus, High Impact, Low WarpageApplication: Electric/Electronic Components (LCD Bracket)Information provided by LG Chemical

Physical Properties	Metric	English	Comments
Specific Gravity	1.50 g/cc	1.50 g/cc	ASTM D792
Linear Mold Shrinkage, Flow	0.00030 - 0.0015 cm/cm @Thickness 3.20 mm	0.00030 - 0.0015 in/in @Thickness 0.126 in	ASTM D955

Mechanical Properties	Metric	English	Comments
Elongation at Break	6.0 % @Thickness 3.20 mm	6.0 % @Thickness 0.126 in	5mm/min; ASTM D638
Flexural Yield Strength	281 MPa @Thickness 3.20 mm	40800 psi @Thickness 0.126 in	1.3mm/min; ASTM D790
Flexural Modulus	13.0 GPa @Thickness 3.20 mm	1890 ksi @Thickness 0.126 in	1.3mm/min; ASTM D790
Izod Impact, Notched	1.57 J/cm @Thickness 3.20 mm, Temperature 23.0 °C	2.94 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F	ASTM D256

Thermal Properties	Metric	English
Flammability, UL94	HB @Thickness >=0.800 mm	HB @Thickness >=0.0315 in
	HB @Thickness >=1.60 mm	HB @Thickness >=0.0630 in
	HB @Thickness >=2.50 mm	HB @Thickness >=0.0984 in
	HB @Thickness >=3.20 mm	HB @Thickness >=0.126 in

Processing Properties	Metric	English	Comments
Rear Barrel Temperature	280 - 300 °C	536 - 572 °F	Injection Molding
Middle Barrel Temperature	280 - 300 °C	536 - 572 °F	Injection Molding
Front Barrel Temperature	280 - 300 °C	536 - 572 °F	Injection Molding
Nozzle Temperature	280 - 320 °C	536 - 608 °F	Injection Molding
Melt Temperature	280 - 300 °C	536 - 572 °F	Injection Molding
Mold Temperature	80.0 - 100 °C	176 - 212 °F	Injection Molding
Drying Temperature	80.0 - 100 °C	176 - 212 °F	Injection Molding
Dry Time	4.00 - 5.00 hour	4.00 - 5.00 hour	Injection Molding
Back Pressure	29.4 - 58.8 MPa	4260 - 8530 psi	Injection Molding
Screw Speed	50 - 150 rpm	50 - 150 rpm	Injection Molding