| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® A 225F PA66, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Unreinforced polyamide 66, medium viscosity, for injection molding, with a special crystallizing agent, for very fast cycles.Available in: Europe, Latin America and North AmericaProduct Applications: TECHNYL ® A 225F offers two main advantages excellent filling qualities and UL 94 V2 under 0.4 mm. It is particularly used in electrical applications to mould parts with a good dimensional stability, such as: Unfilled bobbin coil forers for electrical motors, Transformers, and Connectors. This product is available in natural.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183/A |
| Water Absorption | 1.1 % @Temperature 23.0 °C, Time 86400 sec |
1.1 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage | 0.0083 cm/cm | 0.0083 in/in | Isotropy |
| Linear Mold Shrinkage, Flow | 0.015 cm/cm | 0.015 in/in | |
| Linear Mold Shrinkage, Transverse | 0.018 cm/cm | 0.018 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 70.0 MPa | 10200 psi | ISO 527 Type 1A |
| Tensile Strength, Yield | 85.0 MPa | 12300 psi | ISO 527 type 1 A |
| Elongation at Break | 20 % | 20 % | ISO 527 Type 1A |
| Elongation at Yield | 5.0 % | 5.0 % | ISO 527 type 1 A |
| Tensile Modulus | 3.20 GPa | 464 ksi | ISO 527 Type 1A |
| Flexural Strength | 125 MPa | 18100 psi | ISO 178 |
| Flexural Modulus | 3.15 GPa | 457 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | ISO 180/1eA |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 65.0 µm/m-°C @Temperature 23.0 - 85.0 °C |
36.1 µin/in-°F @Temperature 73.4 - 185 °F |
ISO 11359 |
| Melting Point | 263 °C | 505 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ISO 75/Af |
| Flammability, UL94 | V-2 @Thickness 0.380 mm |
V-2 @Thickness 0.0150 in |
1210 |
| V-2 @Thickness 0.800 mm |
V-2 @Thickness 0.0315 in |
1210 | |
| V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
1210 | |
| Glow Wire Test | 960 °C | 1760 °F | ISO 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 4.00e+14 ohm-cm | 4.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 2.9 | 2.9 | IEC 60250 |
| Dielectric Strength | 27.0 kV/mm | 686 kV/in | IEC 60243 |
| Dissipation Factor | 0.020 | 0.020 | IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 250 - 280 °C | 482 - 536 °F | |
| Front Barrel Temperature | 270 - 300 °C | 518 - 572 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 260-290°C |