Polymer Property : Flexural Strength = 125 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Strength 125 MPa
18100 psi
Plastcom SLOVAMID 6/66 FRc 3 TS PA6/66, flame retardant
FeaturesDetermined for electrotechnical use. Delivered in natural colour. PA 6 + PA 66 alloy for injection moulding with increased flammability resistance, with nonhalogen flame retardant. Excellent..
Flexural Strength 125 MPa
18100 psi
1.3 mm/min, 50 mm span; ASTM D790
Ovation Polymers Nemcon™ E-CPC/X1 Polycarbonate Alloy
PC Alloy-ESD Range Electrical Conductivity with High HDT and improved processability.Information provided by Ovation Polymers
Flexural Strength 125 MPa
18100 psi
ASTM D790
Premix Premi-Glas® 1240-20 Fiberglass Reinforced Thermoset Thick Molding Compound
Premi-Glas® 1240-20 is a fiberglass reinforced thermoset Thick Molding Compound for general purpose applications requiring thermal stability and stiffness.Key features and benefits are:Excellent st..
Flexural Strength 125 MPa
18100 psi
ASTM D790
Premix Premi-Glas® 2203-20 CR-SX Fiberglass Reinforced Thermoset SMC
Premi-Glas® 2203-20 CR-SX is a fiberglass reinforced thermoset sheet molding compound for electrical and flame retardant applications.Key features and benefits are:Excellent stiffness to weight rat..
Flexural Strength 125 MPa
18100 psi
ASTM D790
Premix Premi-Glas® 2205-20 CRSX Polyester SMC
Premi-Glas® 2205-20 CR-SX is a 20% fiberglass reinforced Sheet Molding Compound formulated for condensate pan applications requiring chemical resistance, heat resistance, dimensional stability, we..
Flexural Strength <= 125 MPa
<= 18100 psi
ISO 178
Polykemi AB POLYfill PPH GF15030 PD2 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled
Information provided by Polykemi AB
Flexural Strength 125 MPa
18100 psi
ISO 178
Perstorp Compounds Aminel FX Melamine
Organically reinforced melamine material with excellent flow properties and high flexibility suitable for applications involving high complexity and surface demands.Information provided by Perstorp ..
Flexural Strength 125 MPa
18100 psi
ISO 178
Nilit FRIANYL A63 KV40 Nylon 6.6 for injection molding, 40% glass ball reinforced
Nylon 6.6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Flexural Strength 125 MPa
18100 psi
Lehmann & Voss LUVOCOM® 1105-8174 PEEK, with PTFE, lubricant modified
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Chemical and hydrolysis resistance parts, non flammable.Improved friction and wear behavio..
Flexural Strength 125 MPa
18100 psi
Lehmann & Voss LUVOCOM® 80-7884 Polyacetal-copolymer, with carbon fiber
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts; low thermal coefficient of expansion.Electrically conductive, suitable for..
Flexural Strength 125 - 126 MPa

@Temperature 20.0 °C
18100 - 18300 psi

@Temperature 68.0 °F
3-point
Morgan Advanced Ceramics Steatite 22 Steatite
Good balance of electrical properties. Highly cost-effective for volume production of domestic component.
Flexural Strength 125 MPa
18100 psi
Lehmann & Voss LUVOCOM® 80-8072 Polyacetal-copolymer, with carbon fiber
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts; low thermal coefficient of expansion.Electrically conductive, suitable for..
Flexural Strength 125 MPa
18100 psi
ASTM D790
Solvay TECHNYL® A 221 PA66, DRY
Description TECHNYL ® A 221 is an unreinforced polyamide 66, medium viscosity, for injection molding, with a special crystallizing agent, for fast cycles. It is available in natural colors. Benef..
Flexural Strength 125 MPa
18100 psi
ISO 178
Solvay TECHNYL® B 218 Black 21 N PA66/6, DRY
Description: Unreinforced copolyamide PA 66/6 , heat stabilized , medium viscosity, for injection molding.Available in: EuropeProduct Applications: TECHNYL® B 218 offers all of the primary proper..
Flexural Strength 125 MPa
18100 psi
DIN 54352
Schwartz Technical Plastics LAMIGAMID® 510 Polyethylene Terephthalate
Application: friction bearings, wear linersInformation provided by Schwartz Technical Plastics GmbH
Flexural Strength 125 MPa
18200 psi
ASTM D790
Techmer ES Elastoblend® PA6/6 GF13 IM2 HS L 13% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 13% Filler by WeightAdditive: Heat Stabilizer, Lubricant and Impact ModifierFeatures: Heat Stabilized, Lubri..
Flexural Strength 125 MPa
18100 psi
ASTM D790
Solvay Specialty Polymers Veradel® 3300 PREM Polyethersulfone (PESU)
Veradel® polyethersulfone (PESU) is transparent and offers high heat deflection temperatures, excellent toughness and dimensional stability, and resistance to steam, boiling water, and mineral ac..
Flexural Strength 125 MPa
18100 psi
ASTM D 790
SABIC Innovative Plastics Valox® AB9515 ABS+PBT (Asia Pacific)
This data was supplied by SABIC-IP for the Asia Pacific region.
Flexural Strength 125 MPa
18100 psi
ASTM D790
Solvay TECHNYL® A 217 PA66, DRY
Description: TECHNYL ® A 217 is an unreinforced polyamide 66, heat stabilized, standard viscosity, for injection molding. It is available in black color.Benefits: This product offers all the prim..
Flexural Strength 125 MPa
18100 psi
ASTM D790
Teknor Apex Sinpolene GPP1630 Polypropylene
Availability: Africa & Middle East; Latin America; Asia Pacific; South America Additive: Glass Fiber Reinforcement, 30% Filler by Weight Features: Good Dimensional Stability; High Heat Resistance; ..
Flexural Strength 125 MPa
18100 psi
ISO 178
Unitika A3030N-2 PA6, 30% Mineral Reinforced, Dry
Information provided by Unitika Ltd.
Flexural Strength 125 MPa
18100 psi
ISO 178-93
Wellman Wellamid® MR409 22H-NBK4 40% Mineral Reinforced Nylon 66
Description: Mineral Reinforced Nylon 66Information provided by Wellman.
Flexural Strength 125 MPa
18100 psi
dry; ISO 178
DSM Novamid® 3010N 5-SL4-3X NAT PA66 FR
Low Viscosity, Molding Release, 30% Glass Reinforced
Flexural Strength 125 MPa
18100 psi
ISO 178
Celanese VECTRA MT4350 LCP, 40% Medical Technology
Mineral filled grade with low warp, easy flow and smooth surface appearance.Information provided by Celanese
Flexural Strength 125 MPa
18100 psi
ASTM D790
Celanese Celstran® PA66-SF6-02 PA66, 6% Stainless Steel Reinforced
6% stainless steel reinforced nylon 6/66% stainless steel fiber reinforced, heat stabilized nylon 6/6Celstran can be processed on a standard injection molding unit.Information provided by Celanese
Flexural Strength 125 MPa
18100 psi
ISO Data
BASF Ultramid® A3EG3 15% Glass Filled PA66 (Conditioned)
Ultramid A3EG3 is a 15% glass fiber reinforced injection molding PA66 grade. It conforms to FDA requirements of 21 CFR 177.1500.
Flexural Strength 125 MPa
18100 psi
ISO 178
Celanese VECTRA A430 LCP, 25% Specialty
Provides many of the characteristics of A130 with added lubricity. Suitable for applications requiring excellent wear characteristics. Excellent electrical properties at high frequencies. LCP/PTF..
Flexural Strength 125 MPa
18100 psi
2 mm/min; ISO 178
Hexion Bakelite™ EP 8412 Epoxy Resin, High Arc Resistance, Improved Electrical Properties, Low Shrinkage
Epoxy molding compound, inorganically filled, glass fiber reinforced, heat resistant, dimensionally stable, good electrical and mechanical properties, very good chemical resistance, low viscosity, U..
Flexural Strength 125 MPa
18100 psi
ASTM Test
Styrolution Luran® 368 R SAN
General-purpose grade with well-balanced properties intended for both injection molding and extrusion.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS.
Flexural Strength 125 MPa
18100 psi
ASTM D790
Solvay TECHNYL® A 218 PA66, 33% glass fiber, DRY
Standard viscosity, heat stabilized for injection molding. It is available in natural and black colors.Benefits: This product offers all the primary properties of unreinforced polyamide 66. In addit..