- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 486 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 486 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ASTM D-648 |
| PlastiComp Complet® LCF50 - PA66 Nylon 66, 50% Long Carbon Fiber Reinforced Complēt® long-fiber reinforced pellets are manufactured to exceed expectation for quality and performance.Nylon 66 with 50% carbon fiber reinforcementInformation provided by PlastiComp, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ASTM D-648 |
| PlastiComp Velocity® LCF40-PA66 High Flow Nylon 66, 40% Long Carbon Fiber This compound complies with European Union Directive 2002/95/EC Restriction of Hazardous Substances (RoHS).Information provided by PlastiComp, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ASTM D648 |
| Oxford Polymers Oxnilon 66-50GF 50% Glass Fiber Filled Nylon 66 for Injection Molding 50% Glass Fiber Filled Nylon 66 for Injection MoldingInformation provided by Oxford Polymers. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C @Thickness 3.18 mm |
486 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Nymax™ GF 1200 A 43 Natural Polyamide 66 (Nylon 66) The Nymax® GF 1200 Series of glass fiber-reinforced nylon 6/6 compounds have been specifically formulated for applications requiring high stiffness, tensile properties, heat resistance, and durabil.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | Annealed; ASTM D648 |
| Solvay Specialty Polymers AvaSpire® AV-848 Polyaryletherketone (PAEK)
(Unverified Data**) AvaSpire® AV-848 is a high-temperature, polyaryletherketone (PAEK) that offers several key performance advantages over comparable grades of PEEK above 150°C, including better dimensional stability.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ISO 75, ASTM D648 |
| Nilit Nilamid A3 H7 G7 35% Glass Reinforced PA66 Description: Nilamid A3 H7 G7 is a 35% glass fiber reinforced NYLON 66 with a high heat stabilization. This product combines good overall mechanical performance and impact strength with ease of proc.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP RCL26 PA6.6 LNP* LUBRICOMP* RCL26 is a compound based on Nylon 66 containing 30% Carbon Fiber, 10% PTFE. Added features of this grade include: Wear Resistant, Electrically Conductive. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C @Thickness 3.20 mm |
486 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP RFL36L PA 66 LNP* LUBRICOMP* RFL36L is a compound based on Nylon 66 resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant, Low Extractible. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C @Thickness 3.20 mm |
486 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP RFL36L PA 66 (Asia Pacific) LNP* Lubricomp* RFL36L is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Low Extractible. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP RFN1ASXS PA 66 (Europe-Africa-Middle East) LNP* Lubricomp* RFN1ASXS is a compound based on Nylon 66 resin containing Glass Fiber, MOS2. Added features of this material include: Heat Stabilized. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | Annealed; ASTM D648 |
| Solvay Specialty Polymers AvaSpire® AV-848 Polyaryletherketone (PAEK) AvaSpire® AV-848 is a high-temperature, polyaryletherketone (PAEK) that offers several key performance advantages over comparable grades of PEEK above 150°C, including better dimensional stabi.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C @Thickness 3.20 mm |
486 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP RC004SXS PA 66 LNP* THERMOCOMP* RC004SXS is a compound based on Nylon 66 containing 20% Carbon Fiber. Added feature of this grade includes: Heat Stabilized, Electrically Conductive. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP RC008H PA 66 LNP THERMOCOMP* RC008H is a compound based on Nylon 66 resin containing 40% Carbon Fiber. Added features of this material include: Electrically Conductive, Healthcare. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C @Thickness 3.20 mm |
486 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP RF007H PA 66 LNP* Thermocomp* RF007H is a compound based on Nylon 66 containing glass fiber. Added feature includes: Healthcare. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP VERTON RX06424 PA 66 (Asia Pacific) LNP VERTON* RX06424 is a compound based on Nylon 66 resin containing Long Glass. Added features of this material include: Easy Molding. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ASTM D648 |
| A. Schulman Aqualoy® 645 Glass Fiber Reinforced Hydrolysis Resistant Nylon 66 Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ASTM D648 |
| A. Schulman Aqualoy® 645 Glass Fiber Reinforced Hydrolysis Resistant Nylon 66 Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ASTM D648 |
| A. Schulman Aqualoy® 645 Glass Fiber Reinforced Hydrolysis Resistant Nylon 66 Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | DAM; ISO 75-1/-2 |
| DuPont Performance Polymers Zytel® 70G33L BK031 Nylon 66
(Unverified Data**) 33% Glass Reinforced Polyamide 66Zytel 70G33L BK031 is a 33% glass fiber reinforced black polyamide 66 resin for injection molding.Information provided by DuPont Performance Polymers |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ASTM D648 |
| E-Polymers TEKAMID® TA250G33 33% Glass Fiber Reinforced PA66, DAM 33% Glass Fiber Reinforced, Good surfaceInformation provided by E-Polymers Co. Ltd. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ISO 75-2/A |
| Ascend Performance Materials VYDYNE® R543 Nylon, 43% Glass Reinforced, DAM Vydyne® R543 is general purpose, 43% glass-fiber reinforced PA66 resin. Available in natural, it is an injection-molding grade resin that is lubricated for machine fee, flow and mold release. Glass.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | Unannealed; ISO 75-2/A |
| Ascend Performance Materials Vydyne® R543H BK02 Nylon 66, 43% Glass Reinforced, DAM Vydyne® R543H BK02 is general-purpose, 43% glass-fiber reinforced PA66 resin. Available in black, it is an injection-molding grade resin that is lubricated for machine feed, flow and mold release. .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ASTM Test |
| BASF Ultramid® 1503-2 BK ND3007 33% Glass Filled PA66 (Dry) Ultramid 1503-2 BK ND3007 is a 33% glass reinforced, heat stabilized, pigmented black injection molding PA6/6. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ASTM Test |
| BASF Ultramid® 1503-2 NF2004 33% Glass Filled PA66 (Dry) Ultramid 1503-2 NF2004 is a 33% glass reinforced, heat stabilized injection molding PA6/6. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ASTM D648 |
| A. Schulman ComAlloy E-16901B PPS Alloy, Electrically Conductive - Carbon Fiber Filled Data provided by the manufacturer, ComAlloy International Company.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ASTM D648 |
| A. Schulman ComAlloy E-16902N PPS Alloy, Electrically Conductive - Stainless Steel Fiber Filled Data provided by the manufacturer, ComAlloy International Company.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics LNP STAT-KON RC008 PA 66 (Europe-Africa-Middle East) LNP* Stat-kon* RC008 is a compound based on Nylon 66 resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Verton RV00CEU PA 66 (Europe-Africa-Middle East) LNP* VERTON* RV00CEU is a compound based on PA 66 resin containing Long Glass Fiber. Added features include; Easy Molding, UV Stabilized.This data was supplied by SABIC-IP for the Europe-Africa-Midd.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP VERTON RX06479 PA 66 LNP VERTON* RX06479 is a compound based on Nylon 66 resin containing 35% Long Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized, UV Stabilized, Structural |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | DAM; ISO 75-1/-2 |
| DuPont Performance Polymers Zytel® 70G35HSRX BK099 Nylon 66
(Unverified Data**) Zytel® 70G35HSRX BK099 a 35% glass reinforced, heat stabilized, hydrolysis resistant PA66 for injection molding. Developed for applications designed for direct overmolding of gaskets onto thermopla.. |
|||