Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ASTM D-648 |
PlastiComp Complet® LCF50 - PA66 Nylon 66, 50% Long Carbon Fiber Reinforced Complēt® long-fiber reinforced pellets are manufactured to exceed expectation for quality and performance.Nylon 66 with 50% carbon fiber reinforcementInformation provided by PlastiComp, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ASTM D648 |
Nylene® PA6/6 Glass Filled 5143 HS Nylon 6/6 43% Glass Filler; Property data for dry as molded samples.ALM, Nylene Canada, and Custom Resins are all operting companies of Polymeric Resources Corporation. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ASTM D-648 |
PlastiComp Velocity® LCF40-PA66 High Flow Nylon 66, 40% Long Carbon Fiber This compound complies with European Union Directive 2002/95/EC Restriction of Hazardous Substances (RoHS).Information provided by PlastiComp, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ASTM D-648 |
PlastiComp Velocity® LCF50-PA66 High Flow Nylon 66, 50% Long Carbon Fiber This compound complies with European Union Directive 2002/95/EC Restriction of Hazardous Substances (RoHS).Information provided by PlastiComp, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 485 °F | ASTM D648 |
Polymer Resources NY66-G43-[color]-H Nylon 66, 43% Glass Reinforced, Heat Stabilized Nylon 66, 43% Glass Reinforced, Heat Stabilized, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylo.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 252 °C @Thickness 3.18 mm |
486 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
PolyOne Edgetek® NN-30GF/000 Polyamide 66 (Nylon 66) The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for .. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
SABIC Innovative Plastics LNP LUBRICOMP RCL34 PA 66 (Europe-Africa-Middle East) LNP* Lubricomp* RCL34 is a compound based on Nylon 66 resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
SABIC Innovative Plastics LNP LUBRICOMP RFN1ASXS PA 66 (Europe-Africa-Middle East) LNP* Lubricomp* RFN1ASXS is a compound based on Nylon 66 resin containing Glass Fiber, MOS2. Added features of this material include: Heat Stabilized. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 485 °F | Unannealed; ASTM D648 |
Techmer ES Luriblend® PA6/6 CF10 TL15 BK 10% Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 10% Filler by WeightAdditive: PTFE + Silicone Lubricant(15%)Features: Lubricated and Good Wear ResistanceAppearance: Blac.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 485 °F | Unannealed; ASTM D648 |
Techmer ES Luriblend® PA6/6 CF20 TL15 BK 20% Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 20% Filler by WeightAdditive: PTFE Lubricant(15%) Features: Lubricated, Good Wear Resistance and Low Friction Appearance:.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 485 °F | Unannealed; ASTM D648 |
Techmer ES Luriblend® PA6/6 CF20 TS15 BK 20% Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 20% Filler by WeightAdditive: PTFE Lubricant(10%) and Silicone Lubricant Features: Lubricated, Good Wear Resistance and L.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 252 °C @Thickness 3.20 mm |
486 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics LNP THERMOCOMP RC004SXS PA 66 LNP* THERMOCOMP* RC004SXS is a compound based on Nylon 66 containing 20% Carbon Fiber. Added feature of this grade includes: Heat Stabilized, Electrically Conductive. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 252 °C @Thickness 3.20 mm |
486 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics LNP THERMOCOMP RF006XXY PA 66 LNP* Thermocomp* RF006XXY is a compound based on Nylon 66 containing 30% Glass Fiber. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 252 °C @Thickness 3.20 mm |
486 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics LNP THERMOCOMP RF007SXP PA 66 LNP* THERMOCOMP* RF007SXP is a compound based on Nylon 66 containing 35% Glass Fiber. Added feature of this material includes: Heat Stabilized. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 252 °C @Thickness 3.20 mm |
486 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics LNP THERMOCOMP RX10405H PA 66 LNP* Thermocomp* RX10405H is a compound based on Nylon 6/6 containing Carbon Fiber. Characteristics of this grade are: Healthcare. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 485 °F | Unannealed; ASTM D648 |
Techmer ES HiFill FR® PA6/6 GF25 FR-N IM3 BK 25% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 25% Filler by WeightAdditive: Impact ModifierFeatures: Flame Retardant, Halogen Free and Impact ModifiedAppearance: BlackI.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
SABIC Innovative Plastics LNP STAT-KON OE006C1 PPS - Linear LNP* STAT-KON* OE006C1 is a compound based on PPS - Linear resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 485 °F | ASTM D648 |
Chase Plastics CP Pryme® NN130GMD2 (COND, 50% RH) Nylon 66, 30% Glass Fiber Reinforced, 2% MoS2 Lubricated Information provided by Chase Plastics. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 485 °F | ASTM D648 |
Chase Plastics CP Pryme® NN130GMD2 (DAM) Nylon 66, 30% Glass Fiber Reinforced, 2% MoS2 Lubricated Information provided by Chase Plastics. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 485 °F | ASTM D648 |
Chase Plastics CP Pryme® NN130GMD2HS (COND, 50% RH) Nylon 66, 30% Glass Fiber Reinforced, 2% MoS2 Lubricated, Heat Stabilized Information provided by Chase Plastics. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 485 °F | ASTM D648 |
Chase Plastics CP Pryme® NN143GL (DAM) Nylon 66, 43% Glass Fiber Reinforced, Internally Lubricated Information provided by Chase Plastics. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ASTM D648 |
E-Polymers TEKAMID® TA250G60 60% Glass Fiber Reinforced, High Modulus PA66 Resin Polyamide (Nylon) Resin. TEKAMID is widely being used in manufacturing of automotive and industrial parts with its outstanding mechanical, thermal and chemical properties.T-series: Impact modified,.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | Unannealed; ISO 75-2/A |
Ascend Performance Materials Vydyne® R540H Nylon 66, 40% Glass Reinforced, DAM Vydyne® R540H is general-purpose, heat-stabilized, hydrolysis-resistant, 40% glass-fiber reinforced PA66 resin. Available in natural, it is specifically designed to maximize the retention of physic.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ISO 75-2/A |
Ascend Performance Materials VYDYNE® R543 Nylon, 43% Glass Reinforced, DAM Vydyne® R543 is general purpose, 43% glass-fiber reinforced PA66 resin. Available in natural, it is an injection-molding grade resin that is lubricated for machine fee, flow and mold release. Glass.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | Unannealed; ISO 75-2/A |
Ascend Performance Materials Vydyne® R543H BK02 Nylon 66, 43% Glass Reinforced, DAM Vydyne® R543H BK02 is general-purpose, 43% glass-fiber reinforced PA66 resin. Available in black, it is an injection-molding grade resin that is lubricated for machine feed, flow and mold release. .. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ISO 75-2/A |
Ascend Performance Materials Vydyne® R543H Nylon 66, 43% Glass Filled, Dry as Molded Vydyne® R543H is general-purpose, 43% glass-reinforced PA66 resin. Available in natural, it is an injection-molding grade resin that is lubricated for improved machine feed, flow and mold release. .. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ASTM D648 |
Ashley Polymers Ashlene® 528L-43G Nylon 66, 43% Glass Reinforced A general purpose 43% glass reinforced nylon resin.Data provided by the manufacturer |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ASTM Test |
BASF Ultramid® 1503-2 NF2004 33% Glass Filled PA66 (Dry) Ultramid 1503-2 NF2004 is a 33% glass reinforced, heat stabilized injection molding PA6/6. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ASTM D648 |
Asia International Enterprise (Hong Kong) 60G8-43GF Nylon 66, 43% Filled Information provided by Asia International Enterprise (Hong Kong) Ltd. |