Solvay Specialty Polymers Amodel® A-1133 NL WH 886 Polyphthalamide (PPA) (discontinued **)

Category	Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 10% Glass Fiber Reinforced
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Solvay Specialty Polymers Amodel® A-1133 NL WH 886 Polyphthalamide (PPA) (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Amodel A-1133 NL WH 886 resin is a glass reinforced polyphthalamide (PPA ) which is distinguished by its high-reflectivity white color. This grade features a high deflection temperature for compatibility with SMT processes, and low moisture absorption. - White: A-1133 NL WH 886Information provided by Solvay Specialty Polymers.

Physical Properties	Metric	English	Comments
Density	1.61 g/cc	0.0582 lb/in³	ISO 1183/A
Water Absorption	0.12 % @Time 86400 sec	0.12 % @Time 24.0 hour	ASTM D570
Linear Mold Shrinkage, Flow	0.0020 cm/cm	0.0020 in/in	ASTM D955
Linear Mold Shrinkage, Transverse	0.0040 cm/cm	0.0040 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	125	125	R-Scale; ASTM D785
Tensile Strength	120 MPa	17400 psi	ASTM D638
Elongation at Break	1.5 %	1.5 %	ASTM D638
Tensile Modulus	9.17 GPa	1330 ksi	ASTM D638
Flexural Strength	175 MPa	25400 psi	ASTM D790
Flexural Modulus	7.52 GPa	1090 ksi	ASTM D790
Poissons Ratio	0.41	0.41	ASTM E132
Shear Modulus	3.25 GPa	471 ksi	Calculated
Izod Impact, Notched	0.270 J/cm	0.506 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	20.0 µm/m-°C @Temperature 160 - 249 °C	11.1 µin/in-°F @Temperature 320 - 480 °F	TMA; ASTM E831
	25.0 µm/m-°C @Temperature 0.000 - 100 °C	13.9 µin/in-°F @Temperature 32.0 - 212 °F	TMA; ASTM E831
CTE, linear, Transverse to Flow	41.0 µm/m-°C @Temperature 0.000 - 100 °C	22.8 µin/in-°F @Temperature 32.0 - 212 °F	ASTM E228
	65.0 µm/m-°C @Temperature 160 - 249 °C	36.1 µin/in-°F @Temperature 320 - 480 °F	ASTM E228
Melting Point	325 °C	617 °F	ASTM D570
Deflection Temperature at 1.8 MPa (264 psi)	250 °C	482 °F	Unannealed; ASTM D648

Processing Properties	Metric	English
Rear Barrel Temperature	304 - 318 °C	579 - 604 °F
Front Barrel Temperature	316 - 329 °C	601 - 624 °F
Melt Temperature	321 - 343 °C	610 - 649 °F
Mold Temperature	135 °C	275 °F
Drying Temperature	120 °C	248 °F
Dry Time	4.00 hour	4.00 hour
Moisture Content	0.060 %	0.060 %

Descriptive Properties	Value	Comments
Appearance	White
Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
Features	Good Chemical Resistance
	Good Color Stability
	High Reflectivity
	Low Moisture Absorption
Filler	Glass Fiber Reinforcement
Forms	Pellets
Generic	PPA
Processing Method	Injection Molding
Uses	Automotive Electronics
	LEDs