Sax Polymers SAXATEC 4120 Acrylonitrile Styrene Acrylate

Category Polymer , Thermoplastic , ASA Polymer , Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded
Manufacturer Sax Polymers
Trade Name SAXATEC
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Sax Polymers SAXATEC 4120 Acrylonitrile Styrene Acrylate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
SAXATEC 4120 is a easy lowing, weatherable ASA injection molding grade, characterized by high impact strength, high stiffness and good resistance to heat distortion.Information provided by SAX Polymers
Physical Properties Metric English Comments
Density 1.07 g/cc
0.0387 lb/in³
Linear Mold Shrinkage 0.0040 - 0.0070 cm/cm
0.0040 - 0.0070 in/in
Melt Flow 21 g/10 min

@Load 10.0 kg,
Temperature 220 °C
21 g/10 min

@Load 22.0 lb,
Temperature 428 °F
from MVR; ISO 1033
Mechanical Properties Metric English Comments
Tensile Strength 62.0 MPa
8990 psi
ISO 527-1
Elongation at Break 10 %
10 %
ISO 527-1
Tensile Modulus 2.70 GPa
392 ksi
ISO 527-1
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
ISO 180/1A
7.00 kJ/m²

@Temperature 23.0 °C
3.33 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1A
Izod Impact, Unnotched (ISO) 40.0 kJ/m²

@Temperature -30.0 °C
19.0 ft-lb/in²

@Temperature -22.0 °F
ISO 180
80.0 kJ/m²

@Temperature 23.0 °C
38.1 ft-lb/in²

@Temperature 73.4 °F
ISO 180
Charpy Impact Unnotched 6.00 J/cm²

@Temperature -30.0 °C
28.6 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
10.0 J/cm²

@Temperature 23.0 °C
47.6 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.500 J/cm²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
0.700 J/cm²

@Temperature 23.0 °C
3.33 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Hot Ball Pressure Test 95.0 °C

@Thickness 2.00 mm
203 °F

@Thickness 0.0787 in
IE/CEN 60335-1
Deflection Temperature at 1.8 MPa (264 psi) 89.0 °C
192 °F
80*10*4 s=60mm; ISO 75-1 a
Vicat Softening Point 104 °C
219 °F
50B; ISO 306
Glow Wire Test 750 °C
1380 °F
IEC 60695-2-12
Processing Properties Metric English Comments
Melt Temperature 220 - 260 °C
428 - 500 °F
Mold Temperature 60.0 - 90.0 °C
140 - 194 °F
Drying Temperature 80.0 °C

@Time 7200 - 21600 sec
176 °F

@Time 2.00 - 6.00 hour
Moisture Content <= 0.20 %
<= 0.20 %