Arkema Group Rilsan® BESN G9 TL Nylon 11, Graphite Filled (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 11 , Nylon 11 with Graphite Filler
Manufacturer Arkema
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Rilsan® BESN G9 TL Nylon 11, Graphite Filled (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Designation ISO 1874-PA11,EHLS,18-010,CD10Grade with graphite filler for tubes extrusion. Available color: steel gray. Light and heat stabilized.No need of lubricant. Low friction coefficient. Good abrasion resistance. High chemical resistance.Example applications: Control cable tubing.ISO data provided by the manufacturer, Arkema.
Physical Properties Metric English Comments
Density 1.09 g/cc
0.0394 lb/in³
Melt Flow 1.0 g/10 min

@Load 2.16 kg,
Temperature 235 °C
1.0 g/10 min

@Load 4.76 lb,
Temperature 455 °F
Mechanical Properties Metric English Comments
Tensile Strength, Yield 45.0 MPa
6530 psi
50 mm/min
Elongation at Break >= 50 %
>= 50 %
Nominal Strain; 50 mm/min
Elongation at Yield 7.0 %
7.0 %
50 mm/min
Tensile Modulus 2.10 GPa
305 ksi
1 mm/min
Charpy Impact Unnotched NB
NB
15.4 J/cm²

@Temperature -30.0 °C
73.3 ft-lb/in²

@Temperature -22.0 °F
Charpy Impact, Notched 0.480 J/cm²
2.28 ft-lb/in²
0.460 J/cm²

@Temperature -30.0 °C
2.19 ft-lb/in²

@Temperature -22.0 °F
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 90.0 µm/m-°C

@Temperature 20.0 °C
50.0 µin/in-°F

@Temperature 68.0 °F
Melting Point 183 °C
361 °F
(Dry)
Deflection Temperature at 0.46 MPa (66 psi) 168 °C
334 °F
Deflection Temperature at 1.8 MPa (264 psi) 56.0 °C
133 °F
Vicat Softening Point 162 °C
324 °F
50°C/hr; 50N
Flammability, UL94 V-2

@Thickness 1.60 mm
V-2

@Thickness 0.0630 in
V-2

@Thickness 3.20 mm
V-2

@Thickness 0.126 in
Electrical Properties Metric English Comments
Electrical Resistivity 5.00e+13 ohm-cm
5.00e+13 ohm-cm
Surface Resistance 6.00e+13 ohm
6.00e+13 ohm
Dielectric Strength 55.0 kV/mm
1400 kV/in
Comparative Tracking Index 600 V
600 V