- Sax Polymers SAXAMID 136F6Q32 Nylon 6, 30% Glass Fiber
Sax Polymers SAXAMID 136F6Q32 Nylon 6, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled , Nylon 6, Glass Filled, Impact Grade |
| Manufacturer | Sax Polymers |
| Trade Name | SAXAMID |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sax Polymers SAXAMID 136F6Q32 Nylon 6, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SAXAMID 136F6Q32 is a high-impact-modified polyamide 6 injection-molding-grade reinforced with 30% glass fibers . Beside the high impact strength at low temperatures this grade shows very good processability.Information provided by SAX Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | ISO 1183 |
| Viscosity Test | 150 cm³/g | 150 cm³/g | H<sub>2</sub>SO<sub>4</sub>; ISO 307 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 96.0 MPa | 13900 psi | 5 mm/min; ISO 527-1 |
| Elongation at Break | 4.0 % | 4.0 % | 5 mm/min; ISO 527-1 |
| Tensile Modulus | 6.80 GPa | 986 ksi | 1 mm/min; ISO 527-1 |
| Flexural Strength | 145 MPa | 21000 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 4.80 GPa | 696 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 18.0 kJ/m² @Temperature -30.0 °C |
8.57 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 21.0 kJ/m² @Temperature 23.0 °C |
9.99 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 78.0 kJ/m² @Temperature -30.0 °C |
37.1 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1U |
| 90.0 kJ/m² @Temperature 23.0 °C |
42.8 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | |
| Charpy Impact Unnotched | 8.50 J/cm² @Temperature -30.0 °C |
40.4 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 9.30 J/cm² @Temperature 23.0 °C |
44.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 1.70 J/cm² @Temperature -30.0 °C |
8.09 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 2.00 J/cm² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 186 °C | 367 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Vicat Softening Point | 187 °C | 369 °F | B/120; ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 290 °C | 500 - 554 °F | |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 7200 - 21600 sec |
176 °F @Time 2.00 - 6.00 hour |
|
| Moisture Content | <= 0.20 % | <= 0.20 % |
Users viewing this material also viewed the following:
- Shandong Rike Chemical HELIâ„¢ HG-50 PVC Processing Aid Series (PA)
- SSAB Tunnplat Docol® DC04 (Fe P04) Deep-drawing Steel
- Solvay TECHNYL® A 217 PA66, Conditioned
- A. Schulman POLYFORT™ FXP 2779U UV Stabilized Copolymer Polypropylene
- Polyplastics TOPAS® 6017 Cyclic Olefin Copolymer (COC) (Asia/Pacific Grade)
- Cheng Yu Plastic PP237G2 Polypropylene, 20% Glass Fiber
- Dow Corning SILASTIC® 7-6840 BIOMEDICAL GRADE LSR, KIT
- ELASTO UK Dryflex® 660800S SEBS Based Material, Semi-Filled Qualities, 80A Hardness, Natural
- CMW® ELKONITE® 10W53 Heat Treatable Copper Tungsten
- MetalTek MTEK H46 Martensitic Stainless Steel
Copyright © lookpolymers.com All Rights Reserved