- Polymer Property : Flexural Modulus = 696 ksi
Polymer Property : Flexural Modulus = 696 ksi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Modulus | 4.80 GPa @Temperature 23.0 °C |
696 ksi @Temperature 73.4 °F |
ISO 178 |
| Polykemi AB POLYfill PPH GF5030 PB Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled Information provided by Polykemi AB |
|||
| Flexural Modulus | 4.80 - 5.50 GPa @Temperature 90.0 - 90.0 °C |
696 - 798 ksi @Temperature 194 - 194 °F |
Average value: 5.15 GPa Grade Count:2 |
| Overview of materials for Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled". Specific grades with glass content between 25.. |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | |
| Plastcom SLOVAMID 6 T 20 PA6, 20% mineral filling FeaturesDecreased shrinkage against the BT types, increased heat application up to 170°C. Increased modulus in tension - strength of the material. PA matrix reduction. Application eg. for tools, fi.. |
|||
| Flexural Modulus | 4.80 - 11.0 GPa | 696 - 1600 ksi | Average value: 8.55 GPa Grade Count:5 |
| Overview of materials for Polyetherketoneetherketoneketone (PEKEKK), Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyetherketoneetherketoneketone (PEKEKK), Glass Fiber Filled". Each property range of values reported i.. |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | conditioned, 2 mm/min; ISO 178-A |
| Lanxess Durethan® BKV 130 H3.0 DUS008 000000 Nylon 6, 30% Glass Fiber PA 6, glass fiber, injection molding, impact modified, heat-aged stabilizedInformation provided by LANXESS. |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP THERMOCOMP AF004 ABS (Europe-Africa-Middle East) LNP* THERMOCOMP* AF004 is a compound based on Acrylonitrile Butadiene Styren resin containing Glass Fiber. |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP THERMOCOMP KB008 Acetal Copolymer LNP THERMOCOMP* KB008 is a compound based on Acetal Copolymer resin containing 40% Glass Bead. |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | 2 mm/min; ISO 178 |
| Sax Polymers SAXAMID 136F6Q32 Nylon 6, 30% Glass Fiber SAXAMID 136F6Q32 is a high-impact-modified polyamide 6 injection-molding-grade reinforced with 30% glass fibers . Beside the high impact strength at low temperatures this grade shows very good proce.. |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | 2 mm/min; ISO 178 |
| Sax Polymers SAXAMID 226F3 Nylon 6.6, 15% Glass Fiber SAXAMID 226F3 is a polyamide 6.6 injection-molding-grade reinforced with 15% glass fibers. This grade is suitable for applications requiring high strength and very good flow properties during proces.. |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | ISO 178 |
| SABIC Innovative Plastics LNP STAT-KON DDF029 PC LNP STAT-KON* DDF029 is a compound based on Polycarbonate resin containing Carbon, Glass Fiber. Added features of this material include: Electrically Conductive. Flame Retardant. |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | 2 mm/min; ISO 178 |
| Sax Polymers SAXAMID 236F4Q32 Nylon 6.6, 20% Glass Fiber SAXAMID 236 F4Q32 is a impact-modified polyamide 6.6 injection-molding-grade reinforced with 20% glass fibers and very good flow properties. It is suitable for applications requiring toughness in co.. |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics NORYL GFN1720 PPE+HIPS Noryl* GFN1720 is a 20% glass fiber reinforced, injection moldable grade. This modified polyphenylene ether resin is designed to deliver a balance of heat, strength and electrical properties. Noryl .. |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics NORYL GFN1720 PPE+HIPS (Asia Pacific) Noryl* GFN1720 is a 20% glass fiber reinforced, injection moldable grade. This modified polyphenylene ether resin is designed to deliver a balance of heat, strength and electrical properties. Noryl .. |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | ASTM D790 |
| PlastxWorld Veroplas PB3150 Nylon 66 15% glass filled injection molding gradeInformation provided by PlastxWorld Inc. |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | ISO 178 |
| Polyram PlusTek PB315G33 Nylon 6 for Injection Molding, 33% Glass Fiber Reinforced, UV and Heat Stabilized 33% Glass fiber reinforced, UV and heat stabilized Nylon 6 for injection molding applications.Information provided by Polyram. |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | ISO 178-93 |
| Wellman Wellamid® GS40-66 22L-Bk1 40% Glass Sphere Filled Nylon 66 Description: Glass Sphere Filled Nylon 66Information provided by Wellman. |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | ASTM-D790 |
| Polyram RamSter PF320G2 PBT, 10% Glass Fiber, Flame Retardant 10% Glass fiber reinforced, flame retardant PBT for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | ASTM-D790 |
| Polyram RamSter PF320G3 PBT, 15% Glass Fiber, Flame Retardant 15% Glass fiber reinforced, flame retardant PBT for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | ISO 178 |
| Polyram RamSter PF321G2 PBT, 10% Glass Fiber, Flame Retardant 10% Glass fiber reinforced, flame retardant PBT for injection molding applications.Information provided by Polyram. |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | DIN 52457 |
| CP-Polymer-Technik Wellamid® 6000/58 GV 15 HWUVCP 15% Glass Fiber Nylon 6, Impact Modified Until -40°C, UV Stabilized, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | ASTM D790 |
| E-Polymers TEKAMID® TB120G15 , 15% Glass Fiber Reinforced PA6, DAM 15% Glass Fiber reinforced, Good surface Information provided by E-Polymers Co. Ltd. |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | DAM; ISO 178 |
| DuPont Performance Polymers Zytel® 70G13L NC010 Nylon 66
(Unverified Data**) 13% Glass Reinforced Polyamide 66Zytel 70G13L NC010 is a 13% glass fiber reinforced polyamide 66 resin for injection molding.Information provided by DuPont Performance Polymers |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | Transverse direction; ISO 178 |
| Azdel Plus U421-B01 42% Directionalized Continuous Fiber Mat / PP Resin Matrix AZDEL® U421-B01 is a glass mat thermoplastic laminate based upon a combination of random oriented continuous fiber mat and oriented fiber mat contained within a polypropylene resin matrix. This co.. |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | ASTM D790 |
| Ashley Polymers Ashlene® 528LSB2-20G Nylon 66, 20% Glass Reinforced A UV Stabilized 20% glass fiber reinforced Nylon 66 designed for parts requiring excellent thermal and dimensional stability and higher strength than conventional resins.Data provided by the manufac.. |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | ASTM D790 |
| Chem Polymer Chemlon 113 G Nylon 66, 13% Glass Fiber Reinforced A 13% glass fiber reinforced nylon 66 offering improved creep resistance, stiffness, tensile strength and dimensional stability over unmodified nylon 66 materials.Data provided by the manufacturer, .. |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | ASTM D790 |
| A. Schulman ComAlloy Hiloy® 632 Nylon 6/6, Glass Reinforced, Flow Enhanced, UL Data provided by the manufacturer, ComAlloy International Company.20% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | ASTM D790 |
| Custom Resins Norpex® GF2 PPE (Polyphenylene Ether), 20% Glass Filled
(discontinued **) Properties for dry as molded samples.Data provided by the manufacturer |
|||