SABIC Innovative Plastics Xenoy® IQ1103R PBT+PC (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Xenoy®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Xenoy® IQ1103R PBT+PC (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Xenoy* Resin iQ1103R - Environmetally responsible, sustainable, and low carbon footprint resin. Xenoy iQ1103R is an unreinforced, impact modified PC + iQ-PBT alloy with excellent low temperature impact, chemical resistance, and a special mold release. Range gray, black colors, limited colors.
Physical Properties Metric English Comments
Specific Gravity 1.19 g/cc
1.19 g/cc
ASTM D792
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Moisture Absorption 0.0800 %
0.0800 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.30 %
0.30 %
ISO 62
Linear Mold Shrinkage, Flow 0.0080 - 0.012 cm/cm

@Thickness 3.20 mm
 0.0080 - 0.012 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 13 g/10 min

@Load 5.00 kg,
Temperature 250 °C
 13 g/10 min

@Load 11.0 lb,
Temperature 482 °F
 ASTM D1238
Melt Index of Compound 12 g/10 min

@Load 5.00 kg,
Temperature 250 °C
 12 g/10 min

@Load 11.0 lb,
Temperature 482 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 46.0 MPa
6670 psi
Type I, 50 mm/min; ASTM D638
47.0 MPa
6820 psi
50 mm/min; ISO 527
Tensile Strength, Yield 45.0 MPa
6530 psi
Type I, 50 mm/min; ASTM D638
49.0 MPa
7110 psi
50 mm/min; ISO 527
Elongation at Break 140 %
140 %
Type I, 50 mm/min; ASTM D638
150 %
150 %
50 mm/min; ISO 527
Elongation at Yield 4.0 %
4.0 %
Type I, 50 mm/min; ASTM D638
4.0 %
4.0 %
50 mm/min; ISO 527
Tensile Modulus 1.95 GPa
283 ksi
1 mm/min; ISO 527
2.05 GPa
297 ksi
50 mm/min; ASTM D638
Flexural Yield Strength 70.0 MPa
10200 psi
2 mm/min; ISO 178
74.0 MPa
10700 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 1.92 GPa
278 ksi
2 mm/min; ISO 178
2.00 GPa
290 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 6.50 J/cm
12.2 ft-lb/in
ASTM D256
6.00 J/cm

@Temperature -30.0 °C
 11.2 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Notched (ISO) 55.0 kJ/m²
26.2 ft-lb/in²
80*10*4; ISO 180/1A
47.0 kJ/m²

@Temperature -30.0 °C
 22.4 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 5.50 J/cm²
26.2 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 50.0 J

@Temperature 23.0 °C
 36.9 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 90.0 µm/m-°C

@Temperature -40.0 - 150 °C
 50.0 µin/in-°F

@Temperature -40.0 - 302 °F
 ASTM E 831
90.0 µm/m-°C

@Temperature -30.0 - 80.0 °C
 50.0 µin/in-°F

@Temperature -22.0 - 176 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 95.0 µm/m-°C

@Temperature -40.0 - 150 °C
 52.8 µin/in-°F

@Temperature -40.0 - 302 °F
 ASTM E 831
95.0 µm/m-°C

@Temperature -30.0 - 80.0 °C
 52.8 µin/in-°F

@Temperature -22.0 - 176 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 99.0 °C

@Thickness 3.20 mm
 210 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 76.0 °C
169 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
75.0 °C

@Thickness 3.20 mm
 167 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Vicat Softening Point 115 °C
239 °F
Rate B/50; ISO 306
117 °C
243 °F
Rate B/120; ISO 306
117 °C
243 °F
Rate B/50; ASTM D1525