SABIC Innovative Plastics NORYL PCN2910 PPE+PS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL PCN2910 PPE+PS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
35% Glass/Mica filled. High modulus and tight tolerance molding for the chassis market.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.38 g/cc | 1.38 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0025 - 0.0030 cm/cm | 0.0025 - 0.0030 in/in | SABIC Method |
| Melt Flow | 11 g/10 min @Load 2.16 kg, Temperature 300 °C |
11 g/10 min @Load 4.76 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 115 MPa | 16700 psi | Type I, 10 mm/min; SABIC - Japan Method |
| Tensile Strength, Yield | 106 MPa | 15400 psi | 5 mm/min; ISO 527 |
| 123 MPa | 17800 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.3 % | 1.3 % | 5 mm/min; ISO 527 |
| 1.5 % | 1.5 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 5.0 % | 5.0 % | Type I, 10 mm/min; SABIC - Japan Method |
| Tensile Modulus | 10.6 GPa | 1540 ksi | 1 mm/min; ISO 527 |
| 11.37 GPa | 1649 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 159 MPa | 23100 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| 160 MPa | 23200 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 8.94 GPa | 1300 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| 9.13 GPa | 1320 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.680 J/cm | 1.27 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.31 J/cm | 6.20 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | 80*10*4; ISO 180/1U |
| Charpy Impact Unnotched | 2.00 J/cm² | 9.52 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179/2C |
| Dart Drop, Total Energy | 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 2.10 - 3.30 µm/m-°C @Temperature -30.0 - 30.0 °C |
1.17 - 1.83 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
| Deflection Temperature at 1.8 MPa (264 psi) | 129 °C | 264 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 125 °C @Thickness 6.40 mm |
257 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 140 °C | 284 °F | Rate B/50; ASTM D1525 |
| UL RTI, Electrical | 65.0 °C | 149 °F | UL 746B |
| UL RTI, Mechanical with Impact | 65.0 °C | 149 °F | UL 746B |
| UL RTI, Mechanical without Impact | 65.0 °C | 149 °F | UL 746B |
| Flammability, UL94 | V-1 @Thickness 1.50 mm |
V-1 @Thickness 0.0591 in |
UL 94 |
| V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
UL 94 | |
| 5VB @Thickness 2.30 mm |
5VB @Thickness 0.0906 in |
UL 94 |
Users viewing this material also viewed the following:
- Multibase Nylex™ 2112 FR V0 Natural Polyamide + PP
- PlastiComp Velocity® LGF50-PA66 High Flow Nylon 66, 50% Long Glass Fiber
- Chevron Phillips Ryton® R-7-220NA Polyphenylene Sulfide Resin (discontinued **)
- Ineos L06Z-00 Polypropylene Impact Copolymer
- Momentive Performance Materials RTV159 High Strength Silicone Adhesive Sealant, Red
- Momentive Performance Materials RTV5812 One-Component, Modified Alkoxy Adhesive Sealant, White
- LATI Latilub 73/13-15T G/15 POM, 15% Glass Fiber Reinforced, PTFE Filled
- BLUESTAR 203G30 PBT, 30% Glass Filled
- 3M 93010LE High Strength Double Coated Tape with Adhesive 300LSE
Copyright © lookpolymers.com All Rights Reserved