- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 257 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 257 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C @Thickness 3.20 mm |
257 °F @Thickness 0.126 in |
ASTM D648 |
| Ovation Polymers RIGITRON 10001 Polycarbonate PC – Impact Modified, high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared according to.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | 0.125 in bar; ASTM D648 |
| Network Polymers PC-1029 AS/P Description: Antistatic PolycarbonateInformation provided by Network Polymers Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Lexan® 243R PC (Europe-Africa-Middle East) LEXAN 243R is a medium viscosity multi purpose UV stabilized grade and contains release agent to ensure easy processing. This grade is UL94-V2 at 0.8 mm approved. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C @Thickness 3.20 mm |
257 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® 905AU PC (Asia Pacific) LEXAN resin grade 905AU is a flame retardant polycarbonate featuring non brominated and non chlorinated FR systems, with good flow, and good UV stability. It is available in all colors, intended to .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Lexan® 9945A PC (Asia Pacific) Lexan* resin 9945A Polycarbonate (PC)is a non-filled, injection moldable grade. This non-chlorinated, non-brominated PC has an UL-94 V0 rating at 1.8 mm. Lexan resin 9945A is available in clear tr.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Lexan® 9945A PC (Europe-Africa-Middle East) Lexan* resin 9945A Polycarbonate (PC)is a non-filled, injection moldable grade. This non-chlorinated, non-brominated PC has an UL-94 V0 rating at 1.8 mm. Lexan resin 9945A is available in clear tr.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Lexan® EXL1036 PC Copolymer Lexan* EXL1036 polycarbonate (PC) siloxane copolymer resin is a UV stabilized high viscosity grade designed for (co-)extrusion. This resin offers extreme low temperature (-60 C) ductility and good h.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Lexan® EXL1036 PC Copolymer (Asia Pacific) Lexan* EXL1036 polycarbonate (PC) siloxane copolymer resin is a UV stabilized high viscosity grade designed for (co-)extrusion. This resin offers extreme low temperature (-60 C) ductility and good h.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Lexan® EXL1112 PC Copolymer Lexan* EXL1112 polycarbonate (PC) siloxane copolymer resin is a high flow opaque injection molding (IM) grade. This resin offers good low temperature (-20 C) ductility in combination with excellent .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Lexan® EXL1112 PC Copolymer (Asia Pacific) Lexan* EXL1112 polycarbonate (PC) siloxane copolymer resin is a high flow opaque injection molding (IM) grade. This resin offers good low temperature (-20 C) ductility in combination with excellent .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Lexan® EXL1132 PC Copolymer Lexan* EXL1132 polycarbonate (PC) siloxane copolymer resin is a high flow, UV stabilized injection molding grade. This resin offers good low temperature (-20 C) ductility in combination with high fl.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C @Thickness 3.20 mm |
257 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® LI1813R PC Low-viscosity multi-purpose PC having low levels of ionics species. Internal mold release and UV-stabilized. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Lexan® SLX2471T PC Copolymer Medium viscosity PC copolymer blend with enhanced UV stabilization and added release agent. V2 rated. Available in transparent and tinted colors |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP FARADEX DS0036I PC LNP* FARADEX* DS0036I is a compound based on Polycarbonate resin containing 15% Stainless Steel. Added features of this material include: Electrically Conductive, EMI/RFI Shielding, High Impact, No.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Lexan® HP3NREU PC (Europe-Africa-Middle East) Medium flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO and steam sterilizable. Contains no mo.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | ASTM D648 |
| Asahi Kasei Tenac® LT805 Acetal Homopolymer, Low Friction Grade
(discontinued **) Excellent friction and wear on metals.Applications: Keyboard parts, bearings for office machines, gears.This product is not a part of the standard product line dated 2003. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | |
| LATI Laril 13 G/20-V1 PPOm, 20% Glass Fiber Reinforced, Flame Retardant Modified Polyphenylene Oxide (PPOm) based compound. Glass fibers. UL94 V-1 classified, with brominated flame retardants, PBB/PBDE and antimony trioxide free. High dimensional stability. Good thermal.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C @Thickness 6.40 mm |
257 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL PX9406P PPE+HIPS (Asia Pacific) Nonbrominated, nonchlorinated, flame retarded. Improved productivity and reliability. 125dc HDT. UL94 V-0 rated. Electrical applications. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics PC1500 PC PC1500 resin is a medium-high flow (MFR = 15 at 300ºC/1.2kg), heat stabilized, polycarbonate product designed for use in the custom compounding market. It does not contain UV stabilizer or mold .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C @Thickness 3.20 mm |
257 °F @Thickness 0.126 in |
ASTM D648 |
| SABIC Innovative Plastics PC1500 PC (Europe-Africa-Middle East) PC1500 resin is a medium-high flow (MFR = 15 at 300?C/1.2kg), heat stabilized, polycarbonate product designed for use in the custom compounding market. It does not contain UV stabilizer or mold rel.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C @Thickness 3.20 mm |
257 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON DD000P PC LNP* STAT-KON* DD000P is a compound based on Polycarbonate resin containing Carbon. Added features of this material include: Electrically Conductive, Exceptional Processing. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | Unannealed; ISO 75-2/A |
| Styron CALIBREâ„¢ 201-10 Polycarbonate Resin Overview: CALIBREâ„¢ 201-10 is produced in compliance with the US Food and Drug Administration (FDA) and EU food contact regulations. It provides excellent impact resistance, heat distortion resi.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C @Thickness 6.40 mm |
257 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL HM3020H PPE+PS (Asia Pacific) PPE+PS GF+MF 30% filled, FR V-1, high flow |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | ISO 75-1, 2 |
| Polyplastics Duracon® TR-20 Acetal Co-polymer (POM), Mineral filling, Mineral filling, High rigidity, Low warpage DURACON® is a crystalline thermoplastic acetal copolymer. The primary raw material trioxane, a trimer of formaldehyde.The thermoplastic adopts a copolymer structure in which polyoxymethylene (-C-O).. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | ISO 75-1, 2 |
| Polyplastics Duranex® 361SA Polybutylene Terephthalate (PBT), Low density, Low wear, GF filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | DIN 53461 |
| Polyram RamTough PZ500 Polycarbonate, Flame Retardant Flame retardant polycarbonate for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | GB/1634 |
| Zhejiang Juner PC-A7-5 Top-Grade Flame Retardant UV-Resistant Applications: Top-Grade Wall Switch, BracketInformation provided by Zhejiang Juner New Materials Co, Ltd. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | DAM; ISO 75-1/-2 |
| DuPont Performance Polymers Zytel® HTN FE8200 BK431 Polyphthalamide (PPA)
(Unverified Data**) Unreinforced Toughened PPA High Performance Polyamide Zytel HTNFE8200 BK431 is an unreinforced toughened heat stabilized lubricated high performance polyamide resin for injection molding. It is also.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C @Thickness 3.20 mm |
257 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® HFD4471 PC Lexan* HFD4471 is a 10% glass filled, medium flow, impact modified, injection moldable grade designed for high flow and superior surface appearance. HFD4417 has enhanced mold release, impact ductili.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C @Thickness 3.20 mm |
257 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® HFD4471 PC (Europe-Africa-Middle East) Lexan* HFD4471 is a 10% glass filled, medium flow, impact modified, injection moldable grade designed for high flow and superior surface appearance. HFD4417 has enhanced mold release, impact ductili.. |
|||