Polymer Property : Flexural Yield Strength = 23100 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	159 MPa	23100 psi	ASTM D790
PolyOne Lubri-Tech™ PS-30GF/ 02S PBT Polyester - 30% Glass Fiber - 2% Silicone (discontinued **) Data provided by PolyOne.
Flexural Yield Strength	159 MPa	23100 psi	Flexural Strength
MMCC Aluminum/Graphite Fiber GA 7-230 Metal Matrix Composite Discontinuous graphite fiber aluminum product primarily used for electronic thermal management applications. Lightweight, high damping, stiffer than aluminum, matched cte, easily machined and plate..
Flexural Yield Strength	159 MPa	23100 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ValoxÂ® IQNH4550 PBT Valox* iQNH4550 resin is a glass filled, non-brominated/non-chlorinated flame retardant product based on an environmentally sustainable Valox iQ* PBT resin. Post-consumer recycle (PCR) usage is 31% ..
Flexural Yield Strength	159 MPa	23100 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ValoxÂ® IQNH4550 PBT (Asia Pacific) Valox* iQNH4550 resin is a non-brominated/non-chlorinated flame retardant product based on an environmentally sustainable Valox iQ* PBT resin. Post-consumer recycle (PCR) usage is 31% based on EPEAT..
Flexural Yield Strength	159 MPa	23100 psi	ASTM D790
Techmer ES HiFillÂ® POM CO GF25 CC 25% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforced, 25% Filler by WeightFeatures: Copolymer and Chemically CoupledInformation provided by TP Composites, Inc.
Flexural Yield Strength	159 MPa	23100 psi	2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics NORYL PCN2910 PPE+PS (Asia Pacific) 35% Glass/Mica filled. High modulus and tight tolerance molding for the chassis market.
Flexural Yield Strength	159 MPa	23100 psi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Noryl GFN1420V PPE+PS (Asia Pacific) Noryl* GFN1420V resin is a high flow blend of polyphenylene ether (PPE) and polystyrene (PS) resin that contains 20 % glass reinforcement. The resin is suitable for injection molding and is designe..
Flexural Yield Strength	159 MPa	23100 psi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Noryl GFN1420V PPE+PS (Europe-Africa-Middle East) Noryl* GFN1420V resin is a high flow blend of polyphenylene ether (PPE) and polystyrene (PS) resin that contains 20 % glass reinforcement. The resin is suitable for injection molding and is designe..
Flexural Yield Strength	159 MPa	23100 psi	ASTM D790
A. Schulman ComAlloy E-16831B Polycarbonate, Electrically Conductive - Carbon Fiber Filled Data provided by the manufacturer, ComAlloy International Company.The ComAlloy product line has been integrated into the A Schulman product line.
Flexural Yield Strength	159 MPa	23100 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® HFD4412 PC Lexan* HFD4412 is a 20% glass filled, injection moldable grade designed for high flow and superior surface appearance. Internal mold release.
Flexural Yield Strength	159 MPa	23100 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® HFD4412 PC (Europe-Africa-Middle East) Lexan* HFD4412 is a 20% glass filled, injection moldable grade designed for high flow and superior surface appearance. Internal mold release.
Flexural Yield Strength	159 MPa	23100 psi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Noryl GFN1420V PPE+PS Noryl* GFN1420V resin is a high flow blend of polyphenylene ether (PPE) and polystyrene (PS) resin that contains 20 % glass reinforcement. The resin is suitable for injection molding and is designe..
Flexural Yield Strength	159 MPa	23100 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® HFD4412 PC (Asia Pacific) Lexan* HFD4412 is a 20% glass filled, injection moldable grade designed for high flow and superior surface appearance. Internal mold release.