SABIC Innovative Plastics Lexan® FXD1413T PC Copolymer (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® FXD1413T PC Copolymer (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Clear PC-siloxane copolymer with excellent processability, in special light diffusion colors. Medium flow. Improved toughness compared to medium flow standard PC in same color. Color package may affect performance.
Physical Properties Metric English Comments
Specific Gravity 1.19 g/cc
1.19 g/cc
ASTM D792
Density 1.19 g/cc
0.0430 lb/in³
ISO 1183
Moisture Absorption 0.0900 %
0.0900 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.13 %
0.13 %
ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0080 cm/cm
0.0040 - 0.0080 in/in
on Tensile Bar; SABIC Method
0.0040 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0040 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 10 g/10 min

@Load 1.20 kg,
Temperature 300 °C
10 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Melt Index of Compound 9.0 g/10 min

@Load 5.00 kg,
Temperature 220 °C
9.0 g/10 min

@Load 11.0 lb,
Temperature 428 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 58.0 MPa
8410 psi
50 mm/min; ISO 527
66.0 MPa
9570 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 57.0 MPa
8270 psi
50 mm/min; ISO 527
60.0 MPa
8700 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 116 %
116 %
50 mm/min; ISO 527
130 %
130 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 5.6 %
5.6 %
50 mm/min; ISO 527
6.0 %
6.0 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.27 GPa
329 ksi
50 mm/min; ASTM D638
2.31 GPa
335 ksi
1 mm/min; ISO 527
Flexural Yield Strength 87.0 MPa
12600 psi
1.3 mm/min, 50 mm span; ASTM D790
91.0 MPa
13200 psi
2 mm/min; ISO 178
Flexural Modulus 2.19 GPa
318 ksi
2 mm/min; ISO 178
2.27 GPa
329 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 8.90 J/cm
16.7 ft-lb/in
ASTM D256
7.95 J/cm

@Temperature -30.0 °C
14.9 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 65.0 kJ/m²
30.9 ft-lb/in²
80*10*3; ISO 180/1A
55.0 kJ/m²

@Temperature -30.0 °C
26.2 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
80*10*3; ISO 180/1U
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
80*10*3; ISO 180/1U
Charpy Impact Unnotched NB
NB
Edgew 80*10*3 sp=62mm; ISO 179/1eU
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 7.00 J/cm²
33.3 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eA
6.00 J/cm²

@Temperature -30.0 °C
28.6 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 82.0 J

@Temperature 23.0 °C
60.5 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 71.5 µm/m-°C

@Temperature 23.0 - 80.0 °C
39.7 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
71.5 µm/m-°C

@Temperature -40.0 - 95.0 °C
39.7 µin/in-°F

@Temperature -40.0 - 203 °F
ASTM E 831
CTE, linear, Transverse to Flow 79.3 µm/m-°C

@Temperature 23.0 - 80.0 °C
44.1 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
79.3 µm/m-°C

@Temperature -40.0 - 95.0 °C
44.1 µin/in-°F

@Temperature -40.0 - 203 °F
ASTM E 831
Deflection Temperature at 1.8 MPa (264 psi) 119 °C
246 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
124 °C

@Thickness 3.20 mm
255 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 141 °C
286 °F
Rate A/50; ASTM D1525
141 °C
286 °F
Rate B/50; ISO 306
143 °C
289 °F
Rate B/120; ISO 306
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C PASS
IEC 60695-10-2