SABIC Innovative Plastics LNP STAT-KON 9X02785 PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON 9X02785 PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP STAT-KON* 9X02785 is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 |
| Density | 1.26 g/cc | 0.0455 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0900 % | 0.0900 % | 50% RH, 24 hrs; ASTM D570 |
| 0.140 % | 0.140 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm @Time 86400 sec |
0.0040 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0080 cm/cm @Time 86400 sec |
0.0050 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 52.0 MPa | 7540 psi | Type I, 5 mm/min; ASTM D638 |
| 52.0 MPa | 7540 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 56.0 MPa | 8120 psi | 5 mm/min; ISO 527 |
| 63.0 MPa | 9140 psi | Type I, 5 mm/min; ASTM D638 | |
| 64.0 MPa | 9280 psi | ASTM D638 | |
| Elongation at Break | 3.1 % | 3.1 % | 5 mm/min; ISO 527 |
| 4.0 % | 4.0 % | ASTM D638 | |
| 7.8 % | 7.8 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 2.9 % | 2.9 % | 5 mm/min; ISO 527 |
| 4.3 % | 4.3 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 2.76 GPa | 400 ksi | 1 mm/min; ISO 527 |
| 2.84 GPa | 412 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 75.0 MPa | 10900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 96.0 MPa | 13900 psi | ISO 178 | |
| 103 MPa | 14900 psi | ASTM D790 | |
| Flexural Yield Strength | 107 MPa | 15500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.79 GPa | 405 ksi | 2 mm/min; ISO 178 |
| 2.89 GPa | 419 ksi | ASTM D790 | |
| 2.92 GPa | 424 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.590 J/cm | 1.11 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 21.6 J/cm | 40.5 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 149 kJ/m² | 70.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 35.0 J @Temperature 23.0 °C |
25.8 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 35.0 J | 25.8 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 68.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
37.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 68.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
37.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 114 °C | 237 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 117 °C @Thickness 3.20 mm |
243 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 103 °C | 217 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 106 °C @Thickness 3.20 mm |
223 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 100 - 1.00e+7 ohm-cm | 100 - 1.00e+7 ohm-cm | ASTM D257 |
| Surface Resistance | 100 ohm - 1e+05 | 100 ohm - 1e+05 | ASTM D257 |