- Polymer Property : Flexural Strength = 13900 psi
Polymer Property : Flexural Strength = 13900 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Strength | 95.8 MPa | 13900 psi | ASTM D790 |
| Polymer Resources PC-FD2-[color]-1 Polycarbonate, FDA-compliant Feedstocks, Medium Flow with Mold Release, Gamma Resistant Polycarbonate, FDA-compliant Feedstocks, Medium Flow with Mold Release, Gamma ResistantProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-p.. |
|||
| Flexural Strength | 95.8 MPa | 13900 psi | ASTM D790 |
| Polymer Resources PC-GP2-D-[color]-1 Polycarbonate, General Purpose, Medium Flow with Mold Release Polycarbonate, General Purpose, Medium Flow with Mold ReleaseProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Inf.. |
|||
| Flexural Strength | 95.8 MPa | 13900 psi | ASTM D790 |
| Polymer Resources PC-GP3-D Polycarbonate, General Purpose, High Flow Polycarbonate, General Purpose, High FlowFeatures: • High Impact Resistance • Self ExtinguishingProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inc.. |
|||
| Flexural Strength | 96.0 MPa @Temperature 22.0 °C |
13900 psi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
| Menzolit Menzolit® BMC 2300 Unsaturated Polyester UP BMC 2300 is a special BMC with exceptional high fire retardancy. The glass content is set to a level that provides sufficient mouldability with high strength and stiffness properties. Fire retardanc.. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D 790 |
| MRC Polymers NAXELL™ PC110VL Polycarbonate, Very Low MFR • Available in natural and custom colors• Can be UV Stabilized• Internal and external lubricants can be addedInformation provided by MRC Polymers Inc. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D 790 |
| SABIC Innovative Plastics LNP Lubricomp DX99854 PC (Asia Pacific) LNP* LUBRICOMP* DX99854 is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Internally Lubricated.This data was supplied by SABIC-I.. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D 790 |
| SABIC Innovative Plastics LNP Stat-kon DS0029 PC (Asia Pacific) LNP STAT-KON* DS0029 is a compound based on Polycarbonate resin containing Stainless Steel. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for t.. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP STAT-KON DX03571 PC LNP* STAT-KON* DX03571 is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP STAT-KON DX03571 PC LNP* STAT-KON* DX03571 is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP STAT-KON DX04462C PC LNP STAT-KON* DX04462C is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Clean Compounding System, Electrically Conductive. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP CX05470 PS (Asia Pacific) LNP* Thermocomp* CX05470 is a compound based on Polystyrene resin containing Glass Fiber. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | 2mm/min; ISO 178 |
| Teijin Multilon TN-7000F Filler Reinforced Type, Halogen-Free Flame Resistant PC/ABS Polymer Alloy Halogen-free flame retardant PC/ABS polymer alloy, and is also antimony-free. High stiffness realizes the thin wall of business machine chassis.Information provided by Teijin Chemicals Ltd. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | 2mm/min; ISO 178 |
| Teijin Multilon TN-7500F Filler Reinforced Type, Halogen-Free Flame Resistant PC/ABS Polymer Alloy Halogen-free flame retardant PC/ABS polymer alloy, and is also antimony-free. High stiffness and flowability realize the thin wall of large-scale business machine chassis.Information provided by Tei.. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | 3-point; ISO 178 |
| Styron CALIBREâ„¢ 301V-6 Polycarbonate Resin Overview: CALIBREâ„¢ 301V-6 Polycarbonate resins offer exceptional impact resistance and heat distortion resistance, and meets UL94 V-2 rating. CALIBRE 301V-6 contains a mold release agent and is.. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | ISO 178 |
| SABIC Innovative Plastics LNP STAT-KON 9X02785 PC LNP STAT-KON* 9X02785 is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP STAT-KON DX04462C PC (Asia Pacific) LNP* STAT-KON* DX04462C is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material include: Clean Compounding System. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D 790 |
| SABIC Innovative Plastics LNP Thermocomp 9X04488 POLYPHENYLENESULFONE LNP* Thermocomp* 9X04488 is a compound based on POLYPHENYLENESULFONE resin containing Mineral.This data was supplied by SABIC-IP for the Americas region. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D 790 |
| SABIC Innovative Plastics LNP Thermocomp PZ006 PA 6 LNP* Thermocomp* PZ006 is a compound based on Nylon 6 resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP RZ0069 PA 66 LNP* THERMOCOMP* RZ0069 is a compound based on Nylon 66 resin containing 30% Milled Glass. Added features of this material include: Flame Retardant. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
| Plenco 2535 Phenolic, Granular, Compression Molded PLENCO 02535 is a general purpose, organic filled phenolic molding compound offering optimized cure characteristics and excellent electrical properties. Type ASTM 5948 CFG, and UL recognized under c.. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | 2 mm/min; ISO 178 |
| Covestro Makrolon® 2400 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• General purpose• Low.. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | 2 mm/min; ISO 178 |
| Covestro Makrolon® 3100 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• General purpose• Hig.. |
|||
| Flexural Strength | 95.8 MPa | 13900 psi | ASTM D790 |
| Entec Hylex® P1317L1 HB Polycarbonate UV Stabilized, Higher Flow, Mold Release, Water ClearInformation provided by Entec. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
| A. Schulman ComAlloy Hiloy® 419 Polyester - PBT, Mineral Reinforced Data provided by the manufacturer, ComAlloy International Company.40% Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
| Vyncolit INSUL-PLATE™ X-28057-2HT Hole-Fill Powder For Printed Circuit Boards Vyncolit INSUL-PLATE™ Hole-Fill material delivers true reliability and superior performance. This material, in powder form, is specifically suited for Hole-Fill use in glass epoxy, multi-layer and .. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP PH0460A PA 6 (Asia Pacific) LNP* Thermocomp* PH0460A is a compound based on Nylon 6 resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP SF008 PA 12 (Asia Pacific) LNP* Thermocomp* SF008 is a compound based on Nylon 12 resin containing Glass Fiber. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | GB9341 |
| Beijing Evergrow Resources MC Nylon Information provided by Beijing Evergrow Resources. |
|||
| Flexural Strength | 95.8 MPa @Temperature 150 °C |
13900 psi @Temperature 302 °F |
ISO 178 |
| Solvay Specialty Polymers Amodel® AS-1566 HS Polyphthalamide (PPA)
(Unverified Data**) Amodel AS-1566 HS resin is a 65% glass and mineral reinforced polyphthalamide (PPA) resin that exhibits a high deflection temperature and high flexural modulus. This grade was designed specifically .. |
|||
| Flexural Strength | 95.8 MPa | 13900 psi | ASTM D790 |
| Techmer ES HiFill FR® PBT 0166 B FR Availability: North AmericaForms: PelletsFeatures: Flame RetardantInformation provided by TP Composites, Inc. |
|||