SABIC Innovative Plastics LNP LUBRICOMP DL0049EF PC (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP DL0049EF PC (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* DL0049EF is a compound based on Polycarbonate resin containing PTFE, Flame Retardant. Added features of this material include: Internally Lubricated.
Physical Properties Metric English Comments
Density 1.35 g/cc
0.0488 lb/in³
ASTM D792
1.35 g/cc
0.0488 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Time 86400 sec
0.0050 - 0.0070 in/in

@Time 24.0 hour
ASTM D955
0.0061 cm/cm

@Time 86400 sec
0.0061 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.0085 cm/cm

@Time 86400 sec
0.0085 in/in

@Time 24.0 hour
ISO 294
0.0080 - 0.010 cm/cm

@Time 86400 sec
0.0080 - 0.010 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 40.0 MPa
5800 psi
ASTM D638
43.0 MPa
6240 psi
ISO 527
Tensile Strength, Yield 47.0 MPa
6820 psi
ASTM D638
49.0 MPa
7110 psi
ISO 527
Elongation at Break 23.2 %
23.2 %
ASTM D638
26.1 %
26.1 %
ISO 527
Elongation at Yield 5.2 %
5.2 %
ASTM D638
5.4 %
5.4 %
ISO 527
Tensile Modulus 2.06 GPa
299 ksi
50 mm/min; ASTM D638
2.09 GPa
303 ksi
1 mm/min; ISO 527
Flexural Strength 70.0 MPa
10200 psi
ISO 178
Flexural Modulus 2.06 GPa
299 ksi
ASTM D790
2.20 GPa
319 ksi
ISO 178
Izod Impact, Notched 1.22 J/cm
2.29 ft-lb/in
ASTM D256
Izod Impact, Unnotched 15.69 J/cm
29.39 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 118 kJ/m²
56.1 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 32.0 J
23.6 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 26.0 J
19.2 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.32
0.32
ASTM D3702 Modified
Coefficient of Friction, Static 0.19
0.19
ASTM D3702 Modified
K (wear) Factor 16.1 x 10-8 mm³/N-M
8.00 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 75.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
42.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
76.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
42.2 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 78.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
43.3 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
79.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
44.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 136 °C
277 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
137 °C

@Thickness 3.20 mm
279 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 126 °C
259 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
123 °C

@Thickness 3.20 mm
253 °F

@Thickness 0.126 in
unannealed; ASTM D648