Polymer Property : Linear Mold Shrinkage, Transverse = 0.010 cm/cm Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Linear Mold Shrinkage, Transverse	0.0080 - 0.010 cm/cm @Time 86400 sec	0.0080 - 0.010 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP AL003 ABS LNP LUBRICOMP* AL003 is a compound based on Acrylonitrile Butadiene Styrene resin containing 15% PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Transverse	0.0080 - 0.010 cm/cm @Time 86400 sec	0.0080 - 0.010 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP AL003 ABS LNP LUBRICOMP* AL003 is a compound based on Acrylonitrile Butadiene Styrene resin containing 15% PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Transverse	0.0080 - 0.010 cm/cm @Time 86400 sec	0.0080 - 0.010 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP AL003 ABS (Europe-Africa-Middle East) LNP LUBRICOMP* AL003 is a compound based on Acrylonitrile Butadiene Styrene resin containing PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Transverse	0.0080 - 0.010 cm/cm @Time 86400 sec	0.0080 - 0.010 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP AL003 ABS (Europe-Africa-Middle East) LNP LUBRICOMP* AL003 is a compound based on Acrylonitrile Butadiene Styrene resin containing PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Transverse	0.0080 - 0.010 cm/cm @Time 86400 sec	0.0080 - 0.010 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP AL003 ABS (Asia Pacific) LNP LUBRICOMP* AL003 is a compound based on Acrylonitrile Butadiene Styrene resin containing PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Transverse	0.0080 - 0.010 cm/cm @Time 86400 sec	0.0080 - 0.010 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP AL003 ABS (Asia Pacific) LNP LUBRICOMP* AL003 is a compound based on Acrylonitrile Butadiene Styrene resin containing PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Transverse	0.008 - 0.010 cm/cm @Thickness 2.00 mm	0.008 - 0.010 in/in @Thickness 0.0787 in	ASTM D955
LG Chemical LUMILOY GN1306F Injection Molding FR Heat Resistant mPPO Uses include electric/electronic parts.
Linear Mold Shrinkage, Transverse	0.0080 - 0.010 cm/cm @Time 86400 sec	0.0080 - 0.010 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP DL0049EF PC LNP* Lubricomp* DL0049EF is a compound based on Polycarbonate resin containing 20% PTFE, Flame Retardant. Added features of this material include: Internally Lubricated, Flame Retardant
Linear Mold Shrinkage, Transverse	0.0080 - 0.010 cm/cm @Time 86400 sec	0.0080 - 0.010 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP HFG25Z PA 11 LNP* Lubricomp* HFG25Z is a compound based on Nylon 11 resin containing 25% Glass Fiber, 10% Graphite. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Transverse	0.0050 - 0.010 cm/cm @Time 86400 sec	0.0050 - 0.010 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP WFL36 PBT LNP LUBRICOMP* WFL36 is a compound based on PBT resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant.
Linear Mold Shrinkage, Transverse	0.0050 - 0.010 cm/cm @Time 86400 sec	0.0050 - 0.010 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP WFL36 PBT LNP LUBRICOMP* WFL36 is a compound based on PBT resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant.
Linear Mold Shrinkage, Transverse	0.0050 - 0.010 cm/cm @Time 86400 sec	0.0050 - 0.010 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP WFL36 PBT (Asia Pacific) LNP LUBRICOMP* WFL36 is a compound based on Polybutylene Terephalate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Transverse	0.0050 - 0.010 cm/cm @Time 86400 sec	0.0050 - 0.010 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP WFL36 PBT (Asia Pacific) LNP LUBRICOMP* WFL36 is a compound based on Polybutylene Terephalate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Transverse	0.0050 - 0.010 cm/cm @Time 86400 sec	0.0050 - 0.010 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP WFP36 PBT LNP LUBRICOMP* WFP36 is a compound based on PBT resin containing 30% Glass Fiber, 15% PTFE/Silicone. Added features of this material include: Wear Resistant.
Linear Mold Shrinkage, Transverse	0.0050 - 0.010 cm/cm @Time 86400 sec	0.0050 - 0.010 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP WFP36 PBT LNP LUBRICOMP* WFP36 is a compound based on PBT resin containing 30% Glass Fiber, 15% PTFE/Silicone. Added features of this material include: Wear Resistant.
Linear Mold Shrinkage, Transverse	0.0050 - 0.010 cm/cm @Time 86400 sec	0.0050 - 0.010 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP WFP36 PBT (Asia Pacific) LNP LUBRICOMP* WFP36 is a compound based on Polybutylene Terephalate resin containing Silicone, Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Transverse	0.0050 - 0.010 cm/cm @Time 86400 sec	0.0050 - 0.010 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP WFP36 PBT (Asia Pacific) LNP LUBRICOMP* WFP36 is a compound based on Polybutylene Terephalate resin containing Silicone, Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Transverse	0.0080 - 0.010 cm/cm @Time 86400 sec	0.0080 - 0.010 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRILOY D2000AXH PC LNP LUBRILOY* D2000AXH is a compound based on Polycarbonate resin containing Proprietary Lubricant. Added features of this material include: Wear Resistant, Healthcare.
Linear Mold Shrinkage, Transverse	0.0080 - 0.010 cm/cm @Time 86400 sec	0.0080 - 0.010 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRILOY D2000AXH PC LNP LUBRILOY* D2000AXH is a compound based on Polycarbonate resin containing Proprietary Lubricant. Added features of this material include: Wear Resistant, Healthcare.
Linear Mold Shrinkage, Transverse	0.0080 - 0.010 cm/cm @Thickness 3.20 mm	0.0080 - 0.010 in/in @Thickness 0.126 in	SABIC Method
SABIC Innovative Plastics ValoxÂ® 745 PBT 30% mineral reinforced polyester improved toughness and low warpage. Typical applications are telephone ringer frames and card racks.
Linear Mold Shrinkage, Transverse	0.0080 - 0.010 cm/cm @Time 86400 sec	0.0080 - 0.010 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP STAT-LOY A30009 ABS LNP* STAT-LOY* A30009 is a compound based on ABS. Added features of this material include: Antistatic, Flame Retardant.
Linear Mold Shrinkage, Transverse	0.0080 - 0.010 cm/cm @Time 86400 sec	0.0080 - 0.010 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP STAT-LOY A30009 ABS (Asia Pacific) LNP* Stat-loy* A30009 is a compound based on Acrylonitrile Butadiene Styrene resin containing Flame Retardant. Added features of this material include: Antistat, Flame Retardant.
Linear Mold Shrinkage, Transverse	0.0080 - 0.010 cm/cm @Time 86400 sec	0.0080 - 0.010 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Stat-loy A3000Z ABS LNP* Stat-loy* A3000Z is a compound based on Acrylonitrile Butadiene Styrene resin containing Anti-Static. Added features of this material include: Antistat.This data was supplied by SABIC-IP for t..
Linear Mold Shrinkage, Transverse	0.0080 - 0.010 cm/cm @Time 86400 sec	0.0080 - 0.010 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Stat-loy A3000Z ABS (Asia Pacific) LNP* Stat-loy* A3000Z is a compound based on Acrylonitrile Butadiene Styrene resin containing Anti-Static. Added features of this material include: Antistat.This data was supplied by SABIC-IP for t..
Linear Mold Shrinkage, Transverse	0.0080 - 0.010 cm/cm @Time 86400 sec	0.0080 - 0.010 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP HF008 PA 11 (Asia Pacific) LNP* THERMOCOMP* HF008 is a compound based on Nylon 11 resin containing Glass Fiber.
Linear Mold Shrinkage, Transverse	0.0080 - 0.010 cm/cm @Time 86400 sec	0.0080 - 0.010 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP HF008 PA 11 (Asia Pacific) LNP* THERMOCOMP* HF008 is a compound based on Nylon 11 resin containing Glass Fiber.
Linear Mold Shrinkage, Transverse	0.0080 - 0.010 cm/cm @Thickness 3.20 mm	0.0080 - 0.010 in/in @Thickness 0.126 in	SABIC Method
SABIC Innovative Plastics ValoxÂ® 745 PBT (Asia Pacific) 30% mineral reinforced polyester improved toughness and low warpage. Typical applications are telephone ringer frames and card racks.
Linear Mold Shrinkage, Transverse	0.0080 - 0.010 cm/cm @Time 86400 sec	0.0080 - 0.010 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP HF008 PA11 LNP THERMOCOMP* HF008 is a compound based on Nylon 11 resin containing 40% Glass Fiber.
Linear Mold Shrinkage, Transverse	0.0080 - 0.010 cm/cm @Time 86400 sec	0.0080 - 0.010 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP HF008 PA11 LNP THERMOCOMP* HF008 is a compound based on Nylon 11 resin containing 40% Glass Fiber.
Linear Mold Shrinkage, Transverse	0.0090 - 0.010 cm/cm @Time 86400 sec	0.0090 - 0.010 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP MF004AS PP LNP THERMOCOMP* MF004AS is a compound based on Polypropylene resin containing 20% Glass Fiber. Added features of this material include: Heat Stabilized.