Polymer Property : CTE, linear, Parallel to Flow = 42.0 µin/in-°F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 75.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
 42.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
SABIC Innovative Plastics LNP LUBRICOMP DL002ER PC
LNP* Lubricomp* DL002ER is a compound based on Polycarbonate resin containing 10% PTFE. Added features of this material include: Internally Lubricated, Easy Molding, Mold Release.
CTE, linear, Parallel to Flow 75.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
 42.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
SABIC Innovative Plastics LNP LUBRICOMP DL0049EF PC
LNP* Lubricomp* DL0049EF is a compound based on Polycarbonate resin containing 20% PTFE, Flame Retardant. Added features of this material include: Internally Lubricated, Flame Retardant
CTE, linear, Parallel to Flow 75.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
 42.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
SABIC Innovative Plastics LNP LUBRICOMP DL0049EF PC (Asia Pacific)
LNP* Lubricomp* DL0049EF is a compound based on Polycarbonate resin containing PTFE, Flame Retardant. Added features of this material include: Internally Lubricated.
CTE, linear, Parallel to Flow 75.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
 42.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
SABIC Innovative Plastics LNP LUBRICOMP DX98306H PC
LNP* LUBRICOMP* DX98306H is a compound based on Polycarbonate resin containing Proprietary Fillers. Added features of this material include: Wear Resistant, Low Extractible.
CTE, linear, Parallel to Flow 75.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
 42.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
SABIC Innovative Plastics LNP LUBRICOMP DX98306H PC (Asia Pacific)
LNP* Lubricomp* DX98306H is a compound based on Polycarbonate resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated, Low Extractible.
CTE, linear, Parallel to Flow 75.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
 42.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
SABIC Innovative Plastics Valox® 745 PBT
30% mineral reinforced polyester improved toughness and low warpage. Typical applications are telephone ringer frames and card racks.
CTE, linear, Parallel to Flow 75.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
 42.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
SABIC Innovative Plastics LNP THERMOCOMP RF0029S PA 66
LNP* THERMOCOMP* RF0029S is a compound based on Nylon 66 resin containing 10% Glass Fiber. Added features of this material include: Flame Retardant, Heat Stabilized.
CTE, linear, Parallel to Flow 75.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
 42.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
SABIC Innovative Plastics LNP THERMOCOMP RF0029S PA 66 (Asia Pacific)
LNP* Thermocomp* RF0029S is a compound based on Nylon 66 resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant, Heat Stabilized.
CTE, linear, Parallel to Flow 75.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
 42.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
SABIC Innovative Plastics Valox® 745 PBT (Asia Pacific)
30% mineral reinforced polyester improved toughness and low warpage. Typical applications are telephone ringer frames and card racks.
CTE, linear, Parallel to Flow 75.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
 42.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
SABIC Innovative Plastics LNP LUBRICOMP DL002ER PC (Asia Pacific)
LNP* Lubricomp* DL002ER is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Internally Lubricated, Easy Molding, Mold Release.