SABIC F01552 High Density Polyethylene for Blown Film

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer SABIC
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC F01552 High Density Polyethylene for Blown Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: F01552 is a high molecular weight high density polyethylene copolymer grade specifically designed for blown film applications. Its high molecular weight, broad molecular weight distribution and high density combine successfully to give excellent extrudability with high film strength and drawdown capability.Typical Applications: F01552 resin is recommended for the production of strong strength millinery and notion bags, deep freezer bags, table cloths and thin film as quality replacement for paper products.Information provided by SABIC.
Physical Properties Metric English Comments
Density 0.952 g/cc
0.0344 lb/in³
ASTM D1505
Thickness 15.0 microns
0.591 mil
Melt Flow 0.15 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.15 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
16 g/10 min

@Load 21.6 kg,
Temperature 190 °C
16 g/10 min

@Load 47.6 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 31.0 MPa
4500 psi
ASTM D882
Film Tensile Strength at Yield, TD 30.0 MPa
4350 psi
ASTM D882
Film Elongation at Break, MD 400 %
400 %
ASTM D882
Film Elongation at Break, TD 610 %
610 %
ASTM D882
Elmendorf Tear Strength MD 4.0 g
4.0 g
ASTM D1922
Elmendorf Tear Strength TD 40 g
40 g
ASTM D1922
Elmendorf Tear Strength, MD 0.270 g/micron
6.86 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 2.67 g/micron
67.8 g/mil
ASTM D1922
Dart Drop 12.0 g/micron
305 g/mil
ASTM D1709
Dart Drop Test 180 g
0.397 lb
ASTM D1709
Film Tensile Strength at Break, MD 55.0 MPa
7980 psi
ASTM D882
Film Tensile Strength at Break, TD 49.0 MPa
7110 psi
ASTM D882
1% Secant Modulus, MD 1400 MPa
203000 psi
ASTM D882
1% Secant Modulus, TD 1700 MPa
247000 psi
ASTM D882
Thermal Properties Metric English Comments
Vicat Softening Point 125 °C
257 °F
ASTM D1525
Processing Properties Metric English Comments
Melt Temperature 200 - 235 °C
392 - 455 °F
Blow-up Ratio (BUR) 3.0 - 5.0
3.0 - 5.0