DuPont Performance Polymers Zytel® 444AHS BK152 Nylon 66 (Unverified Data**)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Zytel® 444AHS BK152 Nylon 66
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Zytel® 444AHS is a toughened, heat stabilized, black polyamide 66 resin for injection molding. It is a high flow, processing friendly material.Information provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in³ | DAM; ISO 1183 |
| Water Absorption | 1.3 % @Temperature 23.0 °C |
1.3 % @Temperature 73.4 °F |
Immersion 24h; DAM; ISO 62, Similar to |
| 1.3 % @Thickness 1.00 mm, Temperature 23.0 °C |
1.3 % @Thickness 0.0394 in, Temperature 73.4 °F |
Saturation, immersed; DAM; ISO 62, Similar to | |
| Linear Mold Shrinkage | 0.016 cm/cm @Thickness 3.20 mm |
0.016 in/in @Thickness 0.126 in |
Normal; DAM; ASTM D955 |
| 0.018 cm/cm @Thickness 3.20 mm |
0.018 in/in @Thickness 0.126 in |
Parallel; DAM; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 40.0 MPa @Temperature 23.0 °C |
5800 psi @Temperature 73.4 °F |
50%RH; ISO 527 |
| 62.0 MPa @Temperature 23.0 °C |
8990 psi @Temperature 73.4 °F |
DAM; ISO 527 | |
| Elongation at Break | 25 % @Temperature 23.0 °C |
25 % @Temperature 73.4 °F |
DAM; nominal; ISO 527 |
| 40 % @Temperature 23.0 °C |
40 % @Temperature 73.4 °F |
DAM; ISO 527 | |
| >= 50 % @Temperature 23.0 °C |
>= 50 % @Temperature 73.4 °F |
50%RH; nominal; ISO 527 | |
| Elongation at Yield | 5.5 % @Temperature 23.0 °C |
5.5 % @Temperature 73.4 °F |
DAM; ISO 527 |
| 15 % @Temperature 23.0 °C |
15 % @Temperature 73.4 °F |
50%RH; ISO 527 | |
| Tensile Modulus | 1.10 GPa @Temperature 23.0 °C |
160 ksi @Temperature 73.4 °F |
50%RH; ISO 527 |
| 2.40 GPa @Temperature 23.0 °C |
348 ksi @Temperature 73.4 °F |
DAM; ISO 527 | |
| Flexural Modulus | 2.27 GPa @Temperature 23.0 °C |
329 ksi @Temperature 73.4 °F |
DAM; ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature -40.0 °C |
4.76 ft-lb/in² @Temperature -40.0 °F |
DAM; ISO 180/1A |
| 16.0 kJ/m² @Temperature 23.0 °C |
7.61 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature -30.0 - 30.0 °C |
278 µin/in-°F @Temperature -22.0 - 86.0 °F |
DAM; ASTM E 831 |
| 500 µm/m-°C @Temperature -40.0 - 23.0 °C |
278 µin/in-°F @Temperature -40.0 - 73.4 °F |
DAM; ASTM E 831 | |
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C |
278 µin/in-°F @Temperature 73.4 - 131 °F |
DAM; ASTM E 831 | |
| 500 µm/m-°C @Temperature 55.0 - 160 °C |
278 µin/in-°F @Temperature 131 - 320 °F |
DAM; ASTM E 831 | |
| 500 µm/m-°C @Temperature -30.0 - 30.0 °C |
278 µin/in-°F @Temperature -22.0 - 86.0 °F |
DAM; ISO 11359-1/-2 | |
| 500 µm/m-°C @Temperature -40.0 - 23.0 °C |
278 µin/in-°F @Temperature -40.0 - 73.4 °F |
DAM; ISO 11359-1/-2 | |
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C |
278 µin/in-°F @Temperature 73.4 - 131 °F |
DAM; ISO 11359-1/-2 | |
| 500 µm/m-°C @Temperature 55.0 - 160 °C |
278 µin/in-°F @Temperature 131 - 320 °F |
DAM; ISO 11359-1/-2 | |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
50.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
DAM; ASTM E 831 |
| 90.0 µm/m-°C @Temperature -40.0 - 23.0 °C |
50.0 µin/in-°F @Temperature -40.0 - 73.4 °F |
DAM; ASTM E 831 | |
| 90.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
50.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
DAM; ISO 11359-1/-2 | |
| 90.0 µm/m-°C @Temperature -40.0 - 23.0 °C |
50.0 µin/in-°F @Temperature -40.0 - 73.4 °F |
DAM; ISO 11359-1/-2 | |
| 100 µm/m-°C @Temperature 23.0 - 55.0 °C |
55.6 µin/in-°F @Temperature 73.4 - 131 °F |
DAM; ASTM E 831 | |
| 100 µm/m-°C @Temperature 23.0 - 55.0 °C |
55.6 µin/in-°F @Temperature 73.4 - 131 °F |
DAM; ISO 11359-1/-2 | |
| 130 µm/m-°C @Temperature 55.0 - 160 °C |
72.2 µin/in-°F @Temperature 131 - 320 °F |
DAM; ASTM E 831 | |
| 130 µm/m-°C @Temperature 55.0 - 160 °C |
72.2 µin/in-°F @Temperature 131 - 320 °F |
DAM; ISO 11359-1/-2 | |
| Melting Point | 260 °C | 500 °F | 10°C/min; DAM; ISO 11357-1/-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | DAM; ISO 75-1/-2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 290 °C | 554 °F | DAM; Optimum |
| 280 - 300 °C | 536 - 572 °F | DAM | |
| Mold Temperature | 70.0 °C | 158 °F | DAM; optimum |
| 50.0 - 90.0 °C | 122 - 194 °F | DAM | |
| Drying Temperature | 80.0 °C | 176 °F | DAM |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM |
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Forms | Pellets | DAM |
| Generic | PA66 | DAM |
| Material Status | Preliminary Data | DAM |
| Processing Method | Injection Molding | DAM |
| Product Category | Toughened Resins | DAM |
| Unreinforced Resins | DAM | |
| RoHS Compliance | Contact Manufacturer | DAM |