Rogers Corporation RO3730 Antenna Grade Laminate

Category Polymer , Thermoplastic , Fluoropolymer , PTFE , Polytetrafluoroethylene (PTFE), Glass Filled, Molded
Manufacturer Rogers Corporation
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Rogers Corporation RO3730 Antenna Grade Laminate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
RO3730™ Laminates have the excellent thermo-mechanical properties and electrical characteristics that antenna designers need. The laminates have a dielectric constant of 3.0 and a loss tangent of 0.0013 measured at 2.5 GHz. These values allow antenna designers to realize substantial gain values while minimizing signal loss. Materials are available with a demonstrated low PIM performance, with values better than -154 dBc (measured using Rogers' internal test method).Cladding is 1 ounce rolled annealed copper (35 microns thick).Features and Benefits:RO3730 reinforced woven fiber glass with optimized glass and filler loading - Improved mechanical rigidity, easier handling and processing versus non-reinforced PTFE products and lower dissipation factorLow PIM - reduced signal interferenceLoss - improved antenna gainEconomically priced - volume manufacturingEnvironmentally friendly - Lead-free process compatible and RoHS compliantTypical Applications:Base station antennasRFID antennasWLAN antennasSatellite Radio antennasInformation provided by Rogers Corporation.
Physical Properties Metric English Comments
Specific Gravity 2.10 g/cc
2.10 g/cc
ASTM D792
Moisture Absorption at Equilibrium 0.040 %
0.040 %
D48/50; ASTM D570
Thickness 762 - 1520 microns
30.0 - 60.0 mil
Range of Thicknesses Available
Mechanical Properties Metric English Comments
Flexural Strength 8.00 MPa
1160 psi
Y-Direction; IPC-TM-650, 2.4.4
9.00 MPa
1310 psi
X-Direction; IPC-TM-650, 2.4.4
Peel Strength 1.84 kN/m

@Temperature 288 °C,
Time 10.0 sec
10.5 pli

@Temperature 550 °F,
Time 0.00278 hour
Copper, After Solder Float; IPC-TM-650 2.4.8
Thermal Properties Metric English Comments
CTE, linear 11.0 µm/m-°C
6.11 µin/in-°F
X-Direction; IPC-TM-650 2.4.41
12.0 µm/m-°C
6.67 µin/in-°F
Y-Direction; IPC-TM-650 2.4.41
65.0 µm/m-°C
36.1 µin/in-°F
Z-Direction; IPC-TM-650 2.4.41
Thermal Conductivity 0.450 W/m-K
3.12 BTU-in/hr-ft²-°F
D24/23; IPC-TM-650, 2.6.2.1
Decomposition Temperature 500 °C
932 °F
ASTM D3850
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
Cond. A; IPC 2.5.17.1
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
Cond. A; IPC 2.5.17.1
Dielectric Constant 2.93

@Frequency 8.00e+9 - 4.00e+10 Hz
2.93

@Frequency 8.00e+9 - 4.00e+10 Hz
Z direction, Design; Differential Phase Length Method
2.94 - 3.06

@Frequency 1.00e+10 Hz
2.94 - 3.06

@Frequency 1.00e+10 Hz
Z direction, Process; IPC-TM-650 2.5.5.5
Dissipation Factor 0.0013

@Frequency 2.50e+9 Hz
0.0013

@Frequency 2.50e+9 Hz
IPC-TM-650 2.5.5.5
0.0016

@Frequency 1.00e+10 Hz
0.0016

@Frequency 1.00e+10 Hz
IPC-TM-650 2.5.5.5
Descriptive Properties Value Comments
Dimensional Stability 0.02 mm/m
X direction; IPC-TM-650, 2.4.39A
0.03 mm/m
Y direction; IPC-TM-650, 2.4.39A
PIM < -154 dBc
Thermal Coefficient of Dielectric Constant -22 ppm/°C
-50°C to 150°C