Polymer Property : CTE, linear = 11.0 µm/m-°C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
CTE, linear 11.0 - 17.0 µm/m-°C
6.11 - 9.44 µin/in-°F
Average value: 13.7 µm/m-°C Grade Count:5
Overview of materials for Polyphthalamide (PPA), Carbon Fiber
This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, Carbon Fiber". Each property range of values reported is minimum and maximum values of ..
CTE, linear 11.0 µm/m-°C
6.11 µin/in-°F
ISO 11359-2
Celanese VECTRA E440i LCP, 42% Mineral / Glass Reinforced  (Unverified Data**)
Mineral and glass filled grade with low warp, easy flow and smooth surface apperance.Information provided by Celanese
CTE, linear 11.0 µm/m-°C
6.11 µin/in-°F
ISO 11359-2
Celanese VECTRA E540i LCP, 40% Mineral Reinforced  (Unverified Data**)
Mineral filled grade with low warp, easy flow and smooth surface appearance. 40% mineral, low warp & easy flow with smooth surface appearanceA three-zone screw evenly divided into feed, compression,..
CTE, linear 11.0 - 237 µm/m-°C
6.11 - 132 µin/in-°F
Average value: 74.8 µm/m-°C Grade Count:41
Overview of materials for Polytetrafluoroethylene (PTFE), Glass Filled, Molded
This property data is a summary of similar materials in the MatWeb database for the category "Polytetrafluoroethylene (PTFE), Glass Filled, Molded". Each property range of values reported is minimum..
CTE, linear 11.0 - 17.0 µm/m-°C

@Temperature 20.0 °C
6.11 - 9.44 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Eastman Tenite Butyrate 438E0V16304 Clear, Trsp Cellulose Acetate Butyrate  (discontinued **)
Plasticizer 4%. Weight loss on heating = 0.3% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of pr..
CTE, linear 11.0 - 17.0 µm/m-°C

@Temperature 20.0 °C
6.11 - 9.44 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Eastman Tenite Butyrate 465E2R30012 Natural, Trsp Cellulose Acetate Butyrate  (discontinued **)
Plasticizer 12%. Weight loss on heating = 1.3% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p..
CTE, linear 11.0 µm/m-°C
6.11 µin/in-°F
DIN 53752
Lehmann & Voss LUVOCOM® 1301/XCF/30 N PPS, linear, with carbon fiber
Applications: Automotive industry, textile-and office machinery, medical- and precision engineering.High-strength and stiff parts with low creep.Electrically conductive, suitable for continuous disc..
CTE, linear 11.0 µm/m-°C
6.11 µin/in-°F
Mo-Sci Corporation GB-40-N Green B Filter Glass
Applications: Lead-free NVIS Green B filter glass for white LED sources.Information provided by Mo-Sci Corporation.
CTE, linear 11.0 µm/m-°C

@Temperature 20.0 °C
6.10 µin/in-°F

@Temperature 68.0 °F
SGL Carbon Group Ridurid® EK 60 High Performance Graphite Filled Plastic
Good mechanical strength, good sliding properties, high temperature resistance, high thermal shock resistance, low wettability, high corrosion resistance, high thermal conductivity, high purity, and..
CTE, linear 11.0 µm/m-°C

@Temperature 20.0 - 100 °C
6.11 µin/in-°F

@Temperature 68.0 - 212 °F
Special Metals NIMONIC® Alloy 75
A nickel-chromium alloy with good mechanical properties and oxidation resistance at high temperatures. Used for sheet-metal fabrications in gas-turbine engines, for components of industrial furnace..
CTE, linear 11.0 µm/m-°C

@Temperature 20.0 - 750 °C
6.11 µin/in-°F

@Temperature 68.0 - 1380 °F
BS 1902: section 5.3: 1990
Skamol Group V-LITE 375 Vermiculite Insulating Brick
V-LITE vermiculite insulating bricks have the following characteristics: Max. service temperature 1100°C (2012°F)Hot-face applications and back-up insulationGood insulation valueHigh mechanica..
CTE, linear 11.0 µm/m-°C

@Temperature 20.0 - 750 °C
6.11 µin/in-°F

@Temperature 68.0 - 1380 °F
BS 1902: section 5.3: 1990
Skamol Group V-LITE 475 Vermiculite Insulating Brick
V-LITE vermiculite insulating bricks have the following characteristics: Max. service temperature 1100°C (2012°F)Hot-face applications and back-up insulationGood insulation valueHigh mechanica..
CTE, linear 11.0 µm/m-°C

@Temperature 20.0 °C
6.11 µin/in-°F

@Temperature 68.0 °F
ASTM D 696
Lubrizol Isoplast® 101LGF60NAT Engineering Thermoplastic Polyurethane Resin
Available in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Isoplast product line from Dow in 2009.
CTE, linear 11.0 µm/m-°C

@Temperature 20.0 - 100 °C
6.11 µin/in-°F

@Temperature 68.0 - 212 °F
Goodfellow Aluchrom O® Resistance Alloy
Resistance heating alloy with excellent resistance to oxidation at elevated temperatures. Used in many varied applications - from small household appliances to large industrial furnaces.Information ..
CTE, linear 11.0 - 17.0 µm/m-°C

@Temperature 20.0 °C
6.11 - 9.44 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Eastman Tenite Butyrate 285A2R30016 Natural, Trsp Cellulose Acetate Butyrate
Plasticizer 8%. Weight loss on heating = 0.3% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of pr..
CTE, linear 11.0 - 17.0 µm/m-°C

@Temperature 20.0 °C
6.11 - 9.44 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Eastman Tenite Butyrate 485A2R30016 Natural Cellulose Acetate Butyrate
Plasticizer 16%. Weight loss on heating = 0.8% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.TENITE cellulosic plastics are noted for their excellent balance of properties - toughness,..
CTE, linear 11.0 - 17.0 µm/m-°C

@Temperature 20.0 °C
6.11 - 9.44 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Eastman Tenite Butyrate 550E4861316 Clear, Trsp Cellulose Acetate Butyrate
Plasticizer 16%. Weight loss on heating = 0.8% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p..
CTE, linear 11.0 - 17.0 µm/m-°C

@Temperature 20.0 °C
6.11 - 9.44 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Eastman Tenite Propionate 307A2R30018 Natural, Trsp Cellulose Acetate Propionate
Plasticizer 18%. Weight loss on heating = 1% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of pro..
CTE, linear 11.0 - 17.0 µm/m-°C

@Temperature 20.0 °C
6.11 - 9.44 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Eastman Tenite Propionate 371A2R30009 Natural, Trsp Cellulose Acetate Propionate
Plasticizer 9%. Weight loss on heating = 0.4% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of pr..
CTE, linear 11.0 µm/m-°C

@Temperature 20.0 - 200 °C
6.11 µin/in-°F

@Temperature 68.0 - 392 °F
Crucible Steel CPM® S90V® (420V®) Tool Steel
CPM S90V is a unique tool steel made by the Crucible Particle Metallurgy process. It is a martensitic stainless steel with a high volume of vanadium carbides for exceptionally good wear resistance. ..
CTE, linear 11.0 - 12.0 µm/m-°C

@Temperature 1000 °C
6.11 - 6.67 µin/in-°F

@Temperature 1830 °F
Chosun Refractories CUN-198 Nozzle Brick
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
CTE, linear 11.0 - 17.0 µm/m-°C

@Temperature 20.0 °C
6.11 - 9.44 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Eastman Tenite Propionate 358A4000008 Clear, Trsp Cellulose Acetate Propionate
Plasticizer 14%. Weight loss on heating = 0.6% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p..
CTE, linear 11.0 µm/m-°C

@Temperature 20.0 - 200 °C
6.11 µin/in-°F

@Temperature 68.0 - 392 °F
ATI Allegheny Ludlum AL 444™ Ferritic Stainless Steel
Low carbon, low nitrogen ferritic stainless steel alloy. Characteristics:practically immune to chloride stress corrosion cracking, enhanced resistance to pitting and crevicing, good general corrosi..
CTE, linear 11.0 µm/m-°C

@Temperature 20.0 °C
6.11 µin/in-°F

@Temperature 68.0 °F
DIN 53752
Brandenburger BRA_GLA 3 Thermal Insulation Board
A material with high quality glass fibre fabric and roving layers in conjunction with heat resistant EP matrix, which provides a thermal protection with excellent compressive and flexural strength, ..
CTE, linear 11.0 µm/m-°C

@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C
6.11 µin/in-°F

@Thickness 0.0787 in,
Temperature 73.4 - 131 °F
ISO 11359
Ascend Performance Materials Vydyne® 50BW Nylon 66, Dry as Molded
Vydyne® 50BW is a general purpose Nylon 66 resin. Available in natural. Designed for extrusion applications that do not require use of a high-viscosity resin. This resin offers a well-balanced comb..
CTE, linear 11.0 - 13.0 µm/m-°C

@Temperature 20.0 °C
6.11 - 7.22 µin/in-°F

@Temperature 68.0 °F
Parallel DOM
Alliance A-5-7 Alnico Magnetic Material
CTE, linear 11.0 - 170 µm/m-°C
6.11 - 94.4 µin/in-°F
Average value: 44.8 µm/m-°C Grade Count:36
Overview of materials for Cellulose Acetate Butyrate, Molded
This property data is a summary of similar materials in the MatWeb database for the category "Cellulose Acetate Butyrate, Molded". Each property range of values reported is minimum and maximum value..
CTE, linear 11.0 µm/m-°C
6.11 µin/in-°F
Mo-Sci Corporation YB-40-I Yellow B Filter Glass
Applications: Lead-free NVIS Yellow class B filter glass for incandescent light sources.Information provided by Mo-Sci Corporation.
CTE, linear 11.0 µm/m-°C
6.11 µin/in-°F
Mo-Sci Corporation YB-40-N Yellow B Filter Glass
Applications: Lead-free NVIS Yellow class B filter glass for white LED sources.Information provided by Mo-Sci Corporation.
CTE, linear 11.0 - 17.0 µm/m-°C

@Temperature 20.0 °C
6.11 - 9.44 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Eastman Tenite Butyrate 513E3720012 Clear, Trsp Cellulose Acetate Butyrate  (discontinued **)
Plasticizer 8%. Weight loss on heating = 0.7% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of pr..