Ravago Manufacturing Americas Hybrid S459 ABS + Polycarbonate Alloy
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Ravago Manufacturing Americas, LLC |
| Trade Name | Hybrid |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ravago Manufacturing Americas Hybrid S459 ABS + Polycarbonate Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Entec's proprietary products include a full range of compounds in the Nylon 6/6, Nylon 6, ABS, PBT, Polycarbonate, PC/ABS, PC/ASA, PC/PBT, and PPO/PPE resin families.Information provided by Ravago.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | 0.125 in; ASTM D955 |
| Melt Flow | 4.1 g/10 min @Load 3.80 kg, Temperature 230 °C |
4.1 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| 5.7 g/10 min @Load 2.16 kg, Temperature 260 °C |
5.7 g/10 min @Load 4.76 lb, Temperature 500 °F |
ASTM D1238 | |
| 14.8 g/10 min @Load 3.80 kg, Temperature 260 °C |
14.8 g/10 min @Load 8.38 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 53.8 MPa | 7800 psi | ASTM D638 |
| Elongation at Break | 60 % | 60 % | ASTM D638 |
| Flexural Yield Strength | 68.9 MPa | 10000 psi | ASTM D790 |
| Flexural Modulus | 2.34 GPa | 340 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | Unannealed (0.125 in); ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.6 °C | 204 °F | Unannealed (0.125 in); ASTM D648 |
| Flammability, UL94 | HB | HB | 0.0590 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 232 - 243 °C | 450 - 470 °F | |
| Middle Barrel Temperature | 238 - 249 °C | 460 - 480 °F | |
| Front Barrel Temperature | 243 - 254 °C | 470 - 490 °F | |
| Nozzle Temperature | 249 - 260 °C | 480 - 500 °F | |
| Mold Temperature | 60.0 - 82.2 °C | 140 - 180 °F | |
| Drying Temperature | 104 °C | 220 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |
| Moisture Content | <= 0.020 % | <= 0.020 % | |
| Injection Pressure | 6.89 - 11.7 MPa | 1000 - 1700 psi | |
| Shot Size | 40 - 80 % | 40 - 80 % | |
| Screw Speed | 40 - 60 rpm | 40 - 60 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Rate | Moderate |