TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 20 PHR HAF Black (Typical)

Category	Polymer , Thermoset , Polyester, TS , Polyurethane, TS , Thermoset Polyurethane, Elastomer, Unreinforced , Rubber or Thermoset Elastomer (TSE)
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 20 PHR HAF Black (Typical).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is carried out by the use of various peroxides including dicumyl peroxide (DCP) or 2,5-dimethyl-2,5-bis (t-butylperoxy) hexane (DBPH).All information provided by TSE Industries

Physical Properties	Metric	English	Comments
Specific Gravity	1.28 g/cc	1.28 g/cc
Mooney Viscosity	70 @Temperature 100 °C	70 @Temperature 212 °F	ML 1+4

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	62	62	aged 70 hours at 250ºF
	62	62	aged 70 hours at 300ºF
	66	66
	66	66	aged 70 hours at 250ºF in ASTM Oil #903
	66	66	aged 96 hours at 158ºF
	66	66
	67	67
	67	67	aged 70 hours at 250ºF in ASTM Oil #901
Tensile Strength, Yield	16.5 MPa	2400 psi
	21.0 MPa	3050 psi	aged 70 hours at 300ºF
	22.8 MPa	3300 psi	aged 70 hours at 250ºF in ASTM Oil #901
	23.4 MPa	3400 psi	aged 70 hours at 250ºF in ASTM Oil #903
	25.9 MPa	3750 psi
	27.2 MPa	3950 psi	aged 70 hours at 250ºF
	29.0 MPa	4200 psi
	29.3 MPa	4250 psi	aged 96 hours at 158ºF
Elongation at Yield	300 %	300 %
	370 %	370 %
	400 %	400 %
	410 %	410 %	aged 70 hours at 250ºF in ASTM Oil #903
	420 %	420 %	aged 70 hours at 250ºF
	420 %	420 %	aged 70 hours at 250ºF in ASTM Oil #901
	470 %	470 %	aged 96 hours at 158ºF
	490 %	490 %	aged 70 hours at 300ºF
100% Modulus	0.00352 GPa	0.510 ksi
200% Modulus	0.00979 GPa	1.42 ksi
300% Modulus	0.0121 GPa	1.75 ksi	aged 70 hours at 300ºF
	0.0156 GPa	2.26 ksi	aged 70 hours at 250ºF in ASTM Oil #901
	0.0157 GPa	2.28 ksi	aged 70 hours at 250ºF in ASTM Oil #903
	0.0165 GPa	2.40 ksi
	0.0179 GPa	2.60 ksi	aged 70 hours at 250ºF
	0.0185 GPa	2.68 ksi	aged 96 hours at 158ºF
	0.0186 GPa	2.70 ksi
	0.0190 GPa	2.75 ksi
Tear Strength	550 kN/m	3140 pli	ASTM Die C
Compression Set	20 % @Temperature 70.0 °C, Time 79200 sec	20 % @Temperature 158 °F, Time 22.0 hour	Method B

Thermal Properties	Metric	English	Comments
Minimum Service Temperature, Air	-33.4 °C	-28.1 °F	Retraction Temperature, TR10; ASTM D1329
	-23.7 °C	-10.7 °F	Retraction Temperature, TR10; ASTM D1329
	-11.0 °C	12.2 °F	Retraction Temperature, TR10; ASTM D1329
	-3.40 °C	25.9 °F	Retraction Temperature, TR10; ASTM D1329
Brittleness Temperature	-59.0 °C	-74.2 °F	Bell

Descriptive Properties	Value	Comments
Bashore Resilience (%)	47
Gehman Modulus (ºC)	-25.5	T2
	-33.1	T5
	-35	T10
	-39.5	T100
Mooney Scorch	25	t5, minutes; MS @ 121ºC
Volume Change (%)	-0.67	aged 70 hours at 250ºF in ASTM Oil #901
	-1.03	aged 70 hours at 250ºF in ASTM Oil #903
	1.3	aged 7 days at Room Temp in ASTM Fuel A
	16	aged 7 days at Room Temp in ASTM Fuel B