Polymer Resources TP-FV699 PBT, 10% Glass Reinforced Structural Foam Grade, Low Shrinkage

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled
Manufacturer Polymer Resources, LTD
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources TP-FV699 PBT, 10% Glass Reinforced Structural Foam Grade, Low Shrinkage.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Process: Foam MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Foam grades tested with foamed parts with a 10% weight reduction relative to unfoamed parts.Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ASTM D792
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
ASTM D955
Melt Flow 4.0 - 12 g/10 min
4.0 - 12 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 49.0 MPa
7100 psi
ASTM D638
Tensile Strength, Yield 49.0 MPa
7100 psi
ASTM D638
Flexural Strength 81.4 MPa
11800 psi
ASTM D790
Flexural Modulus 2.90 GPa
420 ksi
ASTM D790
Izod Impact, Unnotched 9.61 J/cm
18.0 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 113 °C
235 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 105 °C
221 °F
ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 238 - 254 °C
460 - 490 °F
Middle Barrel Temperature 243 - 260 °C
470 - 500 °F
Front Barrel Temperature 249 - 266 °C
480 - 510 °F
Melt Temperature 249 - 260 °C
480 - 500 °F
Mold Temperature 71.1 - 93.3 °C
160 - 200 °F
Drying Temperature 82.2 - 121 °C
180 - 250 °F
Dry Time 3 - 4 hour
3 - 4 hour