Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 49.0 MPa | 7100 psi | ASTM D638 |
Polymer Resources PPX-FR2-[color]EN Modified PPO, UL 94 V-1 with HDT of 210 F, Extrusion Grade Process: ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
Tensile Strength, Yield | 49.0 MPa | 7100 psi | ASTM D638 |
Polymer Resources TP-FV699 PBT, 10% Glass Reinforced Structural Foam Grade, Low Shrinkage Process: Foam MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Foam grades tested with foamed parts with a 10% weight reduction rel.. |
|||
Tensile Strength, Yield | 49.0 - 100 MPa | 7100 - 14500 psi | Average value: 76.6 MPa Grade Count:32 |
Overview of materials for Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled".Specific grades with glass content between 5% .. |
|||
Tensile Strength, Yield | 49.0 MPa | 7100 psi | ASTM D638 |
Kostat ICP-STAT ICS-1001 PET Sheet KOSTATs ICP-STAT is a thermoplastic sheet coated with an inherently conductive polymer (ICP). ICP-STAT has distinctive advantages in ESD and cleanliness performances compared to other materials bas.. |
|||
Tensile Strength, Yield | 49.0 MPa | 7100 psi | ASTM D638 |
Kostat ICP-STAT ICS-1005 ABS Sheet KOSTATs ICP-STAT is a thermoplastic sheet coated with an inherently conductive polymer (ICP). ICP-STAT has distinctive advantages in ESD and cleanliness performances compared to other materials bas.. |
|||
Tensile Strength, Yield | 49.0 MPa | 7100 psi | ASTM D638 |
Kostat ICP-STAT ICD-1001 PET Sheet KOSTATs ICP-STAT is a thermoplastic sheet coated with an inherently conductive polymer (ICP). ICP-STAT has distinctive advantages in ESD and cleanliness performances compared to other materials bas.. |
|||
Tensile Strength, Yield | 49.0 MPa | 7100 psi | ASTM D638 |
Kostat ICP-STAT ICD-1005 ABS Sheet KOSTATs ICP-STAT is a thermoplastic sheet coated with an inherently conductive polymer (ICP). ICP-STAT has distinctive advantages in ESD and cleanliness performances compared to other materials bas.. |
|||
Tensile Strength, Yield | 49.0 MPa | 7100 psi | ASTM D638 |
Techmer ES HiFill® ASA 778 UV WT168 Availability: North AmericaForms: PelletsAdditive: UV StabilizerFeatures: Good UV ResistanceAppearance: WhiteInformation provided by TP Composites, Inc. |
|||
Tensile Strength, Yield | 49.0 MPa | 7100 psi | ASTM D638 |
Techmer ES HiFill® PA6 L N MB (Conditioned) Availability: North AmericaForms: PelletsAdditive: Lubricant and Nucleating AgentFeatures: Lubricated, Fast Molding Cycle, Good Processability and NucleatedTPCI# 7964102Information provided by TP Co.. |
|||
Tensile Strength, Yield | 49.0 MPa | 7100 psi | ASTM D638 |
Techmer ES HiFill® PA6 LE BK (Conditioned) Availability: North AmericaForms: PelletsAdditive: Lubricant and Nucleating AgentFeatures: Lubricated, Fast Molding Cycle, Good Processability, Low Extractables and NucleatedAppearance: BlackTPCI# 7.. |
|||
Tensile Strength, Yield | 49.0 MPa | 7100 psi | ASTM D638 |
Techmer ES Luriblend® PC TL15 Availability: North AmericaForms: PelletsAdditive: PTFE LubricantFeatures: LubricatedInformation provided by TP Composites, Inc. |
|||
Tensile Strength, Yield | 49.0 MPa | 7100 psi | ASTM D 638 |
Styrolution PS 1300/1301 GPPS Profile extrusionGood balance of flow and strengthHigh stiffnessUSP Class VI certifiedUL Classification 94 HBInformation provided by Styrolution |
|||
Tensile Strength, Yield | 49.0 MPa @Thickness 3.17 mm |
7100 psi @Thickness 0.125 in |
ASTM D638 |
Samsung Cheil Industries Starex® SR-0310 Heat Resistant Grade ABS Information provided by Polymer Technology and Services, LLC (PTS). |
|||
Tensile Strength, Yield | 49.0 MPa @Thickness 3.17 mm |
7100 psi @Thickness 0.125 in |
ASTM D638 |
Samsung Cheil Industries Starex® SR-0310 Heat Resistant Grade ABS Information provided by Polymer Technology and Services, LLC (PTS). |
|||
Tensile Strength, Yield | 49.0 MPa | 7100 psi | ASTM 638 |
PlastxWorld CEVIAN®-V 500 ABS Medium Impact ABSThese are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc. |
|||
Tensile Strength, Yield | 49.0 MPa | 7100 psi | chs 2 in/min; ASTM D638 |
Diamond Polymers ABS 1501 Description: Injection Molding GradeInformation provided by Diamond Polymers, Inc. |
|||
Tensile Strength, Yield | 49.0 MPa | 7100 psi | chs 2 in/min; ASTM D638 |
Diamond Polymers ABS 1501E Description: Extrusion GradeInformation provided by Diamond Polymers, Inc. |
|||
Tensile Strength, Yield | 49.0 MPa | 7100 psi | chs 2 in/min; ASTM D638 |
Diamond Polymers ABS 1502 Description: Injection Molding Grade, High GlossInformation provided by Diamond Polymers, Inc. |
|||
Tensile Strength, Yield | 49.0 MPa | 7100 psi | chs 2 in/min; ASTM D638 |
Diamond Polymers ABS 4003HH Description: Heat Resistant Grade, Very High HeatInformation provided by Diamond Polymers, Inc. |
|||
Tensile Strength, Yield | 49.0 MPa | 7100 psi | chs 2 in/min; ASTM D638 |
Diamond Polymers ABS TR-7 Description: High Heat ABSInformation provided by Diamond Polymers, Inc. |
|||
Tensile Strength, Yield | 49.0 MPa | 7100 psi | chs 2 in/min; ASTM D638 |
Diamond Polymers ASA S610 Description: ASA Weatherable Polymer, Injection Molding Grade, High ImpactInformation provided by Diamond Polymers, Inc. |
|||
Tensile Strength, Yield | 49.0 MPa | 7100 psi | ASTM D792 |
Clariant Renol PURSP0005 Polyurethane Elastomer, Glass Fiber Reinforced Data provided by Clariant Masterbatches |
|||
Tensile Strength, Yield | 49.0 MPa | 7100 psi | ASTM D-638 |
Axiall 9275J Clear 38 Rigid PVC, Molding, Clear 38 Georgia Gulf 9275J Clear 38 is a food grade used for injection blow molded packages in critical medical, cosmetic and toiletry applications. All ingredients are FDA approved.Information provided by.. |
|||
Tensile Strength, Yield | 49.0 MPa | 7100 psi | ASTM D-638 |
Axiall 3152 Rigid PVC, Extrusion Georgia Gulf 3152 is a twin screw powder blend NSF approved for the extrusion of potable water and drain waste and vent pipe application.Information provided by Georgia GulfGeorgia Gulf became Axial.. |
|||
Tensile Strength, Yield | 49.0 MPa | 7100 psi | ASTM D-638 |
Axiall MD-5009 Rigid PVC, Molding Georgia Gulf MD-5009 is a rigid, fitting-grade PVC compound designed for hot spruce/runner molds, large parts and multi-cavity molds. This compound is characterized by excellent processability, whi.. |
|||
Tensile Strength, Yield | 49.0 MPa | 7100 psi | ASTM D-638 |
Axiall 5006 Rigid PVC, Extrusion, White Georgia Gulf 5006 White is a rigid PVC pellet compound designed for extrusion of rigid PVC house siding, window profiles and various contours where maximum weather resistance is required. Georgia G.. |
|||
Tensile Strength, Yield | 49.0 MPa | 7100 psi | ASTM D638 |
Polymer Resources PPX-FR2 Modified PPO, UL 94 V-1 with HDT of 210 F
(Unverified Data**) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
Tensile Strength, Yield | 49.0 - 227 MPa | 7100 - 32900 psi | Average value: 137 MPa Grade Count:11 |
Overview of materials for Thermoplastic Polyurethane (TPUR), Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Thermoplastic Polyurethane (TPUR), Glass Fiber Reinforced". Each property range of values reported is mi.. |
|||
Tensile Strength, Yield | 49.0 MPa | 7100 psi | 2.0 in/min; ASTM D638 |
LTL Color Compounds ColorFast® PCT2014 PC/PBT Alloy PC/PBT alloy with improved impact strengthAll information provided by LTL Color Compounders, Inc. |
|||
Tensile Strength, Yield | 49.0 MPa | 7100 psi | chs 2 in/min; ASTM D638 |
Diamond Polymers ABS/PC 9801 Description: Injection Molding Grade, High Impact, High HeatInformation provided by Diamond Polymers, Inc. |