PolyOne LubriOne™ NL-30GF/15T Black Polyamide 612 (Nylon 612)
| Category | Polymer , Thermoplastic , Nylon , Nylon 612 |
| Manufacturer | PolyOne Corporation |
| Trade Name | LubriOne™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne LubriOne™ NL-30GF/15T Black Polyamide 612 (Nylon 612).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. LubriOne compounds have been demonstrated to reduce friction, noise, vibration, heat buildup and improve product durability.Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | @ 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.020 cm/cm | 0.010 - 0.020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 119 MPa | 17300 psi | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Strength, Yield | 119 MPa | 17300 psi | ASTM D638 |
| Elongation at Break | 3.6 % | 3.6 % | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 8.45 GPa | 1230 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 191 MPa | 27700 psi | ASTM D790 |
| Flexural Modulus | 7.24 GPa | 1050 ksi | ASTM D790 |
| Izod Impact, Notched | 0.960 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.80 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A |
| Coefficient of Friction, Dynamic | 0.13 | 0.13 | vs. Steel - Dynamic; ASTM D1894 |
| Coefficient of Friction, Static | 0.18 | 0.18 | vs. Steel - Static; ASTM D1894 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 18.0 µm/m-°C | 10.0 µin/in-°F | ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C @Thickness 3.18 mm |
414 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C @Thickness 3.18 mm |
383 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 243 - 271 °C | 469 - 520 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Drying Temperature | 71.1 - 76.7 °C | 160 - 170 °F | |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Black | |
| Features | Good Wear Resistance | |
| High Stiffness | ||
| Lubricated | ||
| Forms | Pellets | |
| Generic Material | Nylon 612 | |
| Generic Name | Polyamide 612 (Nylon 612) | |
| Processing Method | Injection Molding | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| RoHS Compliance | RoHS Compliant | |
| Uses | Appliance Components | |
| Automotive Applications | ||
| Bearings | ||
| Business Equipment | ||
| Consumer Applications | ||
| Conveyor Parts | ||
| Gears | ||
| Industrial Applications | ||
| Printer Parts | ||
| Pulleys | ||
| Rollers |