Plastcom SLOVASTER® B1 GF 15 FRL 4 PBT reinforced with glass fibers, flame retarded

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Glass Fiber Filled, Flame Retardant
Manufacturer Plastcom spol. s r.o.
Trade Name SLOVASTER®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plastcom SLOVASTER® B1 GF 15 FRL 4 PBT reinforced with glass fibers, flame retarded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PBT reinforced with 15 % glass fiber, flame retarded with the halogen flame retardant. Anisotropy of shrinkage enables the injection molding of round, cylindrical or other hole products. Application in engineering, electrical and automotive industry. High mechanical properties also in conditioned status. Delivered in natural mode and in the full RAL color scale.Information Provided by Plastcom spol. s r.o.
Physical Properties Metric English Comments
Density 1.52 g/cc
0.0549 lb/in³
STN EN ISO 1183-1
Filler Content 15 %
15 %
Linear Mold Shrinkage 0.0090 cm/cm
0.0090 in/in
STN EN ISO 294-4
Linear Mold Shrinkage, Transverse 0.010 cm/cm
0.010 in/in
STN EN ISO 294-4
Melt Flow 15 g/10 min

@Load 2.16 kg,
Temperature 250 °C
15 g/10 min

@Load 4.76 lb,
Temperature 482 °F
STN EN ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 90.0 MPa
13100 psi
STN EN ISO 527-2
Elongation at Break 5.0 %
5.0 %
STN EN ISO 527-2
Tensile Modulus 5.60 GPa
812 ksi
STN EN ISO 527-2
Flexural Strength 185 MPa
26800 psi
STN EN ISO 178
Flexural Modulus 5.30 GPa
769 ksi
STN EN ISO 178
Charpy Impact Unnotched 4.50 J/cm²

@Temperature -20.0 °C
21.4 ft-lb/in²

@Temperature -4.00 °F
STN EN ISO 179
5.00 J/cm²

@Temperature 23.0 °C
23.8 ft-lb/in²

@Temperature 73.4 °F
STN EN ISO 179
Charpy Impact, Notched 0.600 J/cm²

@Temperature 23.0 °C
2.86 ft-lb/in²

@Temperature 73.4 °F
STN EN ISO 179
0.600 J/cm²

@Temperature -20.0 °C
2.86 ft-lb/in²

@Temperature -4.00 °F
STN EN ISO 179
Thermal Properties Metric English Comments
Melting Point 250 °C
482 °F
STN EN 11357-1
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
401 °F
STN EN ISO 75-2 (A)
Vicat Softening Point 200 °C
392 °F
STN EN ISO 306
Flammability, UL94 V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
Glow Wire Test 960 °C

@Thickness 3.00 mm
1760 °F

@Thickness 0.118 in
STN EN 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+18 ohm-cm
1.00e+18 ohm-cm
STN 34 6460
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
STN 34 6460
Dielectric Strength 22.0 kV/mm
559 kV/in
STN EN 60243-2
Comparative Tracking Index 450 V
450 V
STN EN 60112
Processing Properties Metric English Comments
Melt Temperature 240 - 260 °C
464 - 500 °F
Mold Temperature 70.0 - 80.0 °C
158 - 176 °F
Drying Temperature 80.0 °C

@Time 14400 sec
176 °F

@Time 4.00 hour
Moisture Content 0.10 %
0.10 %
STN EN ISO 3344
Injection Pressure 70.0 - 90.0 MPa
10200 - 13100 psi