Plaskolite Optix® CP - 1000 E High Impact Grade Acrylic Resin

Category Polymer , Thermoplastic , Acrylic (PMMA) , Acrylic, Impact Modified, Molded , Acrylic, Optical Grade, Molded
Manufacturer Plaskolite
Trade Name Optix®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plaskolite Optix® CP - 1000 E High Impact Grade Acrylic Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
OPTIX® impact-modified grades offer 7 to 10 times the impact resistance of general purpose polymers while maintaining optical clarity.Information provided by Plaskolite, Inc.
Physical Properties Metric English Comments
Density 1.16 g/cc
0.0419 lb/in³
ASTM D-792
Linear Mold Shrinkage 0.0020 - 0.0060 cm/cm
0.0020 - 0.0060 in/in
ASTM D-955
Melt Flow 1.1 g/10 min

@Load 3.80 kg,
Temperature 230 °C
1.1 g/10 min

@Load 8.38 lb,
Temperature 446 °F
ASTM D-1238
Mechanical Properties Metric English Comments
Tensile Strength 44.9 MPa
6510 psi
ASTM D-638
Elongation at Break 38 %
38 %
ASTM D-638
Modulus of Elasticity 1.76 GPa
255 ksi
ASTM D-638
Flexural Strength 61.3 MPa
8890 psi
ASTM D-790
Izod Impact, Notched 0.641 J/cm

@Thickness 6.35 mm
1.20 ft-lb/in

@Thickness 0.250 in
ASTM D-256
Gardner Impact 6.33 J

@Thickness 3.17 mm
4.67 ft-lb

@Thickness 0.125 in
Falling Weight; ASTM D-3029 GB
Thermal Properties Metric English Comments
CTE, linear 120 µm/m-°C
66.7 µin/in-°F
ASTM D-696
Maximum Service Temperature, Air 90.0 °C
194 °F
UL-746 ABC
Deflection Temperature at 1.8 MPa (264 psi) 80.0 °C
176 °F
ASTM D-648
Vicat Softening Point 108 °C
227 °F
ASTM D-1525
Flammability, UL94 HB
HB
Optical Properties Metric English Comments
Haze <= 1.8 %
<= 1.8 %
ASTM D-1003
Transmission, Visible 90.7 %
90.7 %
ASTM D-1003
Descriptive Properties Value Comments
3-Year Weathering Listed
SAE J 576 (AMECA)