Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 1.1 g/10 min @Load 3.80 kg, Temperature 230 °C |
1.1 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D-1238 |
Plaskolite Optix® CP - 1000 E High Impact Grade Acrylic Resin OPTIX® impact-modified grades offer 7 to 10 times the impact resistance of general purpose polymers while maintaining optical clarity.Information provided by Plaskolite, Inc. |
|||
Melt Flow | 1.1 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.1 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Polimeri Europa Clearflex® FG 106 Hexene Copolymer Linear Low Density Polyethylene Clearflex FG 106 is a hexene copolymer linear low density polyethylene (C6-LLDPE), with antioxidants, suitable for blown film extrusion.Films manufactured with Clearflex FG 106 are characterized by .. |
|||
Melt Flow | 1.1 g/10 min | 1.1 g/10 min | ISO 1133:1997 |
Nanocyl PLASTICYL™ PP2001 Polypropylene with 5 wt% Multi-Wall Carbon Nanotubes PLASTICYL™ is a family of Multi-Wall Carbon Nanotube (MWNT) thermoplastic concentrates for applications requiring superior electrical conductivity and electrostatic discharge (ESD) properties. PLA.. |
|||
Melt Flow | 1.1 g/10 min @Load 3.80 kg, Temperature 230 °C |
1.1 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D-1238 |
Plaskolite West Optix® CA - 1000 E High Impact Acrylic Resin Optix® impact-modified grades exhibit 7 to 10 times the impact strength of general purpose grades and maintaining the superior optical properties. Each grade is offered in a grade(G) that resists g.. |
|||
Melt Flow | 1.1 g/10 min @Load 5.00 kg, Temperature 200 °C |
1.1 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM Data |
Americas Styrenics Styron® 495R High Impact Polystyrene
(discontinued **) Data provided by Dow Chemical.Americas Styrenics was formed in 2008 as a joint venture between Dow Chemical and Chevron Phillips Chemical Company. Styron was a Dow trade name before the JV formatio.. |
|||
Melt Flow | 1.1 g/10 min @Load 2.16 kg, Temperature 230 °C |
1.1 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
NOVA Chemicals Dylark® 520XT Glass Reinforced Engineering Resin Features: Higher toughness product, Excellent stiffness, High heat resistance, Superior adhesion to urethane foamApplications: Instrument panel substrates, Mid-Consoles, Center Stacks, Interior tri.. |
|||
Melt Flow | 1.1 g/10 min @Load 1.00 kg, Temperature 235 °C |
1.1 g/10 min @Load 2.20 lb, Temperature 455 °F |
ASTM D1238 |
Honeywell Aegisâ„¢ H155MP Nylon 6 Extrusion Grade Homopolymer Film Description: Aegis H155MP is a lubricated and nucleated high viscosity, nylon 6 extrusion grade homopolymer for cast or blown film. It conforms to Food and Drug Administration requirements of 21 CFR.. |
|||
Melt Flow | 1.1 - 1.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.1 - 1.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238-00 |
Ipiranga Petrochem PH 0130 Polypropylene The production of polypropylene (PP) employs Spheripol technology from Montell / Italy. This technology has been acclaimed all over the world and is known as clean technology, because it does not pr.. |
|||
Melt Flow | 1.1 g/10 min @Load 2.16 kg, Temperature 230 °C |
1.1 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
IRPC Polimaxx Polene 2511HX GA5 Polypropylene Compound CHARACTERISTICS: POLYPROPYLENE BLOCK COPOLYMER WITH 25% GLASS FIBRE REINFORCED VERY HIGH IMPACT STRENGTH, HIGH MECHANICAL STRENGTH, LOW SHRINKAGE, HIGH STIFFNESS, CONTAIN UV STABILIZER AND LONG TERM.. |
|||
Melt Flow | 1.1 g/10 min @Load 10.0 kg, Temperature 230 °C |
1.1 g/10 min @Load 22.0 lb, Temperature 446 °F |
ASTM D1238 |
Techmer ES Statiblend® PA6/6 02013 Availability: North AmericaForms: PelletsFiller/Reinforcement: Unspecified FillerReinforAdditive: Impact ModifierFeatures: Conductive and Impact ModifiedUL File Number: E157318TPCI# 1039101Informati.. |
|||
Melt Flow | 1.1 g/10 min @Load 2.20 kg |
1.1 g/10 min @Load 4.86 lb |
ASTM D1238 |
Sumitomo Chemical ESPOLEX® 817 Thermoplastic Elastomer ESPOLEX® TPE Series is a group of thermoplastic elastomers produced by Sumitomo Chemical Company. Among its material advantages, ESPOLEX® TPE Series is distinguished by offering many low-densi.. |
|||
Melt Flow | 1.1 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.1 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
DuPont Bynel® 4104 Anhydride-Modified LLDPE Adhesive Resin Bynel® Series 4100 resins are anhydride-modified, linear low-density polyethylene (LLDPE) resins. All 4100 Series resins are available in pellet form for use in conventional extrusion and coextrusi.. |
|||
Melt Flow | 1.1 g/10 min | 1.1 g/10 min | ASTM D1238 |
Westlake Elevate™ EF563 6.5% Ethylene Vinyl Acetate Copolymer Westlake EF 563 resin is a fractional melt index 6.5% EVA copolymer with excellent drawdown, low melting/dispersion, and clarity optics in a soft but very tough film. Kosher compliant.Application/U.. |
|||
Melt Flow | 1.1 g/10 min | 1.1 g/10 min | ASTM D1238 |
Westlake LF1020 Butene Linear Low Density Polyethylene Westlake LF1020 is a butene LLDPE with excellent mechanical and downgauging advantages. It is suitable for can liners, stretch wrap, agricultural film, and blending with LDPE. This Kosher compliant .. |
|||
Melt Flow | 1.1 g/10 min | 1.1 g/10 min | ASTM D1238 |
Westlake LF1021 Butene Linear Low Density Polyethylene Westlake LF1021 is a butene LLDPE with excellent mechanical and downgauging advantages. It is suitable for can liners, stretch wrap, agricultural film, and blending with LDPE. This Kosher compliant .. |
|||
Melt Flow | 1.1 g/10 min | 1.1 g/10 min | ASTM D1238L |
Total PPH 3281 Polypropylene, Extrusion Grade Low melt flow homopolymer for sheet extrusion, strapping, and in-line thermoforming applicationsMelt Strength – The high melt strength of FINA 3281 allows uniform drawdown during processing, result.. |
|||
Melt Flow | 1.1 g/10 min | 1.1 g/10 min | Condition D; ASTM D 1238 |
CPT C-Flex® R70-072 Opaque Biocompatible TPE C-Flex® is a family of patented thermoplastic elastomers which range in hardness from 5 shore A to 95 shore A. C-Flex® TPE's are biocompatible polymer blends which meet or exceed the current.. |
|||
Melt Flow | 1.1 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.1 g/10 min @Load 4.76 lb, Temperature 374 °F |
condition E; ASTM D1238 |
DuPont™ Surlyn® 9520 Ionomer Resin, Zinc Surlyn® 9520 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with zinc ions. The amount of MAA and neutr.. |
|||
Melt Flow | 1.1 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.1 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
ExxonMobil LD 103.59 Industrial Film Resin Product Description: LD 103 resins are homopolymer industrial film resins with excellent toughness. LD 103 resins have a low melt index, which provides good impact strength and melt strength over a .. |
|||
Melt Flow | 1.1 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.1 g/10 min @Load 4.76 lb, Temperature 374 °F |
ExxonMobil Method |
ExxonMobil Vistamaxx™ 3020FL Propylene-based Elastomer - High Purity, Low Gel Product Description: Vistamaxx 3020FL propylene-based elastomer is an olefinic elastomer primarily composed of isostatic propylene repeat units with random ethylene distribution. It is produced us.. |
|||
Melt Flow | 1.1 g/10 min @Load 5.00 kg, Temperature 230 °C |
1.1 g/10 min @Load 11.0 lb, Temperature 446 °F |
|
Arkema Group Kynar® 1000 HDC N 118 PVDF
(discontinued **) Designation ISO 12086-PVDF-E,GG1C,P.?E5.I.B.E.C,, ?(1.5-2.5)Kynar PVDF are fluorinated thermoplastic homopolymers.Outstanding characteristics of Kynar: chemical resistance, imperviousness to UV, hig.. |
|||
Melt Flow | 1.1 g/10 min | 1.1 g/10 min | Condition 230/3.8; ASTM D1238 |
Plaskolite West Optix® CA-1000 E Impact Modified Acrylic Resin Extrusion Grade Pellets. Excellent blend stock material for impact applications. |
|||
Melt Flow | 1.1 g/10 min @Load 2.16 kg, Temperature 230 °C |
1.1 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Solvay Engineered Polymers SEQUEL® E3000 HMS TPO
(discontinued **) Description: SEQUEL® E3000HMS thermoplastic olefinic elastomer (TPO) is designed for exterior and interior applications that require stiffness and durability. This extrusion-grade material is spec.. |
|||
Melt Flow | 1.1 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.1 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 - ISO 1133 |
DuPont Elvaloy® 3107 AC Ethylene and 7% Butyl Acrylate Copolymer
(discontinued **) Elvaloy® 3107 AC contains antioxidant, slip and antiblock additives.Elvaloy® 3107 AC is developed to give films with good sealing properties, impact strength at lower temperature, and low shrinkag.. |
|||
Melt Flow | 1.1 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.1 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
LG Chemical LC175 Polyolefin Elastomer for Polymer Modification Features: Improved impact strength in polypropylene; Excellent filler acceptance; Available as pellet form; Outstanding toughness with flexible performance; and Reduction of product weightApplicatio.. |
|||
Melt Flow | 1.1 g/10 min | 1.1 g/10 min | ASTM D1238 |
Huntsman Rexell® L8101 Cast Film Extrusion LLDPE
(discontinued **) Linear-low density copolymer, general purpose blown film extrusion, FDA compliant.Features: Excellent combination of sealability, mechanical strength and optics.Applications: Sealing layer in coextr.. |
|||
Melt Flow | 1.1 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.1 g/10 min @Load 4.76 lb, Temperature 374 °F |
Procedure A; ASTM D1238 |
PolyOne Syncure™ S1044B Polyethylene, Crosslinked (XLPE) Available as Catalyst Masterbatch component for PolyOne Syncure System.Gel values are >70, and were measured on a 90 phr S1054A / 10 phr S1044B Syncure System; and cured for 8 hours in steam. Pellet.. |
|||
Melt Flow | 1.1 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.1 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 - ISO 1133 |
DuPont Elvaloy® 3108 AC Ethylene and 7% Butyl Acrylate Copolymer
(discontinued **) Elvaloy® 3108 AC contains antioxidant, slip and antiblock additives.Elvaloy® 3108 AC is developed to give films with good sealing properties, impact strength at lower temperature, and low shrinkag.. |
|||
Melt Flow | 1.1 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.1 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
DuPont Bynel® 41E558 Anhydride-Modified LLDPE Adhesive Resin
(discontinued **) Bynel® Series 4100 resins are anhydride-modified, linear low-density polyethylene (LLDPE) resins. All 4100 Series resins are available in pellet form for use in conventional extrusion and coextrusi.. |