Overview of materials for Nylon, Flexible Alloy

Category Polymer , Thermoplastic , Nylon , Nylon, Flexible Alloy
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Nylon, Flexible Alloy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Nylon, Flexible Alloy". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.01 - 1.14 g/cc
0.0365 - 0.0412 lb/in³
Average value: 1.06 g/cc Grade Count:20
Water Absorption 1.60 - 6.40 %
1.60 - 6.40 %
Average value: 5.62 % Grade Count:18
Moisture Absorption at Equilibrium 1.10 - 2.70 %
1.10 - 2.70 %
Average value: 1.73 % Grade Count:17
Melt Flow 0.300 - 7.00 g/10 min
0.300 - 7.00 g/10 min
Average value: 2.70 g/10 min Grade Count:20
Mechanical Properties Metric English Comments
Tensile Strength, Yield 20.0 - 79.3 MPa
2900 - 11500 psi
Average value: 35.6 MPa Grade Count:21
21.3737 - 125.485 MPa

@Temperature -40.0 - 121 °C
3100.01 - 18200.0 psi

@Temperature -40.0 - 250 °F
Average value: 73.4 MPa Grade Count:1
Elongation at Break 15.0 - 70.0 %
15.0 - 70.0 %
Average value: 48.4 % Grade Count:24
8.00 - 8.00 %

@Temperature -40.0 - 121 °C
8.00 - 8.00 %

@Temperature -40.0 - 250 °F
Average value: 154 % Grade Count:1
Elongation at Yield 4.00 - 10.0 %
4.00 - 10.0 %
Average value: 6.68 % Grade Count:18
Modulus of Elasticity 0.200 - 2.20 GPa
29.0 - 319 ksi
Average value: 1.02 GPa Grade Count:20
Charpy Impact, Notched 1.25 J/cm² - NB
5.95 ft-lb/in² - NB
Average value: 4.72 J/cm² Grade Count:3
0.900 - 2.20 J/cm²

@Temperature -30.0 - -30.0 °C
4.28 - 10.5 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 1.38 J/cm² Grade Count:3
Tensile Creep Modulus, 1 hour 420 - 1520 MPa
60900 - 220000 psi
Average value: 938 MPa Grade Count:11
Tensile Creep Modulus, 1000 hours 270 - 690 MPa
39200 - 100000 psi
Average value: 464 MPa Grade Count:11
Thermal Properties Metric English Comments
CTE, linear 60.0 - 170 µm/m-°C
33.3 - 94.4 µin/in-°F
Average value: 104 µm/m-°C Grade Count:3
Melting Point 216 - 220 °C
420 - 428 °F
Average value: 220 °C Grade Count:24
Deflection Temperature at 0.46 MPa (66 psi) 47.0 - 204 °C
117 - 399 °F
Average value: 156 °C Grade Count:4
Vicat Softening Point 97.0 - 99.0 °C
207 - 210 °F
Average value: 97.3 °C Grade Count:6
Flammability, UL94 HB - V-0
HB - V-0
Grade Count:23
Electrical Properties Metric English Comments
Electrical Resistivity 7.40e+13 - 2.00e+14 ohm-cm
7.40e+13 - 2.00e+14 ohm-cm
Average value: 1.00e+14 ohm-cm Grade Count:5
Surface Resistance 1.30e+13 - 1.00e+15 ohm
1.30e+13 - 1.00e+15 ohm
Average value: 8.03e+14 ohm Grade Count:5
Dielectric Constant 3.10 - 4.80
3.10 - 4.80
Average value: 3.79 Grade Count:5
Dielectric Strength 34.0 - 39.0 kV/mm
864 - 991 kV/in
Average value: 36.2 kV/mm Grade Count:5
Dissipation Factor 0.00600 - 0.130
0.00600 - 0.130
Average value: 0.0789 Grade Count:5
Comparative Tracking Index 600 V
600 V
Average value: 600 V Grade Count:23