Overview of materials for Nylon 11, Powder

Category	Polymer , Thermoplastic , Nylon , Nylon 11 , Nylon 11, Powder
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Overview of materials for Nylon 11, Powder.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

This property data is a summary of similar materials in the MatWeb database for the category "Nylon 11, Powder". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.

Physical Properties	Metric	English	Comments
Density	1.04 - 1.35 g/cc	0.0376 - 0.0488 lb/in³	Average value: 1.11 g/cc Grade Count:8
Water Absorption	1.90 %	1.90 %	Average value: 1.90 % Grade Count:8

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	38.0 - 47.0 MPa	5510 - 6820 psi	Average value: 42.5 MPa Grade Count:3
Taber Abrasion, mg/1000 Cycles	17.0	17.0	Average value: 17.0 Grade Count:3

Thermal Properties	Metric	English	Comments
CTE, linear	150 µm/m-°C	83.3 µin/in-°F	Average value: 150 µm/m-°C Grade Count:3
Melting Point	185 °C	365 °F	Average value: 185 °C Grade Count:8
Vicat Softening Point	160 °C	320 °F	Average value: 160 °C Grade Count:8
Flammability, UL94	HB - V-2	HB - V-2	Grade Count:8

Electrical Properties	Metric	English	Comments
Electrical Resistivity	1.00e+14 - 3.50e+14 ohm-cm	1.00e+14 - 3.50e+14 ohm-cm	Average value: 1.68e+14 ohm-cm Grade Count:11
Surface Resistance	1.00e+14 - 2.40e+14 ohm	1.00e+14 - 2.40e+14 ohm	Average value: 1.38e+14 ohm Grade Count:11
Dielectric Constant	3.10 - 3.90	3.10 - 3.90	Average value: 3.50 Grade Count:3
Dielectric Strength	9.00 - 30.5 kV/mm	229 - 775 kV/in	Average value: 28.2 kV/mm Grade Count:11