Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | ASTM D638 |
Shell Carilon® DB6F0A10 Polyketone, Flame-Retarded (V-0) Injection Molding Grade
(discontinued **) Shell announced in Feb. 2000 that the Carilon product line is being discontinued. CARILON Polymer DB6F0A10 is a flame-retarded injection molding grade with mechanical properties which classify it a.. |
|||
Tensile Strength, Ultimate | 38.0 MPa @Temperature 90.0 °C |
5510 psi @Temperature 194 °F |
ISO 527 |
LATI LARIL 13-V1KC Mineral Filled Polyphenylene Oxide (PPOm) (UL94V-1)
(Unverified Data**) Description: Laril thermoplastics are polyphenylene oxide (PPOm) products. They exhibit excellent toughness, even at low temperatures, good thermal resistance and dimensional stability are the most .. |
|||
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | ASTM D638 |
PolyOne Lubri-Tech™ AT-15GP/05T Acetal With Graphite - 5% PTFE
(discontinued **) Data provided by PolyOne. |
|||
Tensile Strength, Ultimate | 38.0 - 120 MPa | 5510 - 17400 psi | Average value: 64.6 MPa Grade Count:17 |
Overview of materials for Phenolic, Novolac, Cellulose Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Cellulose Filled". Each property range of values reported is minimum and maximum valu.. |
|||
Tensile Strength, Ultimate | 38.0 - 105 MPa | 5510 - 15200 psi | Average value: 70.9 MPa Grade Count:17 |
Overview of materials for Nylon 6, 20% Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 20% Mineral Filled". Specific grades with primary filler content between 15% and 24% are includ.. |
|||
Tensile Strength, Ultimate | 38.0 - 110 MPa | 5510 - 16000 psi | Average value: 88.2 MPa Grade Count:25 |
Overview of materials for Nylon 12, 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, 20% Glass Fiber Filled". Specific grades with glass content between 15% and 24% are included. .. |
|||
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | ASTM D638 |
IDI Composites 44-10 MW Thermoset Polyester, Molding Moderate strength material specifically formulated for microwave oven performance.Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | ASTM D638 |
IDI Composites W-102 Thermoset Polyester, Molding Premium appearance grade materials in a range of strengths for cookware and appliance applications.Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | ASTM D638 |
Ineos Innovene H07B-00 Polypropylene Homopolymer Extrusion. Features: No Slip, Antiblock.Applications: Cast filmTypical property data below from injection molded samples. |
|||
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | at max load; ASTM D638 |
A. Schulman POLYPUR™ FPU 1109 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | at max load; ASTM D638 |
A. Schulman POLYPUR™ FPU 1112 Thermoplastic Polyurethane Compound (15% Glass) Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 388 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 388 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | at max load; ASTM D638 |
A. Schulman POLYPUR™ FPU 1112 Thermoplastic Polyurethane Compound (15% Glass) Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | DIN 53504 |
Lubrizol ESTANE® 58888 Ether Based Thermoplastic Polyurethane (European Grade) Description: Estane® thermoplastic polyurethanes (TPUs) include elastomeric materials that bridge the gap between flexible rubber and rigid plastics. These materials offer toughness and durability .. |
|||
Tensile Strength, Ultimate | 38.0 MPa @Temperature 80.0 °C |
5510 psi @Temperature 176 °F |
ASTM D638 |
Toyobo T-661 Nylon 66, Standard Grade (DAM) Features: Non-reinforced, Standard GradeInformation provided by Toyobo. |
|||
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 388 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | at max load; ASTM D638 |
A. Schulman POLYPUR™ FPU 1109 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | DIN 53504 |
Lubrizol ESTANE® 58237 Ether Based Thermoplastic Polyurethane (European Grade) Description: Estane® thermoplastic polyurethanes (TPUs) include elastomeric materials that bridge the gap between flexible rubber and rigid plastics. These materials offer unmatched toughness and d.. |
|||
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | ISO 527-1 |
Chengdu Polyster CH7563 Thermoplastic Polyether-ester Elastomer (TPEE) Poly-basic block copolymer. Good compatibility with PBT, PET and PA. For blending with PBT, PET and PA to improve impact resilience properties.Information provided by Chengdu Polyster Co., Ltd. |
|||
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | ASTM D638/D412 |
Covestro Bayflex® 190 Polyurethane Elastomeric RIM, 20% Mineral Filled, MDI-based 2-Component Liquid System 0.150 in. thickness. Calcium Silicate filled. RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was se.. |
|||
Tensile Strength, Ultimate | 38.0 - 47.0 MPa | 5510 - 6820 psi | |
Arkema Group Rilsan® Fine Powders Grey 49 Polyamide 11 Rilsan® fine powder coatings offer weatherability, long-lasting adhesion, chalk resistance, chemical resistance to aliphatic hydrocarbons, bases, salt solutions, oils, greases and other petroleum p.. |
|||
Tensile Strength, Ultimate | 38.0 - 47.0 MPa | 5510 - 6820 psi | |
Arkema Group Rilsan® Fine Powders Natural Polyamide 11 Rilsan® fine powder coatings offer weatherability, long-lasting adhesion, chalk resistance, chemical resistance to aliphatic hydrocarbons, bases, salt solutions, oils, greases and other petroleum p.. |
|||
Tensile Strength, Ultimate | 38.0 - 47.0 MPa | 5510 - 6820 psi | |
Arkema Group Rilsan® Fine Powders Polyamide 11 Rilsan® fine powder coatings offer weatherability, long-lasting adhesion, chalk resistance, chemical resistance to aliphatic hydrocarbons, bases, salt solutions, oils, greases and other petroleum p.. |
|||
Tensile Strength, Ultimate | 38.0 MPa @Thickness 2.00 mm |
5510 psi @Thickness 0.0787 in |
molded plaque, cured 20 hr at 100°C; ASTM D412 |
BASF Elastollan® 1185A10W Wire & Cable Grade Polyurethane Elastomer As with all TPU products this grade must be dried prior to processing.Information provided by BASF Corporation. |
|||
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | ASTM D638 |
Solvay Specialty Polymers Algoflon® 0.1 Mos PTFE; Molybdenum Disulfide Filled
(discontinued **) Data provided by the manufacturer.0.1 wt.% Molybdenum Disulfide. Suspension polymer powder grade recommended for compression molding. Pure PTFE possesses high inertness, excellent dielectric propert.. |
|||
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 388 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 388 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | DIN 53504 |
Lubrizol ESTANE® T5191 Ether Based Thermoplastic Polyurethane (European Grade) Description: Estane® thermoplastic polyurethanes (TPUs) include elastomeric materials that bridge the gap between flexible rubber and rigid plastics. These materials offer toughness and durability .. |
|||
Tensile Strength, Ultimate | 38.0 - 89.3 MPa | 5510 - 13000 psi | Average value: 59.5 MPa Grade Count:125 |
Overview of materials for Acrylic, Optical Grade, Molded This property data is a summary of similar materials in the MatWeb database for the category "Acrylic, Optical Grade, Molded". Each property range of values reported is minimum and maximum values of.. |