Polymer Property : Dielectric Strength = 229 kV/in Product List

Electrical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Electrical Properties	Metric	English	Comments
Dielectric Strength	9.00 kV/mm	229 kV/in
Pyrotek TS-125 Thermoset Electrical Insulation Product Glass reinforcement, Polyester Resin, Brown Color. Very high mechanical strength at room and elevated temperature. Flame retardant.Information provided by Pyrotek.
Dielectric Strength	9.00 kV/mm	229 kV/in	Step by Step; ASTM D149
Plenco 2424 Phenolic, Granular, Injection Molded (discontinued **) Two-stage Phenolic. PLENCO 02424 is a black, two stage, general purpose phenolic molding compound. It has a good balance of properties for a general purpose type material. It is used in electrical ..
Dielectric Strength	9.00 - 30.5 kV/mm	229 - 775 kV/in	Average value: 28.2 kV/mm Grade Count:11
Overview of materials for Nylon 11, Powder This property data is a summary of similar materials in the MatWeb database for the category "Nylon 11, Powder". Each property range of values reported is minimum and maximum values of appropriate M..
Dielectric Strength	9.00 kV/mm	229 kV/in	AC 60 Hz
Fujipoly Industries SarconÂ® 30GHR Thin-Film GHR Sarcon HR is Fujipolys originally developed High Heat Conductive Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Sarcon GHR is a composite of ..
Dielectric Strength	9.00 kV/mm	229 kV/in	AC 60 Hz
Fujipoly Industries SarconÂ® 30H Thin-Film HR Sarcon HR is Fujipolys originally developed High Heat Conductive Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Sarcon GHR is a composite of ..
Dielectric Strength	9.00 kV/mm	229 kV/in	AC 60 Hz
Fujipoly Industries SarconÂ® 30U Thin-Film UR Sarcon UR is Fujipolys originally developed High Heat Conductive/Low Hardness Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Information prov..
Dielectric Strength	9.00 kV/mm	229 kV/in	-40Â°C for 1,000 hrs; JIS-K-6249; ASTM D149
Fujipoly Industries SarconÂ® NR-c Gap Filler Pad Non-Silicone Sarcon NR-c consists of an Acrylate resin and some thermal conductive fillers. It is a highly conformable/ thermally conductive material in a versatile sheet form that makes reliable and complete p..
Dielectric Strength	9.00 kV/mm	229 kV/in	ASTM D149-95a
Thermoseal KLINGERSIL® C-8200 Chemical Resistant Gasketing Synthetic FiberHypalon® BinderAcid ResistantGood Oil-Fuel ResistanceGood Gas SealabilityNo Color AddedInformation provided by Thermoseal Inc.
Dielectric Strength	9.00 kV/mm	229 kV/in	ASTM D149
Tipco Tipcolite® TG 211 Phenolic Compound, Mineral & Wood Flour, Soft Flow & High Electrical Properties Soft Flow Phenolic Compound, Reinforced with Mineral & Wood FlourApplications: Electrical & ElectronicsProcessing: Compression MoldingInformation provided by the Manufacturer, Tipco Industries Ltd..
Dielectric Strength	9.00 kV/mm	229 kV/in	ASTM D149
Tipco Tipcolite® THD 111 Phenolic Compound, Short Glass Fibers & Minerals, Medium -Soft Flow & High Strength Medium -Soft Flow Phenolic Compound, Reinforced with Short Glass Fibres & MineralsApplications: Automotives & ElectricalProcessing: Compression & TransferInformation provided by the Manufacturer, T..
Dielectric Strength	9.00 kV/mm	229 kV/in	ASTM D149
Tipco Tipcolite® THD 121 Phenolic Compound, Wood Flour, having Medium Flow & High Strength Medium Flow Phenolic Compound, Reinforced with Wood FlourApplications: Electrical & ElectronicsProcessing: Compression MoldingInformation provided by the Manufacturer, Tipco Industries Ltd., India...
Dielectric Strength	9.00 kV/mm	229 kV/in	ASTM D149
Tipco Tipcolite® THR 211 Phenolic Compound, Asbestos Wood Flour & Minerals, Soft Flow & High Electrical Properties Soft Flow Phenolic Compound, Reinforced with Asbestos Wood Flour & MineralsApplications: Switchgear, HRC FusesProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industrie..
Dielectric Strength	9.00 kV/mm	229 kV/in	ASTM D149
Tipco Tipcolite® TX 211 Phenolic Compound, Wood Flour, having Medium Flow & High Electrical Properties Medium Flow Phenolic Compound, Reinforced with Wood FlourApplications: Switchgear, HRC FusesProcessing: Compression MoldingInformation provided by the Manufacturer, Tipco Industries Ltd., India.
Dielectric Strength	9.00 kV/mm	229 kV/in	ASTM D149
Tipco Tipcolite® TX 321 Phenolic Compound, Wood Flour & Minerals, having Soft Flow & High Electrical Properties Soft Flow Phenolic Compound, Reinforced with Wood Flour & MineralsApplications: Switchgear, HRC FusesProcessing: Injection MouldingInformation provided by the Manufacturer, Tipco Industries Ltd., I..
Dielectric Strength	9.00 kV/mm	229 kV/in	ac; ASTM D116
CoorsTek Yttria Partially Stabilized Zirconia, YZTP, Sintered Thermal Shock Delta Tc = 350°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar..
Dielectric Strength	9.00 kV/mm	229 kV/in	AC; ASTM D116
CoorsTek YZTP Yttria Partially Stabilized Zirconia, Hipped Thermal Shock Delta Tc = 350°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar..
Dielectric Strength	9.00 kV/mm	229 kV/in	ac; ASTM D116
CoorsTek Zirconia-Toughened Alumina, ZTA Thermal Shock Delta Tc = 300°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar..
Dielectric Strength	9.00 kV/mm	229 kV/in	AC Rapid Rise; ASTM D149
DuPont™ Nomex® 411 Paper, 10 mil Nominal Thickness Nomex® Type 411 is the uncalendared precursor of Type 410. It has a lower density and lower property values. It is used in applications such as motor phase insulation and transformer coil end fil..
Dielectric Strength	9.00 kV/mm	229 kV/in	AC Rapid Rise; ASTM D149
DuPont™ Nomex® 411 Paper, 15 mil Nominal Thickness Nomex® Type 411 is the uncalendared precursor of Type 410. It has a lower density and lower property values. It is used in applications such as motor phase insulation and transformer coil end fil..
Dielectric Strength	9.00 kV/mm	229 kV/in	AC Rapid Rise; ASTM D149
DuPont™ Nomex® 411 Paper, 23 mil Nominal Thickness Nomex® Type 411 is the uncalendared precursor of Type 410. It has a lower density and lower property values. It is used in applications such as motor phase insulation and transformer coil end fil..
Dielectric Strength	9.00 kV/mm	229 kV/in	AC Rapid Rise; ASTM D149
DuPont™ Nomex® 411 Paper, 5 mil Nominal Thickness Nomex® Type 411 is the uncalendared precursor of Type 410. It has a lower density and lower property values. It is used in applications such as motor phase insulation and transformer coil end fil..
Dielectric Strength	9.00 kV/mm	229 kV/in	AC Rapid Rise; ASTM D149
DuPont™ Nomex® 411 Paper, 7 mil Nominal Thickness Nomex® Type 411 is the uncalendared precursor of Type 410. It has a lower density and lower property values. It is used in applications such as motor phase insulation and transformer coil end fil..
Dielectric Strength	9.00 kV/mm	229 kV/in	AC Rapid Rise; ASTM D149
DuPont™ Nomex® N196 Paper, 3 mil Nominal Thickness Nomex® Type N196 is a high floc grade of Nomex® paper. This leads to a high degree of saturability combined with high stiffness and mechanical properties. Type N196 is used where good saturabili..
Dielectric Strength	9.00 kV/mm @Thickness 0.400 mm	229 kV/in @Thickness 0.0157 in	thick
Arkema Group Rilsan® Fine Powders Grey 49 Polyamide 11 Rilsan® fine powder coatings offer weatherability, long-lasting adhesion, chalk resistance, chemical resistance to aliphatic hydrocarbons, bases, salt solutions, oils, greases and other petroleum p..
Dielectric Strength	>= 9.00 kV/mm @Temperature 90.0 °C	>= 229 kV/in @Temperature 194 °F	IS 2584-1963
Amity Thermosets ATO 156 Phenolic Molding Glass Filler, Compression Molded Characteristics:High electrical insulationHigh mechanical strengthDimensional stabilityLow water absorptionColor-black Medium flow Applications: High electric insulation componentsHigh voltage swit..
Dielectric Strength	>= 9.00 kV/mm @Temperature 90.0 °C	>= 229 kV/in @Temperature 194 °F	IS 2584-1963
Amity Thermosets ATO 159 Phenolic Molding Glass/ inorganic Filler, Compression Molded Characteristics:High electrical insulationHigh mechanical strengthDimensional stabilityLow water absorptionColor-black Medium flow Applications: High electric insulation componentsHigh voltage swit..