Multibase TPSiV® 3111-60A Thermoplastic Elastomer

Category Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Vulcanizate Elastomer (TPV) , Silicone, Thermoplastic
Manufacturer Multibase
Trade Name TPSiV®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Multibase TPSiV® 3111-60A Thermoplastic Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FEATURES & BENEFITS: Soft silky feel; Excellent abrasion and scratch resistance; Excellent bonding to PC, ABS; Hydrolysis resistant; FDA 21 CFR 177.2600 CompliantAPPLICATIONS: Solution for soft touch overmolding on consumer electronics, mobile communication devices, computers, and sport &leisure applications; Seals and enclosures.Information provided by Multibase, a Dow Corning Company
Physical Properties Metric English Comments
Specific Gravity 1.15 g/cc
1.15 g/cc
ISO 1183
Linear Mold Shrinkage 0.010 - 0.030 cm/cm
0.010 - 0.030 in/in
Mechanical Properties Metric English Comments
Hardness, Shore A 63
63
ISO 868
Tensile Strength 5.70 MPa
827 psi
ISO 37
Tensile Strength, Ultimate 3.20 MPa
464 psi
ISO 37
Elongation at Break 475 %
475 %
ISO 37
Flexural Strength 1.20 MPa
174 psi
ISO 178
Flexural Modulus 0.0221 GPa
3.21 ksi
ISO 178
Tear Strength 25.3 kN/m
144 pli
ISO 34
Compression Set 13 %

@Temperature 23.0 °C,
Time 79200 sec
13 %

@Temperature 73.4 °F,
Time 22.0 hour
ISO 815
72 %

@Temperature 70.0 °C,
Time 79200 sec
72 %

@Temperature 158 °F,
Time 22.0 hour
ISO 815
Processing Properties Metric English Comments
Feed Temperature 185 - 195 °C
365 - 383 °F
Middle Barrel Temperature 190 - 200 °C
374 - 392 °F
Front Barrel Temperature 200 - 215 °C
392 - 419 °F
Nozzle Temperature 205 - 220 °C
401 - 428 °F
Melt Temperature 215 °C
419 °F
Mold Temperature 30.0 - 60.0 °C
86.0 - 140 °F
Drying Temperature 65.0 - 80.0 °C
149 - 176 °F
Dry Time 2 - 4 hour
2 - 4 hour
Descriptive Properties Value Comments
Injection Speed MED-FAST