LNP Lubricomp® GFL-4034 EM M Polysulfone, Milled Glass Fiber Reinforcement, PTFE Lubricant  (discontinued **)&

Category Polymer , Thermoplastic , Polysulfone (PSU)
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LNP Lubricomp® GFL-4034 EM M Polysulfone, Milled Glass Fiber Reinforcement, PTFE Lubricant  (discontinued **)&.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: Good Moldability, LubricatedForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
Physical Properties Metric English Comments
Specific Gravity 1.53 g/cc
1.53 g/cc
Method A; ASTM D792
Linear Mold Shrinkage 0.0070 cm/cm
0.0070 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
0.0060 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 44.8 MPa
6500 psi
ASTM D638
Elongation at Break 2.4 %
2.4 %
ASTM D638
Flexural Strength 75.8 MPa
11000 psi
ASTM D790
Flexural Modulus 3.45 GPa
500 ksi
ASTM D790
Izod Impact, Notched 0.534 J/cm

@Thickness 3.18 mm
1.00 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Unnotched 2.40 J/cm

@Thickness 3.18 mm
4.50 ft-lb/in

@Thickness 0.125 in
ASTM D256
Processing Properties Metric English Comments
Melt Temperature 360 - 371 °C
680 - 700 °F
Mold Temperature 149 °C
300 °F
Drying Temperature 121 - 149 °C
250 - 300 °F
Dry Time 4 hour
4 hour
Moisture Content 0.050 %
0.050 %
Suggested
Back Pressure 0.172 - 0.345 MPa
24.9 - 50.0 psi