LATI Latigray 62-01 CX/75 PA 6

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced
Manufacturer	LATI
Trade Name	Latigray
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latigray 62-01 CX/75 PA 6.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Radiopaque compound based on Polyamide 6 (PA6). Special mineral filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	2.46 g/cc	0.0889 lb/inÂ³
Linear Mold Shrinkage, Flow	0.0050 - 0.0090 cm/cm	0.0050 - 0.0090 in/in
Linear Mold Shrinkage, Transverse	0.0050 - 0.0090 cm/cm	0.0050 - 0.0090 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	75.0 MPa	10900 psi
Elongation at Break	1.1 %	1.1 %
Tensile Modulus	7.90 GPa	1150 ksi
Charpy Impact Unnotched	2.50 J/cmÂ²	11.9 ft-lb/inÂ²
Charpy Impact, Notched	0.150 J/cmÂ²	0.714 ft-lb/inÂ²

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	190 Â°C	374 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	145 Â°C	293 Â°F
Vicat Softening Point	180 Â°C @Load 5.00 kg	356 Â°F @Load 11.0 lb

Processing Properties	Metric	English
Melt Temperature	250 - 290 Â°C	482 - 554 Â°F
Mold Temperature	80.0 - 100 Â°C	176 - 212 Â°F
Drying Temperature	80.0 - 100 Â°C @Time 10800 sec	176 - 212 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa