LATI Laticonther 83 CP/80 PA12, Impact Modified

Category Polymer , Thermoplastic , Nylon , Nylon 12
Manufacturer LATI
Trade Name Laticonther
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Laticonther 83 CP/80 PA12, Impact Modified.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High thermal conductivity product based on Polyamide 12 (PA12), impact modified. Special filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 2.96 g/cc
0.107 lb/in³
Linear Mold Shrinkage, Flow 0.0065 - 0.0085 cm/cm
0.0065 - 0.0085 in/in
Linear Mold Shrinkage, Transverse 0.0065 - 0.0085 cm/cm
0.0065 - 0.0085 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 40.0 MPa
5800 psi
Elongation at Break 1.4 %
1.4 %
Tensile Modulus 3.70 GPa
537 ksi
Charpy Impact Unnotched 2.50 J/cm²
11.9 ft-lb/in²
Charpy Impact, Notched 0.350 J/cm²
1.67 ft-lb/in²
Thermal Properties Metric English Comments
Thermal Conductivity 2.10 W/m-K
14.6 BTU-in/hr-ft²-°F
Longitudinal
Deflection Temperature at 0.46 MPa (66 psi) 120 °C
248 °F
Deflection Temperature at 1.8 MPa (264 psi) 70.0 °C
158 °F
Vicat Softening Point 150 °C

@Load 5.00 kg
302 °F

@Load 11.0 lb
Glow Wire Test 750 °C

@Thickness 1.00 mm
1380 °F

@Thickness 0.0394 in
GWFI/GWT
750 °C

@Thickness 2.00 mm
1380 °F

@Thickness 0.0787 in
GWFI/GWT
775 °C

@Thickness 1.00 mm
1430 °F

@Thickness 0.0394 in
GWIT
775 °C

@Thickness 2.00 mm
1430 °F

@Thickness 0.0787 in
GWIT
Processing Properties Metric English Comments
Melt Temperature 240 - 260 °C
464 - 500 °F
Mold Temperature 50.0 - 70.0 °C
122 - 158 °F
Drying Temperature 70.0 - 90.0 °C

@Time 10800 sec
158 - 194 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa