LATI Later 4 G/50 PBT, 50% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 50% Glass Fiber Filled
Manufacturer LATI
Trade Name Later
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Later 4 G/50 PBT, 50% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polybutylene Terephthalate (PBT) based compound. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.74 g/cc
0.0629 lb/in³
Linear Mold Shrinkage, Flow 0.0030 - 0.0040 cm/cm
0.0030 - 0.0040 in/in
Linear Mold Shrinkage, Transverse 0.0070 - 0.0090 cm/cm
0.0070 - 0.0090 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 45.0 MPa

@Temperature 150 °C
 6530 psi

@Temperature 302 °F
55.0 MPa

@Temperature 120 °C
 7980 psi

@Temperature 248 °F
70.0 MPa

@Temperature 90.0 °C
 10200 psi

@Temperature 194 °F
90.0 MPa

@Temperature 60.0 °C
 13100 psi

@Temperature 140 °F
135 MPa

@Temperature 23.0 °C
 19600 psi

@Temperature 73.4 °F
Elongation at Break 1.8 %

@Temperature 23.0 °C
 1.8 %

@Temperature 73.4 °F
2.5 %

@Temperature 60.0 °C
 2.5 %

@Temperature 140 °F
2.5 %

@Temperature 90.0 °C
 2.5 %

@Temperature 194 °F
3.0 %

@Temperature 120 °C
 3.0 %

@Temperature 248 °F
3.0 %

@Temperature 150 °C
 3.0 %

@Temperature 302 °F
Tensile Modulus 4.50 GPa

@Temperature 150 °C
 653 ksi

@Temperature 302 °F
5.50 GPa

@Temperature 120 °C
 798 ksi

@Temperature 248 °F
7.70 GPa

@Temperature 90.0 °C
 1120 ksi

@Temperature 194 °F
10.0 GPa

@Temperature 60.0 °C
 1450 ksi

@Temperature 140 °F
15.5 GPa

@Temperature 23.0 °C
 2250 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 4.00 J/cm²

@Temperature -20.0 °C
 19.0 ft-lb/in²

@Temperature -4.00 °F
4.50 J/cm²

@Temperature 23.0 °C
 21.4 ft-lb/in²

@Temperature 73.4 °F
Charpy Impact, Notched 0.800 J/cm²

@Temperature -20.0 °C
 3.81 ft-lb/in²

@Temperature -4.00 °F
0.900 J/cm²

@Temperature 23.0 °C
 4.28 ft-lb/in²

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 140 °C
284 °F
Deflection Temperature at 0.46 MPa (66 psi) 225 °C
437 °F
Deflection Temperature at 1.8 MPa (264 psi) 215 °C
419 °F
Vicat Softening Point 215 °C

@Load 5.00 kg
 419 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 240 - 260 °C
464 - 500 °F
Mold Temperature 70.0 - 90.0 °C
158 - 194 °F
Drying Temperature 110 - 130 °C

@Time 10800 sec
 230 - 266 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa