- Polymer Property : Tensile Strength at Break = 45.0 MPa
Polymer Property : Tensile Strength at Break = 45.0 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 45.0 MPa @Temperature 225 °C |
6530 psi @Temperature 437 °F |
ISO 527 |
| Victrex® PEEK 450FC30 General Purpose Product Description: High performance thermoplastic material, 30% reinforced with carbon fibre / graphite / PTFE PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection molding and ext.. |
|||
| Tensile Strength at Break | 45.0 MPa @Temperature 275 °C |
6530 psi @Temperature 527 °F |
ISO 527 |
| Victrex® PEEK 90GL30 Polyetheretherketone, 30% Glass Fiber Reinforced Product Description:High performance thermoplastic material, 30% glass fibre reinforced Polyetheretherketone (PEEK), semi crystalline, granules for injection moulding, very easy flow, FDA food conta.. |
|||
| Tensile Strength at Break | 45.0 MPa @Temperature 23.0 °C |
6530 psi @Temperature 73.4 °F |
50%RH; ISO 527 |
| DuPont Performance Polymers Zytel® FR70M30V0 BK010 Nylon 66
(Unverified Data**) Zytel® FR70M30V0 BK010 is a 30% mineral reinforced, flame retardant, black polyamide 66 resin for injection molding.Information provided by DuPont Performance Polymers |
|||
| Tensile Strength at Break | 45.0 MPa @Temperature 250 °C |
6530 psi @Temperature 482 °F |
ASTM D638 |
| Gharda Chemicals G-PAEKâ„¢ 1230FC Ultra High Performance PEK Polymer Product Details: Ultra High Performance Thermoplastic material, 10% carbon fiber, 10% PTFE and 10% graphite reinforced in Poly Aryl Ether Ketone, semi-crystalline granules suitable for injection mo.. |
|||
| Tensile Strength at Break | 45.0 MPa @Temperature 60.0 °C |
6530 psi @Temperature 140 °F |
|
| LATI Kelon® B FR H2 CE/25-V2HF PA 6, Mineral Reinforced, Flame Retardant, Heat Stabilized Polyamide 6 (PA6) based compound. Heat stabilized. Mineral filler. UL94 V-2 classified, halogens-based flame retardants and red phosphorous free.Availability: Africa & Middle East; Asia Pacific; Eur.. |
|||
| Tensile Strength at Break | 45.0 MPa @Temperature 60.0 °C |
6530 psi @Temperature 140 °F |
|
| LATI Kelon® B H CER/30 PA 6, 30% Mineral Reinforced, Heat Stabilized Polyamide 6 (PA6) based compound. Heat stabilized. Mineral filler. Very high dimensional stability. Good elongation.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North Ame.. |
|||
| Tensile Strength at Break | 45.0 MPa @Temperature 60.0 °C |
6530 psi @Temperature 140 °F |
|
| LATI Lastilac 10 ABS/PC ABS/PC Blend (ABS/PC). Unfilled. Very good surface appearance. High impact resistance. Good thermal properties.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaI.. |
|||
| Tensile Strength at Break | 45.0 MPa @Temperature 60.0 °C |
6530 psi @Temperature 140 °F |
|
| LATI Lastilac RT K/10 ABS, 10% Carbon Fiber Reinforced Acrylonitrile-Butadiene-Styrene copolymer (ABS) based compound. Carbon fiber. High dimensional stability.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInforma.. |
|||
| Tensile Strength at Break | 45.0 MPa @Temperature 150 °C |
6530 psi @Temperature 302 °F |
|
| LATI Latamid 66 H2 G/35-V0KB3 PA 66, 35% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant Polyamide 66 (PA66) based compound. Heat stabilized. Glass fibers. UL94 V-0 classified, with red phosphorous. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaIn.. |
|||
| Tensile Strength at Break | 45.0 MPa @Temperature 120 °C |
6530 psi @Temperature 248 °F |
|
| LATI Latamid 66 H2E21 G/13 PA 66, 13% Glass Fiber Reinforced Polyamide 66 (PA66) based compound. Heat stabilized. Toughened. Glass fibers. High impact resistance. Good impact resistance even at low temperature.Availability: Africa & Middle East; Asia Pacific;.. |
|||
| Tensile Strength at Break | 45.0 MPa @Temperature 150 °C |
6530 psi @Temperature 302 °F |
|
| LATI Laramid CE/60 PPA, 60% Mineral Reinforced Semi-aromatic polyamide (PPA) based compound. Mineral filler. High dimensional stability. Good chemical resistance. Low moisture absorption.Availability: Africa & Middle East; Asia Pacific; Europe; .. |
|||
| Tensile Strength at Break | 45.0 MPa @Temperature 90.0 °C |
6530 psi @Temperature 194 °F |
|
| LATI Laril 13 G/20-V1 PPOm, 20% Glass Fiber Reinforced, Flame Retardant Modified Polyphenylene Oxide (PPOm) based compound. Glass fibers. UL94 V-1 classified, with brominated flame retardants, PBB/PBDE and antimony trioxide free. High dimensional stability. Good thermal.. |
|||
| Tensile Strength at Break | 45.0 MPa @Temperature 150 °C |
6530 psi @Temperature 302 °F |
|
| LATI Larton L K/20 L-PPS, 20% Carbon Fiber Reinforced Linear Polyphenylene Sulfide (L-PPS) based compound. Carbon fiber. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa & Middle.. |
|||
| Tensile Strength at Break | 45.0 MPa @Temperature 90.0 °C |
6530 psi @Temperature 194 °F |
|
| LATI Latamid 6 H2 G/30-V2HF PA 6, 30% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant Polyamide 6 (PA6) based compound. Heat stabilized. Glass fibers. UL94 V-2 classified, halogens-based flame retardants and red phosphorous freeAvailability: Africa & Middle East; Asia Pacific; Europe.. |
|||
| Tensile Strength at Break | 45.0 MPa @Temperature 60.0 °C |
6530 psi @Temperature 140 °F |
|
| LATI Latamid 6 S/30 PA 6, 30% Glass Bead Reinforced Polyamide 6 (PA6) based compound. Glass beads. Very high dimensional stability.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Indu.. |
|||
| Tensile Strength at Break | 45.0 MPa @Temperature 150 °C |
6530 psi @Temperature 302 °F |
|
| LATI Latamid 66 E21 G/30 PA 66, 30% Glass Fiber Reinforced Polyamide 66 (PA66) based compound. Toughened. Glass fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici.. |
|||
| Tensile Strength at Break | 45.0 MPa @Temperature 60.0 °C |
6530 psi @Temperature 140 °F |
|
| LATI Latamid 66 H2PX-V2 PA 66, Heat Stabilized, Flame Retardant Polyamide 66 (PA66) based compound. Heat stabilized. Toughened. UL94 V-2 classified, with brominated flame retardants, PBB/PBDE free.Availability: Africa & Middle East; Asia Pacific; Europe; Latin A.. |
|||
| Tensile Strength at Break | 45.0 MPa @Temperature 60.0 °C |
6530 psi @Temperature 140 °F |
|
| LATI Latamid 68 H2-V0 PA6/PA66 copolymer, Heat Stabilized, Flame Retardant PA6/PA66 copolymer (PA6/PA66) based compound. Heat stabilized. UL94 V-0 classified, halogens-based flame retardants and red phosphorous free. Good surface appearance.Availability: Africa & Middle Ea.. |
|||
| Tensile Strength at Break | 45.0 MPa @Temperature 23.0 °C |
6530 psi @Temperature 73.4 °F |
|
| LATI Latan 13 S/15 POM, 15% Glass Bead Reinforced Polyoxymethylene (POM) based compound. Glass beads. Medium viscosity. High dimensional stability.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation pro.. |
|||
| Tensile Strength at Break | 45.0 MPa @Temperature 23.0 °C |
6530 psi @Temperature 73.4 °F |
|
| LATI Latan 13 S/20 POM, 20% Glass Bead Reinforced Polyoxymethylene (POM) based compound. Glass beads. Medium viscosity. High dimensional stability.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation pro.. |
|||
| Tensile Strength at Break | 45.0 MPa @Temperature 60.0 °C |
6530 psi @Temperature 140 °F |
|
| LATI Latene® AG3H2W G/30-V0E PP Homopolymer, 30% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant Polypropylene homopolymer (PPh) based compound. Chemical grafting Heat stabilized. Metal stabilized. Glass fibers. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE freeAvailability: A.. |
|||
| Tensile Strength at Break | 45.0 MPa @Temperature 120 °C |
6530 psi @Temperature 248 °F |
|
| LATI Later 4 G/20 PBT, 20% Glass Fiber Reinforced Polybutylene Terephthalate (PBT) based compound. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplast.. |
|||
| Tensile Strength at Break | 45.0 MPa @Temperature 150 °C |
6530 psi @Temperature 302 °F |
|
| LATI Later 4 G/50 PBT, 50% Glass Fiber Reinforced Polybutylene Terephthalate (PBT) based compound. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplast.. |
|||
| Tensile Strength at Break | 45.0 MPa @Temperature 150 °C |
6530 psi @Temperature 302 °F |
|
| LATI Later 4 K/30 PBT, 30% Carbon Fiber Reinforced Polybutylene Terephthalate (PBT) based compound. Carbon fiber.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplasti.. |
|||
| Tensile Strength at Break | 45.0 MPa @Temperature 23.0 °C |
6530 psi @Temperature 73.4 °F |
DAM; 50mm/min; ISO 527 |
| DuPont Performance Polymers Zytel® ST801AW NC010 Nylon 66
(Unverified Data**) Zytel® ST801AW NC010 is a Super Tough, high performance polyamide 66 resin. It is UV stabilized and when appropriately colored offers the best resistance to indirect sunlight in automotive interior.. |
|||
| Tensile Strength at Break | 45.0 MPa @Temperature 23.0 °C |
6530 psi @Temperature 73.4 °F |
|
| LATI Later 4-V0 PBT, Flame Retardant Polybutylene Terephthalate (PBT) based compound. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE and antimony trioxide freeAvailability: Africa & Middle East; Asia Pacific; Europe; L.. |
|||
| Tensile Strength at Break | 45.0 MPa @Temperature 120 °C |
6530 psi @Temperature 248 °F |
|
| LATI Laticonther 62 CEG/500-V0HF1 PA 6, Glass/Mineral Reinforced, Flame Retardant High thermal conductivity product based on Polyamide 6 (PA6). Glass fibers / Mineral filler. UL94 V-0 classified, halogens-based flame retardants and red phosphorous free. Availability: Africa & Mid.. |
|||
| Tensile Strength at Break | 45.0 MPa @Temperature 120 °C |
6530 psi @Temperature 248 °F |
ISO 527 |
| DuPont Performance Polymers Crastin® HR5315HF NC010 PBT
(Unverified Data**) Crastin® HR5315HF is a 15% glass reinforced PBT with high flow (HF), moderately toughened, hydrolysis resistant (HR) resin. Excellent balance of properties between terminal pullout and impact resis.. |
|||
| Tensile Strength at Break | 45.0 MPa @Temperature 90.0 °C |
6530 psi @Temperature 194 °F |
|
| LATI Kelon® A H CEG/40 PA 66, Glass/Mineral Reinforced, Heat Stabilized Polyamide 66 (PA66) based compound. Heat stabilized. Glass fibers / Mineral filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati.. |
|||
| Tensile Strength at Break | 45.0 MPa @Temperature 175 °C |
6530 psi @Temperature 347 °F |
ISO 527 |
| Victrex® PEEK 450GL15 Polyetheretherketone, 15% Glass Fibre Reinforced Product Description:High performance thermoplastic material, 15% glass fibre reinforced Polyetheretherketone (PEEK), semi crystalline, granules for injection moulding and extrusion, standard flow, F.. |
|||