Iran Petrochemical (PCC) LT0470/KJ Low Density Polyethylene
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade |
| Manufacturer | Iran Petrochemical Commercial Co. (PCC) |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Iran Petrochemical (PCC) LT0470/KJ Low Density Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LT0470/KJ is a high molecular weight low density polyethylene film grade combining good flexible extrusion behavior and superior mechanical properties. Application: stiffer thin films for textile packaging.Information provided by Iran Petrochemical Commercial Co.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in³ | ISO 1183 |
| Melt Flow | 4.7 g/10 min @Load 2.16 kg, Temperature 190 °C |
4.7 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 12.0 MPa | 1740 psi | ISO 527 |
| Film Tensile Strength at Yield, TD | 12.0 MPa | 1740 psi | ISO 527 |
| Elongation at Break | 100 % | 100 % | ISO 527, MD |
| 500 % | 500 % | ISO 527, TD | |
| Modulus of Elasticity | 0.250 GPa | 36.3 ksi | MD; ISO 527 |
| Tensile Impact | 130 J/cm | 244 ft-lb/in | ASTM D4272 |
| Coefficient of Friction | 0.20 | 0.20 | ASTM D1894 |
| Tear Strength | 30.0 kN/m | 171 pli | TD; ISO 6383-2 |
| 90.0 kN/m | 514 pli | MD; ISO 6383-2 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 12.5 % | 12.5 % | ASTM D1003A |
| Gloss | 50 % | 50 % | ASTM D2457 |