- Ineos ABS Lustran® SAN Sparkle Highest-Clarity
Ineos ABS Lustran® SAN Sparkle Highest-Clarity
| Category | Polymer , Thermoplastic , SAN Polymer , Styrene Acrylonitrile (SAN), Transparent |
| Manufacturer | Ineos ABS |
| Trade Name | Lustran® SAN |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Lustran® SAN Sparkle Highest-Clarity.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 - 0.0040 cm/cm | 0.0030 - 0.0040 in/in | ASTM D955 |
| Melt Flow | 12 g/10 min @Load 3.80 kg, Temperature 230 °C |
12 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 75 | 75 | ASTM D785 |
| Tensile Strength, Ultimate | 62.0 MPa | 8990 psi | ASTM D638 |
| Tensile Modulus | 3.20 GPa | 464 ksi | ASTM D638 |
| Flexural Yield Strength | 96.5 MPa | 14000 psi | ASTM D790 |
| Flexural Modulus | 3.40 GPa | 493 ksi | ASTM D790 |
| Izod Impact, Notched | 0.200 J/cm @Thickness 3.17 mm |
0.375 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Unnotched | 1.60 J/cm @Thickness 3.17 mm |
3.00 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 68.0 µm/m-°C @Temperature 20.0 °C |
37.8 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C @Thickness 12.7 mm |
199 °F @Thickness 0.500 in |
Unannealed; ASTM D648 |
| Vicat Softening Point | 108 °C | 226 °F | Rate B; ASTM D1525 |
| UL RTI, Electrical | 50.0 °C @Thickness 1.60 mm |
122 °F @Thickness 0.0630 in |
UL746B |
| UL RTI, Mechanical with Impact | 50.0 °C @Thickness 1.60 mm |
122 °F @Thickness 0.0630 in |
UL746B |
| UL RTI, Mechanical without Impact | 50.0 °C @Thickness 1.60 mm |
122 °F @Thickness 0.0630 in |
UL746B |
| Flammability, UL94 | HB @Thickness 1.57 mm |
HB @Thickness 0.0618 in |
Clear color |
| HB @Thickness 1.57 mm |
HB @Thickness 0.0618 in |
Clear color |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.57 | 1.57 | ASTM D542 |
| Haze | 0.70 % @Thickness 3.17 mm |
0.70 % @Thickness 0.125 in |
ASTM D1003 |
| Transmission, Visible | 89.5 % @Thickness 3.20 mm |
89.5 % @Thickness 0.126 in |
ASTM D1003 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 205 - 260 °C | 401 - 500 °F |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P3670 TPE, PP Overmold or Standalone use
- SABIC Innovative Plastics Lexan® HP2C PC (Asia Pacific)
- Ineos H20Z-01 Polypropylene Homopolymer (discontinued **)
- Mitsubishi Iupilon® S2000UR 9.5 MFI, UV Stabilized Polycarbonate With Release
- Haynes 25 alloy, room temperature sheet after 100 hours of 760°C exposure
- SABIC Innovative Plastics LNP Thermocomp KF003 Acetal Copoly (Asia Pacific)
- Samsung Cheil Industries Infino® XP-2150IM PPS, 50% Glass Reinforced
- Dow Saran® 540 Vapor Retarder Film
- 3M FM011 Indoor UL Recognized Clear Polyester Overlaminate Label Product
- A. Schulman POLYPUR™ FPU 1380 Thermoplastic Polyurethane Compound
Copyright © lookpolymers.com All Rights Reserved