Alcoa Excalibar® 6013-T651 Aluminum

Category Metal , Nonferrous Metal , Aluminum Alloy , 6000 Series Aluminum Alloy
Manufacturer Alcoa
Trade Name Excalibar®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Alcoa Excalibar® 6013-T651 Aluminum.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Alcoa recommends as a higher machinability alternative to 6061-T651. It has the potential for higher machining speeds and feed rates, easier deburring,ease of clearing 'chips' and better finishes. It is also stronger tand harder than 6061-T651.Weldability = A; Stress Corrosion Cracking Resistance = A; General Corrosion Resistance = B (A = best; E = worst). General 6013 characteristics and uses: High strength and good corrosion resistance. Easily joined by all welding and brazing methods. Excellent compressive properties. Good applied coating acceptance and good machinability.Uses: ABS Braking systems, hydraulic applications, valves, machine parts, roller blade parts, munitions.Data supplied by the manufacturer, Alcoa.
Physical Properties Metric English Comments
Density 2.71 g/cc
0.0979 lb/in³
Mechanical Properties Metric English Comments
Hardness, Brinell 130
130
500 kg load/10 mm ball
Hardness, Knoop 163
163
Estimated from Brinell
Hardness, Rockwell A 49.5
49.5
Estimated from Brinell
Hardness, Rockwell B 80
80
Estimated from Brinell
Hardness, Vickers 149
149
Estimated from Brinell
Tensile Strength, Ultimate >= 379 MPa
>= 55000 psi
Tensile Strength, Yield >= 359 MPa
>= 52100 psi
Elongation at Break 5.0 %
5.0 %
Modulus of Elasticity 69.6 GPa
10100 ksi
Machinability 70 %
70 %
0-100 Scale (A=90; B=70; C=50; D=30; E=10)
Shear Strength 248 MPa
36000 psi
Thermal Properties Metric English Comments
CTE, linear 23.4 µm/m-°C

@Temperature 20.0 - 100 °C
13.0 µin/in-°F

@Temperature 68.0 - 212 °F
average
Thermal Conductivity 164 W/m-K
1140 BTU-in/hr-ft²-°F
Component Elements Properties Metric English Comments
Aluminum, Al 97 %
97 %
Chromium, Cr <= 0.10 %
<= 0.10 %
Copper, Cu 0.60 - 1.1 %
0.60 - 1.1 %
Iron, Fe <= 0.50 %
<= 0.50 %
Magnesium, Mg 0.80 - 1.2 %
0.80 - 1.2 %
Manganese, Mn 0.20 - 0.80 %
0.20 - 0.80 %
Silicon, Si 0.60 - 1.0 %
0.60 - 1.0 %
Titanium, Ti <= 0.10 %
<= 0.10 %
Zinc, Zn <= 0.25 %
<= 0.25 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.00000490 ohm-cm
0.00000490 ohm-cm