ExxonMobil Escorene® CR-5810 EVA Resin, for High Cling Stretch Film  (discontinued **)

Category Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Escorene® CR-5810 EVA Resin, for High Cling Stretch Film  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by the manufacturer, Exxon Chemical.A tackified Ethylene Vinyl Acetate resin for blown or cast stretch film.Applications: Packing films (cling). Data for film properties below based on 1.25 mil film.
Physical Properties Metric English Comments
Density 0.926 g/cc
0.0335 lb/in³
Exxon Method
Thickness 31.8 microns
1.25 mil
Melt Flow 2.8 g/10 min
2.8 g/10 min
Exxon Method
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 500 %
500 %
ASTM D882
Film Elongation at Break, TD 850 %
850 %
ASTM D882
Secant Modulus, MD 0.117 GPa
17.0 ksi
ASTM D882
Secant Modulus, TD 0.117 GPa
17.0 ksi
ASTM D882
Elmendorf Tear Strength MD 150 g
150 g
ASTM D1922
Elmendorf Tear Strength TD 200 g
200 g
ASTM D1922
Elmendorf Tear Strength, MD 4.72 g/micron
120 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 6.30 g/micron
160 g/mil
ASTM D1922
Dart Drop 5.04 g/micron
128 g/mil
F50; ASTM D1709
Dart Drop Test 160 g
0.353 lb
F50; ASTM D-1709
Film Tensile Strength at Break, MD 24.0 MPa
3480 psi
ASTM D882
Film Tensile Strength at Break, TD 22.0 MPa
3190 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 102 °C
216 °F
Exxon Method
Optical Properties Metric English Comments
Haze 5.0 %
5.0 %
ASTM D1003
Gloss 74 %
74 %
45°, ASTM D-2457